Reliability Degradation Characteristics of Ultra-thin Gate Dielectrics for Nano-CMOS Application

Reliability Degradation Characteristics of Ultra-thin Gate Dielectrics for Nano-CMOS Application. J.F. Kang. Institute of Microelectronics Peking University Beijing 100871, China. Acknowledgment:. N. Sa, B.G. Yan, H. Yang, J.F. Yang , Z.L. Xia (IME, PKU)

eblackburn
Download Presentation

Reliability Degradation Characteristics of Ultra-thin Gate Dielectrics for Nano-CMOS Application

An Image/Link below is provided (as is) to download presentation Download Policy: Content on the Website is provided to you AS IS for your information and personal use and may not be sold / licensed / shared on other websites without getting consent from its author. Content is provided to you AS IS for your information and personal use only. Download presentation by click this link. While downloading, if for some reason you are not able to download a presentation, the publisher may have deleted the file from their server. During download, if you can't get a presentation, the file might be deleted by the publisher.

E N D

Presentation Transcript


  1. Reliability Degradation Characteristics of Ultra-thin Gate Dielectrics for Nano-CMOS Application J.F. Kang Institute of Microelectronics Peking University Beijing 100871, China SINANO Workshop, Montreux, Switzerland Sept. 12~16, 2006

  2. Acknowledgment: N. Sa, B.G. Yan, H. Yang, J.F. Yang, Z.L. Xia(IME, PKU) X.Y. Liu, R.Q. Han, Y.Y. Wang (IME, PKU) D.-L. Kwong (ECE, UT Austin) H.Y. Yu (IMEC) C. Ren, M-F. Li, D.S.H. Chan (SNDL, NUS) C. C. Liao, Z. H. Gan, M. Liao, J. P. Wang, and W. Wong (SMIC) SINANO Workshop, Montreux, Switzerland Sept. 12~16, 2006

  3. Outline • Introduction • Reliability characteristics of ultra thin gate dielectrics • HfO2 gate stack • High temperature annealing effect • TDDB, PBTI, and NBTI • SiON in pMOS • Dynamic NBTI • S/D bias effect on NBTI • Summary SINANO Workshop, Montreux, Switzerland Sept. 12~16, 2006

  4. Introduction • Leading-edge production technology of CMOS has scaled down to sub 90nm nodes. • SiON gate dielectrics are used in 90nm and 65nm nodes technology. • High-K/metal gate stacks will be required in sub 45nm nodes technology. SINANO Workshop, Montreux, Switzerland Sept. 12~16, 2006

  5. Introduction (SiON) • NBTI in p-MOS is a critical reliability issue for CMOS with SiON gate dielectric • NBTI is in general attributed to reaction-diffusion (R-D) model involving interfacial bond breaking followed by a diffusion process of hydrogen species (S. Mahapatra et al, IEDM2004, p.105) SINANO Workshop, Montreux, Switzerland Sept. 12~16, 2006

  6. R-D model (S. Mahapatra et al, IEDM2004, p.105; S. Ogawa and N. Shiono, PRB 51, 4218, 1995) SINANO Workshop, Montreux, Switzerland Sept. 12~16, 2006

  7. Introduction (SiON) • Mechanisms of NBTI under various operation modes is not clear • Release of hydrogen from Si-H bonds followed by the lateral motion of protons along the interface (X.J. Zhou et al, APL 84, p.4394, 2004) • Re-passivation effect of interface trap during the post stress phase (T. Yang et al, EDL 26, p.758, 2005) • Hot carrier effect on NBTI (D. Saha et al, EDL 27, p.188, 2006) • Hole energy effect on NBTI due to broken Si-H and Si-O bonds (D. Varghese et al, EDL 26, p.527, 2005) • …… SINANO Workshop, Montreux, Switzerland Sept. 12~16, 2006

  8. Introduction (SiON) • The characteristics of NBTI under various operation modes need to be identified • Dynamic NBTI has been demonstrated the significant difference with static NBTI (G. Chen et al, IRPS 2003, p.196; M. Ershov et al, APL 83, p.1647, 2003) • There is few report on NBTI characteristics in S/D bias mode (N.K. Jha et al, IPRS 2005, p.524) • We will address the S/D bias effect on NBTI SINANO Workshop, Montreux, Switzerland Sept. 12~16, 2006

