1 / 25

Mechanical and Metallurgical Properties and Forces of Immersed Friction Stir Welding of AA6061-T6

Mechanical and Metallurgical Properties and Forces of Immersed Friction Stir Welding of AA6061-T6. Thomas Bloodworth Vanderbilt University. Overview. Introduction Theory and Objective VWAL Test Bed Experimental Setup Materials Testing Results and Conclusions Future Work. Introduction.

kandaceh
Download Presentation

Mechanical and Metallurgical Properties and Forces of Immersed Friction Stir Welding of AA6061-T6

An Image/Link below is provided (as is) to download presentation Download Policy: Content on the Website is provided to you AS IS for your information and personal use and may not be sold / licensed / shared on other websites without getting consent from its author. Content is provided to you AS IS for your information and personal use only. Download presentation by click this link. While downloading, if for some reason you are not able to download a presentation, the publisher may have deleted the file from their server. During download, if you can't get a presentation, the file might be deleted by the publisher.

E N D

Presentation Transcript


  1. Mechanical and Metallurgical Properties and Forces of Immersed Friction Stir Welding of AA6061-T6 Thomas Bloodworth Vanderbilt University Materials Science & Technology 2007; September 16-20, 2007 — Detroit, MI, USA

  2. Overview • Introduction • Theory and Objective • VWAL Test Bed • Experimental Setup • Materials Testing • Results and Conclusions • Future Work Materials Science & Technology 2007; September 16-20, 2007 — Detroit, MI, USA

  3. Introduction • Friction Stir Welding (FSW) • Frictional heat with sufficient axial (z) force plasticizes weld-piece (Thomas et al) • Advantageous to conventional welding techniques • Welds maintain up to 95% of UTS compared to parent material Schematic of the FSW Process (Record JH, 2005) Materials Science & Technology 2007; September 16-20, 2007 — Detroit, MI, USA

  4. Introduction • Light weight materials used in production (e.g. Aluminum) • FSW is used primarily to weld Aluminum Alloys (AA) • Process currently becoming more prevalent: • Aerospace (e.g. Boeing, Airbus) • Automotive (e.g. Audi) • Marine (SFSW / IFSW) Materials Science & Technology 2007; September 16-20, 2007 — Detroit, MI, USA

  5. Objective • Submerged / Immersed FSW (SFSW / IFSW) • Joining of the weld piece completely submerged in a fluid (i.e. water) • Greater heat dissipation reduces grain size in the weld nugget (Hofmann and Vecchio) • Increases material hardness • Theoretically increases tensile strength Materials Science & Technology 2007; September 16-20, 2007 — Detroit, MI, USA

  6. Objective • Hofmann and Vecchio show decrease in grain size by an order of magnitude • Increase in weld quality in SFSW may lead to prevalent use in underwater repair and/or construction (Arbegast et al) • Friction Stir Spot Welds (FSSW) • Repair of faulty MIG welds (TWI) • Process must be quantitatively verified and understood before reliable uses may be attained Materials Science & Technology 2007; September 16-20, 2007 — Detroit, MI, USA

  7. VWAL Test Bed Materials Science & Technology 2007; September 16-20, 2007 — Detroit, MI, USA

  8. VWAL Capabilities • VUWAL Test Bed: Milwaukee #2K Universal Milling Machine utilizing a Kearney and Treker Heavy Duty Vertical Head Attachment modified to accommodate high spindle speeds. • 4 – axis position controlled automation • Experimental force and torque data recorded using a Kistler 4 – axis dynamometer (RCD) Type 9124 B • Rotational Speeds: 0 – 4000 rpm • Travel Speeds: 0 – 30 ipm Materials Science & Technology 2007; September 16-20, 2007 — Detroit, MI, USA

  9. VWAL Test Bed • Anvil modified for a submerged welding environment • Water initially at room temperature • Equivalent welds run in air and water for mechanical comparison (i.e. Tensile testing, Cross Sectioning) Materials Science & Technology 2007; September 16-20, 2007 — Detroit, MI, USA

  10. Experimental Setup • Optimal dry welds run 2000 rpm, 16 ipm • Submerged welds speeds: 2000 – 3000 rpm, travel speeds 10 – 20 ipm • Weld samples • AA 6061-T6: 3 x 8 x ¼” (butt weld configuration) • Tool • 01PH Steel (Rockwell C38) • 5/8” non – profiled shoulder • ¼” – 20 tpi LH tool pin (probe) of length .235” • Clockwise rotation • Single pass welding Materials Science & Technology 2007; September 16-20, 2007 — Detroit, MI, USA

