4/19/06: Group 8 – Chapters 34 and 35

4/19/06: Group 8 – Chapters 34 and 35. Jason Becker Andrew Nawrocki Ryan Niehaus Jonathan Ogaldez Stephen Wakeland. Chapter 34. Surface Treatments, Coatings, and Cleaning. Introduction. Performing surface treatments can: Improve resistance to wear Control friction Reduce adhesion

rehan
Download Presentation

4/19/06: Group 8 – Chapters 34 and 35

An Image/Link below is provided (as is) to download presentation Download Policy: Content on the Website is provided to you AS IS for your information and personal use and may not be sold / licensed / shared on other websites without getting consent from its author. Content is provided to you AS IS for your information and personal use only. Download presentation by click this link. While downloading, if for some reason you are not able to download a presentation, the publisher may have deleted the file from their server. During download, if you can't get a presentation, the file might be deleted by the publisher.

E N D

Presentation Transcript


  1. 4/19/06: Group 8 – Chapters 34 and 35 Jason Becker Andrew Nawrocki Ryan Niehaus Jonathan Ogaldez Stephen Wakeland

  2. Chapter 34 Surface Treatments, Coatings, and Cleaning

  3. Introduction Performing surface treatments can: Improve resistance to wear Control friction Reduce adhesion Improve lubrication Improve resistance to corrosion Improve fatigue resistance Rebuild surfaces Modify surface texture Impart decorative features

  4. Mechanical Surface Treatments Shot peening Uses a large number of cast steel, glass, or ceramic shot (small balls) Causes compressive residual stresses, improving fatigue life Used on shafts, gears, springs and jet-engine parts

  5. Mechanical Surface Treatments Laser shot peening Uses short laser pulses to produce compressive stress on the surface Very effective Lasers are expensive and require a lot of power

  6. Mechanical Surface Treatments Water-jet peening Uses up to 60,000 psi water blasts to produce compressive stresses Process variables must be controlled Pressure Velocity Nozzle design Distance from surface Ultrasonic peening Piezoelectric transducer

  7. Mechanical Surface Treatments Roller burnishing Uses a roller to "cold-work" a component's surface Induces compressive surface residual stresses

  8. Mechanical Surface Treatments Roller burnishing (cont'd) Internal surfaces can be treated by ballizing or ball burnishing A smooth ball that is slightly larger than the bore diameter is pushed through the length of the hole

  9. Mechanical Surface Treatments Explosive hardening Detonation of a layer of an explosive sheet directly on the workpiece

  10. Mechanical Plating and Cladding Mechanical plating Fine metal particles are compacted over the work piece surface by glass, ceramic, or porcelain beads Beads are propelled by rotary means (like a dryer!)

  11. Mechanical Plating and Cladding Cladding Metal is bonded with a layer of corrosion-resistant metal Can be applied by rolls, dies, explosives, or lasers Aluminum (Alclad) is a typical application

  12. Case Hardening and Hard Facing Case hardening Discussed in chapter 4 Heat surface treatment

  13. Case Hardening and Hard Facing Hard facing A piece of wear-resistant hard metal is deposited on the work piece using fusion-welding Can be used to repair worn parts Enhances wear resistance Used for tools, dies, and other industrial components

  14. Case Hardening and Hard Facing Spark hardening Hard coating of tungsten, chromium, or molybdenum carbides are deposited using an electric arc Used for valve seats, oil-well drilling tools, and dies for hot metalwork

  15. Thermal Spraying A coating of various metals, alloys, carbides, ceramics, and polymers are applied to metal surfaces by a spray gun Surfaces must be clean, oil-free and roughened

  16. Thermal Spraying Combustion spraying Thermal wire spraying Oxyfuel flame melts wire Thermal metal-powder spraying Uses metal powder instead of wire Detonation gun Controlled and repeated explosions Performance similar to plasma High-velocity oxyfuel-gas (HVOF) High performance Lower cost

  17. Thermal Spraying Electrical spraying Twin-wire arc An arc is formed between two wire electrodes Good strength, lowest cost Plasma Produces temperatures of around 15,000oF Good bond strength Very low oxide content Very low levels of porosity