  9. Introduction (HfO2 gate stack) • Severe reliability problems exist in high K/metal gate stacks due to high pre-existing charge trapping in the stacks (A. Shanware et al, IRPS 2003; C. Shen et al, IEDM 2004) • High temperature RTA ( >900oC) is effective to reduce the preexisting charge trapping in high K gate stack(G.D. Wilk,VLSI 2002) • However, high temperature RTA usually causes significant EOT increase(C.S. Kang, VLSI 2002 ) SINANO Workshop, Montreux, Switzerland Sept. 12~16, 2006

  10. Introduction (HfO2 gate stack) • We have demonstrated the HfN/HfO2 gate stack is robust thermally stable (H. Yu et al, IEDM’03) • EOT increase is negligible after a high temperature annealing on the stack (PGA) • We could expect the excellent reliability and sub-1 nm EOT to be achieved simultaneously SINANO Workshop, Montreux, Switzerland Sept. 12~16, 2006

  11. In this talk, I will address : • HfO2 gate stack • High temperature annealing effect on EOT and reliability • Intrinsic characteristics of TDDB, PBTI, and NBTI in HfN/HfO2 gate stack fabricated by high temperature process • SiON • DNBT characteristics and nitrogen effect • S/D bias effect on NBTI SINANO Workshop, Montreux, Switzerland Sept. 12~16, 2006

  12. Experiments (HfO2 gate stack) • High K gate stack devices were fabricated by using a high temperature process (a gate first process ): • DHF-last pre-gate cleaning process • Deposition of HfO2 gate dielectrics using a MOCVD cluster tool (deposited at 400oC followed by a 700oC PDA in N2 for 1 min) • Deposition of TaN/HfN metal gate stack by PVD • Gate patterning by using RIE • (Followed by S/D implantations for MOSFET devices) • RTA in N2 at 950oC or 1000oC for 30s SINANO Workshop, Montreux, Switzerland Sept. 12~16, 2006

  13. Experiment (SiON) • P+ poly-Si MOSFETs were fabricated using a 90nm CMOS technology. • SiON gate dielectrics: RTO+ Plasma Nitridation+PDA • Static and Dynamic stresses were performed @ RT and 125oC • S/D bias=0 • Various S/D biases SINANO Workshop, Montreux, Switzerland Sept. 12~16, 2006

  14. Outline • Introduction • Reliability characteristics of ultra thin gate dielectrics • HfO2 gate stack • High temperature annealing effect • TDDB, PBTI, and NBTI • SiON in pMOS • Dynamic NBTI • S/D bias effect on NBTI • Summary SINANO Workshop, Montreux, Switzerland Sept. 12~16, 2006

  15. High temperature annealing effect • High temperature process causes the significant reduction of bulk charge trapping in HfN/HfO2 gate stack (J.F. Kang et al, ESL 8 : G311-G313 2005) • After a high temperature (>900oC) process : • Hysteresis- Significant reduction • Extra inversion capacitance- Disappearance SINANO Workshop, Montreux, Switzerland Sept. 12~16, 2006

  16. High temperature annealing effect Scalability of HfN/HfO2 gate stack (MOSC) (J.F. Kang et al, ESL 8 ; H. Yu et al, IEDM’03) 0.75 nm EOT (W/ SN) and 0.91 nm EOT (W/O SN) were achieved in MOSC undergoing a 1000oC PGA process SINANO Workshop, Montreux, Switzerland Sept. 12~16, 2006

  17. HfN HfN HfO2~2.0nm HfO2~2.2nm IL~0.9 nm IL~0.7 nm 1000oC RTA FGA • High temperature annealing effect Scalability of HfN/HfO2 gate stack (MOSC) The robust thermal stability could be attributed to barrier effect of HfN layer against oxygen diffusion into HfO2/Si interface, which effectively suppresses the growth of IL during high temperature RTA 1000oC RTA FGA SINANO Workshop, Montreux, Switzerland Sept. 12~16, 2006

  18. IL ~0.8 nm • High temperature annealing effect Scalability of HfN/HfO2 gate stack (MOSFET) (J.F. Kang et al, EDL 26 ,2005;) 0.95 nm EOT and low gate leakage (9.7X10-5A/cm2 @VFB+1V and 1.3X10-3A/cm2 @VFB-1V ) are achieved in HfN/HfO2 gated nMOSFET SINANO Workshop, Montreux, Switzerland Sept. 12~16, 2006

  19. High temperature annealing effect Well-behaved device performances are achieved in the 0.95 nm EOT nMOSFET (J.F. Kang et al, EDL 26, p.237, 2005) SINANO Workshop, Montreux, Switzerland Sept. 12~16, 2006