  11. Experimental Procedure • Shoulder plunge and lead angle: .004” , 20 • Fine adjustments in plunge depth have been noted to create significant changes in force data as well as excess flash buildup • Therefore, significant care and effort was put forth to ensure constant plunge depth of .004” • Vertical encoder accurate to 10 microns • Tool creeps into material from the side and run at constant velocity off the weld sample Materials Science & Technology 2007; September 16-20, 2007 — Detroit, MI, USA

  12. Materials Testing • Tensile testing done using standards set using the AWS handbook • Samples milled for tensile testing • Tensile specimens were milled for each weld run • Nominal ½ “ wide x ¼ “ thick specimens were used for the testing Materials Science & Technology 2007; September 16-20, 2007 — Detroit, MI, USA

  13. Materials Testing • Tensile specimens tested using an Instron Universal Tester • Recorded values included UTS and UYS in lbf Materials Science & Technology 2007; September 16-20, 2007 — Detroit, MI, USA

  14. Results • Stress – Strain curves were generated from the data gathered from the tensile test • Weld pitch “rule” is not followed in IFSW (Revolutions / Inch) Materials Science & Technology 2007; September 16-20, 2007 — Detroit, MI, USA

  15. Results Materials Science & Technology 2007; September 16-20, 2007 — Detroit, MI, USA

  16. Cross Section • Dry Weld Section (left) • IFSW (right) Materials Science & Technology 2007; September 16-20, 2007 — Detroit, MI, USA

  17. Cross Section • Dry FSW 10x (left) • SFSW 50x (right) Materials Science & Technology 2007; September 16-20, 2007 — Detroit, MI, USA

  18. Results Materials Science & Technology 2007; September 16-20, 2007 — Detroit, MI, USA

  19. Results Materials Science & Technology 2007; September 16-20, 2007 — Detroit, MI, USA

  20. Results Materials Science & Technology 2007; September 16-20, 2007 — Detroit, MI, USA

  21. Conclusions • Submerged welds maintained 90-95% of parent UTS • Parent material UTS of 44.88 ksi compared well to the welded plate averaging UTS of ~41 ksi • Worm hole defect welds failed at 65% of parent UTS • effective dry weld equivalent tests not run • Optimal welds for IFSW required a weld pitch increase of 60% • Weld pitch of dry to wet optimal welds • Dry welds: wp = 2000/16 = 125 rev/inch • Wet welds: wp = 2000/10 = 200 rev/inch Materials Science & Technology 2007; September 16-20, 2007 — Detroit, MI, USA

  22. Summary and Conclusions • Average torque increased from FSW to IFSW • FSW: 16 Nm • SFSW: 18.5 Nm • Optimal submerged (wet) FSW’s were compared to conventional dry FSW • Decrease in grain growth in the weld nugget due to inhibition by the fluid (water) • Water welds performed as well if not better than dry welds in tensile tests Materials Science & Technology 2007; September 16-20, 2007 — Detroit, MI, USA

  23. Acknowledgements • This work was supported in part by: • Los Alamos National Laboratory • NASA (GSRP and MSFC) • The American Welding Society • Robin Midgett for materials testing capabilities • UTSI for cross sectioning and microscopy Materials Science & Technology 2007; September 16-20, 2007 — Detroit, MI, USA

  24. Future Work • Fracture Surface Microscopy • Hardness Testing for comparison • Further Mechanical testing • e.g. root bend tests Materials Science & Technology 2007; September 16-20, 2007 — Detroit, MI, USA

  25. References • Thomas M.W., Nicholas E.D., Needham J.C., Murch M.G., Templesmith P., Dawes C.J.:G.B. patent application No. 9125978.8, 1991. • Crawford R., Cook G.E. et al. “Robotic Friction Stir Welding”. Industrial Robot 2004 31 (1) 55-63. • Hofmann D.C. and Vecchio K.S. “Submerged friction stir processing (SFSP): An improved method for creating ultra-fine-grained bulk materials”. MS&E 2005. • Arbegast W. et al. “Friction Stir Spot Welding”. 6th International Symposium on FSW. 2006. Materials Science & Technology 2007; September 16-20, 2007 — Detroit, MI, USA