APLIKASI METODE DESAIN TAGUCHI UNTUK BELAJAR MENGETAHUI PERILAKU BAJA AISI 1040 BORONIZED

APLIKASI METODE DESAIN TAGUCHI UNTUK BELAJAR MENGETAHUI PERILAKU BAJA AISI 1040 BORONIZED. Disusun Oleh : Syamsul Khaerudin Syah 082679. Boronizing menggunakan metode Taguchi.

cosmo
Download Presentation

APLIKASI METODE DESAIN TAGUCHI UNTUK BELAJAR MENGETAHUI PERILAKU BAJA AISI 1040 BORONIZED

An Image/Link below is provided (as is) to download presentation Download Policy: Content on the Website is provided to you AS IS for your information and personal use and may not be sold / licensed / shared on other websites without getting consent from its author. Content is provided to you AS IS for your information and personal use only. Download presentation by click this link. While downloading, if for some reason you are not able to download a presentation, the publisher may have deleted the file from their server. During download, if you can't get a presentation, the file might be deleted by the publisher.

E N D

Presentation Transcript

  1. APLIKASI METODE DESAIN TAGUCHI UNTUK BELAJAR MENGETAHUI PERILAKU BAJA AISI 1040 BORONIZED DisusunOleh : SyamsulKhaerudinSyah 082679

  2. Boronizing menggunakan metode Taguchi • Boronizing adalah termo-kimia proses difusi boron yang menyebar ke baja pada tinggi suhu. Permukaan besi dan baja boronized memiliki kekerasan tinggi, ketahanan aus yang sangat baik, baik ketahanan korosi dan stabilitas kimia yang kuat

  3. WEAR TES DAN DESAINEKSPERIMENTAL • Pin bahan uji terbuat dari baja AISI 1040 digunakan untuk hasil studi AISI 440C baja digunakan sebagai bahan untuk ujian Kenakan spesimen uji mesin dari sampel boronized untuk membentuk pin silinder berdiameter 6 mm dan panjang 10 mm. Wajah spesimen kemudian metallographically dipoles. Komposisi kimia dari AISI 1040 dan baja 440C

  4. Rinciankondisimemakaites yang digunakandalampenelitianini. • Pin bahan baja AISI 1040 Disc bahan stainless steel AISI 440C dengan kekerasan 63 HRC Pin dengan diameter 6mm Silinder dan tinggi 10mm dimensi Sliding kecepatan (m / s) 0.5-1.0-1.5 Beban normal (N) 30,60,120 Jarak luncur (m) 150300600

  5. Tingkat kontrol faktor • J: waktu Boronizing Unboronized 2 jam 4 jam jam B: Normal memuat 30 60 120 N C: Sliding jarak 150 300 600 m D: Sliding kecepatan 0,5 1,0 1,5 m / s

  6. Sebuahstandar Taguchi rencanaeksperimentaldengannotasi L27 (313) • DalammetodeTaguchi, hasileksperimen yang diubahmenjadisinyal-to-noise (S / N) rasio. MetodeinimerekomendasikanpenggunaanS / N rasiountukmengukurkarakteristikkualitasmenyimpangdarinilai yang diinginkan. Adatigakategorikarakteristikkualitasdalamanalisisrasio S / N, yang merupakan-rendah-yang-lebihbaik, lebihtinggi-yang-baik, dan-nominal-the-baik.

  7. (Lanjutan) • Untukmendapatkan parameter pengujian yang optimal,-rendah-yang-baikkualitaskarakteristikuntukmenurunkanberatbadandiambil. Rasio S / N untuksetiaptingkatparameter pengujiandihitungberdasarkananalisis S / N. Selainitu, analisisstatistikvarians (ANOVA) adalahdilakukanuntukmelihatmana parameter ujistatistiksignifikan. Dengan S / N rasiodananalisis ANOVA, kombinasi optimal parameter pengujiandapatdiprediksiuntuktingkatkepercayaan 95%. 240 Int

  8. WASSSALAAAAM…… SEKIAN DAN TERIMAKASIH