  18. Thermal Spraying Cold spraying Particles are at a lower temperature Oxidation is minimal High impact velocities

  19. Thermal Spraying

  20. Vapor Deposition Process of coating the surface of a work piece (substrate) using chemicals in gaseous form Deposited materials: metals, alloys, carbides, nitrides, borides, ceramics or oxides Typical applications include coating of cutting tools, drills, reamers, milling cutters, punches and dies Two distinct processes: Physical vapor deposition and Chemical vapor deposition

  21. Physical Vapor Deposition Three basic types: 1) Vacuum deposition 2)sputtering 3)ion plating Carried out at temperatures between 200 and 500 degrees Celsius Processes carried out in high vacuum

  22. Vacuum Deposition Metal is evaporated at a high temperatures and deposited onto the substrate which is usually at room temperature Provides coatings of uniform thickness even of complex shapes Similar to arc deposition (cathode is to a plasma state evaporated using electric arc evaporators) Arc deposition provides both functional and decorative applications Pulsed laser is the latest development in vacuum deposition

  23. Sputtering Electric field ionizes an inert gas which then bombards the cathode causing the ejected atoms to coat the substrate Substrate is heated to improve bonding Reactive sputtering uses a reactive gas like oxygen. This deposits oxides onto the surface of the Radio-frequency sputtering is used for nonconductive materials (electrical insulators and semiconductors)

  24. Ion Plating Generic term used for various combined processes of sputtering and vacuum evaporation Ion-beam enhanced deposition is capable of producing thin films as coatings for semiconductors and optical applications Large bulky parts can be coated in large cambers but require high-current power supplies Dual-Ion beam deposition combines physical vapor deposition with simultaneous ion-beam bombardment Provides good adhesion for metalsm ceramics and polymers. Used to make ceramic bearings and dental instruments

  25. Chemical Vapor Depositon Aka CVD Thermochemical process. Induced gas reacts with the heated substrate to coat the substrate through a chemical reaction Used for coating cutting tools with titanium nitride and titanium carbide Coatings usually are thicker that those obtained using PVD and CVD cycle is longer, however the types of coatings and work piece materials are fairly unrestricted CVD process is used to produce diamond coatings without using binders Latest development is medium-temperature CVD which provides a higher resistance to crack propogation

  26. Ion Implantation Ions are accelerated in a vacuum and penitrate the surface of the substrate a few μm Process actually alters the surface properties (can increase surface hardness and improve resistance to friction, wear and corrosion) Can mask the surface of the substrate to accurately control surface properties in certain locations Typically used on cutting and forming tools, semiconductors, dies, molds and metal prostheses

  27. Electroplating The workpiece (cathode) is coated with a different metal (anode) through a water-based electrolytic solution. Process is long because the deposition rate is low (75μm/hour) Thin plate layers are typically 1μm thick layers are generally 500μm Rinse tanks are a necessity because of environmental hazards and recycling of unused material Common coating materials include chromium, nickel, cadmium, copper, tin and zinc. Process used for wire, printed circuits, chrome-plated hardware, galvanizing sheet metal and metalworking dies

  28. Electroplating

  29. Electroless Plating Process carried out by a chemical reaction rather than with an external source of electricity Used for nonconductive materials like plastics and ceramics More expensive than electroplating but coating surface is always uniform Common metals used for coating include copper and nickel

  30. Electroforming Variation of electroplating but is actually a metal fabrication process Metal is electrodeposited onto a mandrel or matrix then removed (the coating itself is the product Mandrels can be made of conducting materials, non-conducting materials coated with a conducting material or have a low melting point and are melted away or dissolved with chemicals Process only suitable for low production quantities, aerospace parts or intricate parts like molds, dies and nozzles

  31. Anodizing Conversion coating process Oxidation process in which the work piece surface is converted to a hard and porous oxide layer that provides corrosion resistance and decorative finish The work piece absorbs oxygen into its surface by a chemical reaction between it and an acid bath Organic dyes can be used to produce a stable and durable surface finish Anodized surfaces also provide a good surface to paint otherwise difficult materials like aluminum

  32. Movie

  33. Coloring Process that alters the surface color of metals, alloys and ceramics. Caused by the conversion of the surface into chemical compounds like oxides, chromates and phosphates. Coloring can be a chemical, electrochemical or thermal process Example: blackening of iron cookware

  34. Hot Dipping Hot dipping is the process where a continuous thin sheet is run through a liquid metal. Used in making galvanized sheets and food cans Protects against corrosion.