  20. Reliability of HfN/HfO2 gate stack • TDDB • Polarity dependent TDDB had been reported in devices with high-k dielectrics(*,**,***) • Two mechanisms were proposed for TDDB • Interfacial layer initiated breakdown • Bulk layer initiated breakdown • E-field dependent TDDB will be shown *R. Degraeve, et all; IRPS 2003. ** Wei Yip Loh, et all; IEDM 2003. *** Y. H. Kim, et all; Device Research Conference, 2003. SINANO Workshop, Montreux, Switzerland Sept. 12~16, 2006

  21. Reliability of HfN/HfO2 gate stack • Intrinsic TDDB characteristics (J.F. Kang et al, submitted to T-ED) • Nearly constant slopes for different areas are the indication of the intrinsic TDDB (A. S. Oates, IEDM, p.923, 2003 ) • Observed TDDB in the HfO2 gate stack fabricated by a high temperature process is intrinsic SINANO Workshop, Montreux, Switzerland Sept. 12~16, 2006

  22. Reliability of HfN/HfO2 gate stack • E-field dependent TDDB (J.F. Kang et al, submitted to T-ED) • Under low E-fields, constant weibull slope indicates IL initiated breakdown • Under high electric field, the E-field dependent weibull slope indicates bulk initiated breakdown SINANO Workshop, Montreux, Switzerland Sept. 12~16, 2006

  23. Reliability of HfN/HfO2 gate stack • E-field dependent TDDB (J.F. Kang et al, submitted to T-ED) • Under high E-fields, hole trapping behavior was observed • Under low E-fields, electron trapping behavior was observed SINANO Workshop, Montreux, Switzerland Sept. 12~16, 2006

  24. Reliability of HfN/HfO2 gate stack • E-field dependent TDDB (J.F. Kang et al, submitted to T-ED) • High energetic holes or electrons trapping dominate the dielectric breakdown (K. Torii et al, in IEDM p.129-132, 2004 ) • Under a high CVS, hole trapping in HfO2 bulk is dominant • Under a low CVS, electron trapping in IL layer is dominant due to the higher E-field in IL layer based on Gauss law εILEIL=εBulkEBulk SINANO Workshop, Montreux, Switzerland Sept. 12~16, 2006

  25. Reliability of HfN/HfO2 gate stack • BTI (J.F. Kang et al, submitted to T-ED) • Under positive stressing, negligible Vt shifts were observed both in nMOS and pMOS SINANO Workshop, Montreux, Switzerland Sept. 12~16, 2006

  26. Reliability of HfN/HfO2 gate stack • BTI (J.F. Kang et al, submitted to T-ED) • Under negative stressing,significant Vt shifts were observed both in nMOS and pMOS devices SINANO Workshop, Montreux, Switzerland Sept. 12~16, 2006

  27. Reliability of HfN/HfO2 gate stack • BTI (J.F. Kang et al, submitted to T-ED) Vt shiftsis bias polarity dependent for nMOSFET SINANO Workshop, Montreux, Switzerland Sept. 12~16, 2006

  28. Reliability of HfN/HfO2 gate stack • BTI (J.F. Kang et al, submitted to T-ED) Vt shiftsis bias polarity dependent for pMOSFET SINANO Workshop, Montreux, Switzerland Sept. 12~16, 2006

  29. Reliability of HfN/HfO2 gate stack • NBTI in pMOS • DCIV indicates increasing interfacial traps under NBT; • Increasing hysteresis indicates the generation of new bulk traps during NBT stressing SINANO Workshop, Montreux, Switzerland Sept. 12~16, 2006

  30. Reliability of HfN/HfO2 gate stack • NBTI in p-MOS • NBTI well fitted by R-D model was observed (S. Zafar et al, VLSI’04 p.208) • Intrinsic NBTI similar to SiO2-devices could be attributed to the breaking of Si-H bonds followed by the H species diffusion SINANO Workshop, Montreux, Switzerland Sept. 12~16, 2006

  31. Reliability of HfN/HfO2 gate stack • PBTI in n-MOS (N. Sa et al, EDL 26, p.610, 2005 ) • At room temperature, a “turn-around” phenomenon was observed. (left) • Negative Vt shifts was observed and shows strong • dependence on temperature and electrical field. (right) SINANO Workshop, Montreux, Switzerland Sept. 12~16, 2006

