1 / 1

Analytical transmission electron microscopy investigations

Si. Si. Y. Y. Al. Al. Sm. Sm. N. N. Ca. O. O. Ca. Lattice Images of As-received and Heat Treated /-SiAlON. A-Received. Heat Treated. Heat Treated. TJ Amorphous. TJ crystalline. TJ crystalline. Analytical transmission electron microscopy investigations

guy-william
Download Presentation

Analytical transmission electron microscopy investigations

An Image/Link below is provided (as is) to download presentation Download Policy: Content on the Website is provided to you AS IS for your information and personal use and may not be sold / licensed / shared on other websites without getting consent from its author. Content is provided to you AS IS for your information and personal use only. Download presentation by click this link. While downloading, if for some reason you are not able to download a presentation, the publisher may have deleted the file from their server. During download, if you can't get a presentation, the file might be deleted by the publisher.

E N D

Presentation Transcript

  1. Si Si Y Y Al Al Sm Sm N N Ca O O Ca Lattice Images of As-received and Heat Treated /-SiAlON A-Received Heat Treated Heat Treated TJ Amorphous TJ crystalline TJ crystalline Analytical transmission electron microscopy investigations on the effect of heat treatment of SiAION ceramics H Yurdakul, S Turan and H Mandal Anadolu University,Dept. of Materials Science & Eng., Iki Eylul Campus, Eskisehir, 26555 TURKEY Purpose of Study Experimental Procedure XRD Results Producing SiAlON ceramics (1)  Triple Junctions/ Secondary Phase or Phases  Explain the composition of triple junctions/secondary phases and /-SiAlON grains by using Jeol 2100 F transmission electron microscope with attached Jeol STEM-HAADF and EDX dedectors ,  Heat treatment process to SiAlON ceramics         Characterisation of as-received and heat treated SiAlON ceramics by using XRD (2) Determine the heat treatment effects on to triple junctions composition by using analytical electron microscope techniques Characterisation of as-received and heat treated SiAlON ceramics by using Jeol 2100F with attached Jeol STEM-HAADF and EDX dedectors Heat-Treated /-SiAlON ceramics As-Received /-SiAlON ceramics STEM-HAADF Images and EDX Analysis Results of As-Received /-SiAlON STEM-HAADF Images and EDX Analysis Results of Heat-Treated/-SiAlON Triple Junction -SiAlON Secondary Phase Secondary Phase α-SiAlON Composition Y-Sm-Ca-Si-Al-O-N Composition Y-Si-Al-O-N Composition Y-Si-Al-O-N Composition Si-Al-O-N Composition Y--Si-Al-O-N Polytype Composition Si-Al-O-N α-SiAlON -SiAlON -SiAlON Secondary Phase Triple Junction Collapse of Triple Junctions Composition Y-Ca-Si-Al-O-N Composition Y-Sm-Ca-Si-Al-O-N Composition Y-Si-Al-O-N Composition Y-Sm-Ca-Si-Al-O-N Composition Si-Al-O-N Composition Si-Al-O-N EDX Elemental Line Scan Analysis Results of As-Received /-SiAlON EDX Elemental Line Scan Analysis Results of Heat Treated /-SiAlON Results Present preliminary research of as-recevied and heat treated /-SiAlON ceramics were performed by using EDX analysis with STEM-HAADF images and XRD techniques. According to these first results; it was seen that secondary phases couldn’t be dedected their elemental constituents by XRD were present both as-recevied and heat treated /-SiAlON ceramics in such as Y-Si-Al-O-N. Triple junctions compositions of both samples were shown in such as Y-Sm-Ca-Si-Al-O-N and ıttrium was incorparated to -SiAlON structure. But actually EFTEM 3-window elemental mapping, EFTEM-SI (spectum imaging), STEM-SI and PEELS (parallel electron energy loss spectrometer studies sould be performed in future works. If you would like to take more information, please get in contact to sturan@anadolu.edu.tr

More Related