Metal Forming

Metal Forming. Metal forming includes a large group of manufacturing processes in which plastic deformation is used to change the shape of metal work pieces. Plastic deformation: a permanent change of shape, i.e., the stress in materials is larger than its yield strength.

matthias-xylon
Download Presentation

Metal Forming

An Image/Link below is provided (as is) to download presentation Download Policy: Content on the Website is provided to you AS IS for your information and personal use and may not be sold / licensed / shared on other websites without getting consent from its author. Content is provided to you AS IS for your information and personal use only. Download presentation by click this link. While downloading, if for some reason you are not able to download a presentation, the publisher may have deleted the file from their server. During download, if you can't get a presentation, the file might be deleted by the publisher.

E N D

Presentation Transcript

  1. Metal Forming • Metal forming includes a large group of manufacturing processes in which plastic deformation is used to change the shape of metal work pieces • Plastic deformation: a permanent change of shape, i.e., the stress in materials is larger than its yield strength • Usually a die is needed to force deformed metal into a shape of the die so that the product has the same cross area as the die handout 7a

  2. Metal Forming • Metal with low yield strength and high ductility is in favor of metal forming • One important difference between plastic forming and metal forming is: Plastic: solids are heated up to be polymer melt Metal: solid remains a solid state in the whole process handout 7a

  3. Metal Forming Metal forming is divided into (1) bulk and (2) sheet Bulk: (1) there is a significant deformation (2) there is a massive shape change (3) surface area to volume of the work is small Sheet: Surface area to volume of the work is large handout 7a

  4. Bulk deformation processes Forging Rolling Traditionally Hot Extrusion Drawing handout 7a

  5. Sheet deformation processes (Press working/ Stamping) Drawing Bending Shearing Actually Cutting handout 7a

  6. In the following series of lecture, we discuss: • For general metal forming process, general mechanics principle / law / effect • For individual processes: • - mechanics principles • - design for manufacturing (DFM) rules • - equipment handout 7a

  7. 1. General mechanics principle • The underlying mechanics principle for metal forming is the stress-strain relationship; see Figure 1. Figure 1 handout 7a

  8. L0: the initial length of a specimen L: the length of the specimen at time t the true strain at time t • True Stress: Applied load divided by instantaneous value of cross-section area • True strain: Instantaneous elongation per unit length of the material handout 7a

  9. In the forming process we are more interested in the plastic deformation region (Figure 1) Plastic deformation region handout 7a

  10. Called FLOW CURVE • The stress-strain relationship in the plastic deformation region is described by Where K= the strength coefficient, (MPa)  = the true strain, σ=the true stress n= the strain hardening exponent, The flow stress (Yf) is used for the above stress (which is the stress beyond yield) handout 7a

  11. FLOW STRESS • As deformation occurs, increasing STRESS is required to continue deformation • Flow Stress: Instantaneous value of stress required to continue deforming the material (i.e., to keep metal “flowing”): handout 7a

  12. AVERAGE FLOW STRESS • For many bulk deforming processes, rather than instantaneous stress, average stress is used (extrusion) • The average flow stress can be obtained by integrating the flow stress along the trajectory of straining, from zero to the final strain value which defines the range of interest: Strength Coefficient Max. strain during deformation Average flow stress Strain hardening exponent handout 7a

  13. Example 1: Determine the value of the strain-hardening exponent for a metal that will cause the average flow stress to be three-quarters of the final flow stress after deformation. Solution: According to the statement of the problem, we have of handout 7a

  14. The above analysis is generally applicable to the cold working, where the temperature factor is not considered. • The metal forming process has three kinds in terms of temperature: (1) cold, (2) warm, (3) hot • In the case of warm and hot forming, the temperature factor needs to be considered, in particular Temperature up The (yield) strength down and ductility up handout 7a

  15. Instantaneous height of work-piece being deformed Speed of deformation (could be equal to velocity of ram) Strain Rate h Flow stress • Strain rate (related to elevated temperatures) • Rate at which metal is strained in a forming process • Such a strain rate can affect the flow stress h handout 7a

  16. Strength coefficient but not the same as K where C  strength constant m  strain-rate sensitivity exponent C and m are determined by the following figure which is generated from the experiment handout 7a

  17. handout 7a