  32. Reliability of HfN/HfO2 gate stack • PBTI in n-MOS (N. Sa et al, EDL 26, p.610, 2005 ) • The increased S with stressing time indicates the increased interfacial trap density • PBTI fitted by R-D model was observed and the slop was ~0.6 corresponding to the process of the charged species diffusion SINANO Workshop, Montreux, Switzerland Sept. 12~16, 2006

  33. Reliability of HfN/HfO2 gate stack • PBTI in n-MOS (N. Sa et al, EDL 26, p.610, 2005 ) • Intrinsic PBTI fitted by R-D model is observed • PBTI can be explained by the breaking mechanism of Si-O bonds in IL induced by the injected electrons SINANO Workshop, Montreux, Switzerland Sept. 12~16, 2006

  34. Reliability of HfN/HfO2 gate stack • PBTI in n-MOS (N. Sa et al, EDL 26, p.610, 2005 ) • The breaking mechanism of Si-O bonds induced by the injected electrons was confirmed by the measurement on activation energy SINANO Workshop, Montreux, Switzerland Sept. 12~16, 2006

  35. Outline • Introduction • Reliability characteristics of ultra thin gate dielectrics • HfO2 gate stack • High temperature annealing effect • TDDB, PBTI, and NBTI • SiON in pMOS • Dynamic NBTI • S/D bias effect on NBTI • Summary SINANO Workshop, Montreux, Switzerland Sept. 12~16, 2006

  36. Reliability of SiON gate dielectric • DNBTI characteristics • Frequency dependent NBTI @ AC stressing SINANO Workshop, Montreux, Switzerland Sept. 12~16, 2006

  37. Reliability of SiON gate dielectric • DNBTI characteristics • Frequency dependent NBTI is related to the generation of interface traps SINANO Workshop, Montreux, Switzerland Sept. 12~16, 2006

  38. Reliability of SiON gate dielectric • DNBTI characteristics • Process of Nit generation and passivation associated with Si-H bonds meets the R-D model in DC and AC modes SINANO Workshop, Montreux, Switzerland Sept. 12~16, 2006

  39. Reliability of SiON gate dielectric • DNBTI characteristics • Origin of frequency dependent DNBTI could be attributed to the nitrogen trapping effect on diffused H species • The trapped H species will not be responsible for the re-passivation of Si-H bonds during recover phase SINANO Workshop, Montreux, Switzerland Sept. 12~16, 2006

  40. Reliability of SiON gate dielectric • S/D bias effect on NBTI • In low Vds region, NBTI is consistent with one predicted by R-D model (S. Mahapatra et al, EDL 51, p.1371, 2004) • Anomalous E-field dependent NBTI was observed in high Vds region • More severe NBTI with S/D bias was observed in the short channel devices SINANO Workshop, Montreux, Switzerland Sept. 12~16, 2006

  41. Reliability of SiON gate dielectric • S/D bias effect on NBTI • Time evolution of △Vthobeys a power law depicted by generalized reaction-diffusion (R-D) model • The mechanism involving the release of hydrogen from Si-H bonds followed by H species diffusion is responsible for the NBTI • We guess that the energetic holes are responsible for the anomalous E-field dependence of NBTI SINANO Workshop, Montreux, Switzerland Sept. 12~16, 2006

  42. Mechanism of S/D bias enhanced NBTI • S/D bias causes the formation of energetic holes in the channel inversion layer; • Energetic holes are captured by Si-H bonds causing weakened Si-H bond; • Additional energies of the captured holes causes Si-H bond breaking SINANO Workshop, Montreux, Switzerland Sept. 12~16, 2006

  43. Summary (1) • High temperature process could effectively reduce the pre-existing charge trapping in HfO2 gate stacks • For HfN/HfO2 gate stack, sub-1 nm EOT could be achieved even after a high temperature process SINANO Workshop, Montreux, Switzerland Sept. 12~16, 2006

  44. Summary (2) • Intrinsic characteristics of TDDB, NBTI and PBTI could be observed in the HfN/HfO2 with low pre-existing charge trapping • The combination of high temperature process and HfN/HfO2 gate stack is a potential solution for the application in sub-45 nm nodes technology SINANO Workshop, Montreux, Switzerland Sept. 12~16, 2006

  45. Summary (3) • Nitrogen trapping effect on the diffused H species is critical for DNBTI • S/D bias effect on NBTI is significant, especially in the short channel devices • New models on reliability evaluation, including nitrogen effect and S/D bias effect, is required SINANO Workshop, Montreux, Switzerland Sept. 12~16, 2006