Sheet Metal Forming Processes

Sheet Metal Forming Processes. Introduction. Ratio – Surface Area:Volume is very high for sheet metal process. Plates – thickness > 0.25 inches Boilers, bridges, ships, etc. use relatively thick plates Usually sheet forming is done on relatively thin material. Shapes can be of various size

amclaughlin
Download Presentation

Sheet Metal Forming Processes

An Image/Link below is provided (as is) to download presentation Download Policy: Content on the Website is provided to you AS IS for your information and personal use and may not be sold / licensed / shared on other websites without getting consent from its author. Content is provided to you AS IS for your information and personal use only. Download presentation by click this link. While downloading, if for some reason you are not able to download a presentation, the publisher may have deleted the file from their server. During download, if you can't get a presentation, the file might be deleted by the publisher.

E N D

Presentation Transcript


  1. Sheet Metal Forming Processes

  2. Introduction • Ratio – Surface Area:Volume is very high for sheet metal process. • Plates – thickness > 0.25 inches • Boilers, bridges, ships, etc. use relatively thick plates • Usually sheet forming is done on relatively thin material. • Shapes can be of various size • Beverage can, car body • Sheet metal forming includes many widely used processes.

  3. Sheet Metal Characteristics • Formability • Methods • Sheet metal is formed as coils of sheets (by rolling) or plates. • Blanks are created for required shapes. • Shearing – sheets • Flame cutting - plates

  4. Sheet Metal Characteristics • Main forces acting in sheet metal forming – tensile • No (or very low) compressive load. Can lead to buckling or folding and wrinkling. • What is the big difference between bulk deformation and sheet metal? • What factors affect stretching and bending? • Elongation, Yield point elongation, anisotropy, grain size, residual stresses, springback, wrinkling.

  5. Elongation • Uniform elongation region • Postuniform elongation region • True stress, true strain: • Necking begins at • Uniform strain  strain hardening index ‘n’ • Large ‘n’, uniform elongation is better.

  6. Necking occurs at an angle ‘’ • Localized • Diffuse • Depends on strain rate sensitivity ‘m’ of the material. • Postuniform elongation is higher with higher values of ‘m.’ • Total elongation  ‘n’ and ‘m.’

  7. Yield Point Elongation • Low carbon steel • Certain points elongate more in the specimen. • Strain rate  elongation  • Grain size  Y.P. elongation  • Leuder’s bands = stretcher strain marks • May not be acceptable in many cases • To avoid: “skin rolling” (cold rolling) • Reduces thickness of sheet 0.5 to 1.5 % • Strain aging can cuase the Y.P elongation to appear after a few days.

  8. Residual Stresses • Because of non uniform deformation. Cause distortion if some parts are removed. • Stress corrosion cracking • Springback • Thin – considerable springback • Wrinkles • Due to compressive load in certain areas.

  9. Anisotropy • Previous history of the sheet metal can cause anisotropy. • Crystallographic – grain orientation • Mechanical Fibering - alignment of impurities, inclusions • Grain Size • Mechanical properties • Appearance: coarse grain causes rough surface appearance (orange peel)