  35. Porcelain Enameling Porcelains Porcelains are applied by heating both the workpiece and coating meterail to 425 to 1000 C Can be applied by dipping spraying or electrodeposition. Good corrosion resistance

  36. Ceramic Coatings Ceramic coatings consist of hard metals, aluminum oxide, or zirconium oxide applied to the workpiece with the use of binders. Used for thermal barriers such as hot extrusion dies and in plasma arcs.

  37. Organic Coatings Consist of coatings, films, and laminates that provide corrosion resistance and improve appearance. Uses in cabinets, paneling and aircrafts.

  38. Diamond Coating Diamond coatings are produced by the various vapor deposition. Used for such things as scratchproof windows, sunglasses, drills, cutting tools, and missile sensors.

  39. Surface Texturing Uses Etching, arcs, lasers, and atomic oxygen to modify the surface texture of the workpiece for appearance and function.

  40. Painting Paints serve 2 main purposes, appearance and a protective covering. Paints are relatively cheap easy to apply. Paints are available with good resistance to abrasion, temperature extremes, and fading also resistant environmental attack.

  41. Cleaning Cleaning is the removal of contaminates from the suface. Cleaning can be done in many different ways, mechanically, electrolytically, and chemically with a variety of cleaning fluids. When designing always making sure that the part to be made can be cleaned. Avoid deep blind holes, large parts, and incorporate drainage holes.

  42. Engineering Metrology and Instrumentation

  43. Engineering Metrology Defined as the measurement of dimensions such as length, thickness, diameter, taper, angle, flatness, profile, and others. Post-process inspection; measuring the dimensions after the part is created In-process, on-ling, or real-time inspection; measuring the dimensions while the part is being created Dimensional Tolerance is an important aspect of metrology because it influences the functionality of the part, interchangeability, and manufacturing cost.

  44. Analog and Digital Measurements Resolution The smallest difference in dimension that an instrument can detect or distinguish. Precision The degree to which the instrument gives a repeated measurement of the same standard. • Accuracy • How close the dimensional tolerances are to the required value/measurement.

  45. Analog and Digital Measurements (cont.) Common geometric features typically measured in engineering practice and manufacturing. Length: all linear dimensions of parts Diameter: outside and inside dimensions Roundness: out-of-roundness, concentricity, and eccentricity Depth: such as drilled or bored holes and cavities Straightness: such as shafts bars and tubing Flatness: machined and ground surfaces Parallelism: such as two shafts or sideways in machines Perpendicularity: such as a threaded bar inserted in a flat plate Angles Profiles: such as curvatures in casings, forgings, and on car bodies • Major advantage of Digital instruments: They do not require any particular skill to operate, like with the analog instruments

  46. Traditional Measuring Methods and Instruments Linear Measurement: Direct Reading Rules: Simplest and most commonly used instrument for making linear measurements. Calipers: Used to measure inside and outside lengths. Micrometers: Commonly used to measure the thickness and inside or outside dimensions of parts.

  47. Traditional Measuring Methods and Instruments (cont.) Linear Measurement: Indirect reading Bevel Protractor: Made with 2 blades joined at a central point and both blades come in contact with the part and the angle is read directly on the scale Sine Bar: Involves placing the part on an inclined bar or plate and adjusting the angle until the top surface it parallel to the surface plate and the angle is calculated using trigonometric identities. Surface Plates: Extensively used in Metrology and are typically made from cast iron or natural stone. Granite is the most common due to its low thermal expansion, nonmagnetic, and corrosion resistance. Parts and the measuring instruments are placed on these plates.

  48. Measuring Geometric Features Straightness: Commonly checked with a straightedge or a dial indicator. Autocollimators are used to accurately detect the slightest imperfections in the surfaces of the part. Lasers are used for aligning machine components. Flatness: Flatness can be measured using surface plate and dial indicator (mechanical), or Interferometer, which uses an optical flat. This device is a flat disk of glass or fused quartz with parallel flat surfaces and placed on the surface of the work piece. When a monochromatic light is aimed at the surface, the optical flat splits the light into two beams appearing as light and dark bands to the naked eye. The number of fringes that appear is directly related to the bottom surface of the flat and the work piece. When the work piece is truly flat, the light beams are not split and fringes will not appear. When a work piece is not flat, the fringes are curved. With modern equipment, the resolution can achieve 2.5µm (0.00001 in) and having 1000 lines/in.