Vertical Pillars for Biological Force Sensing

Vertical Pillars for Biological Force Sensing. Sarah Coulthard, Nahid Harjee, Nathan Klejwa, Ronald Kwon. Class update – July 6th. Device Overview. Training. Completed: MERL clean shop: All wafersaw: Ron amtetcher: Nahid wbgeneral: Nathan To be completed: innotec Critical point dryer.

phuoc
Download Presentation

Vertical Pillars for Biological Force Sensing

An Image/Link below is provided (as is) to download presentation Download Policy: Content on the Website is provided to you AS IS for your information and personal use and may not be sold / licensed / shared on other websites without getting consent from its author. Content is provided to you AS IS for your information and personal use only. Download presentation by click this link. While downloading, if for some reason you are not able to download a presentation, the publisher may have deleted the file from their server. During download, if you can't get a presentation, the file might be deleted by the publisher.

E N D

Presentation Transcript


  1. Vertical Pillars for Biological Force Sensing Sarah Coulthard, Nahid Harjee, Nathan Klejwa, Ronald Kwon Class update – July 6th

  2. Device Overview

  3. Training • Completed: • MERL clean shop: All • wafersaw: Ron • amtetcher: Nahid • wbgeneral: Nathan • To be completed: • innotec • Critical point dryer

  4. Fabrication • 1. Quartz wafers – Obtained from stockroom • Glass vs. Quartz substrate • Quartz More flexible when working at wet benches • Glass etches 5~10x faster • Adhesion of SU-8 in HF will be final determinant

  5. Fabrication (Alignment Marks) • 2. Etch alignment marks • Adhesion of resist to quartz • Shipley 3612 or 3617m • Isotropic or anisotropic etch(HF bath or amtetcher) • Visibility on a transparent substrate • Etch rates • “Frosting” of quartz in Piranha1 or HF 1 K. R. Williams, et al., J. Microelectromech. Syst., vol. 12, no. 6, pp. 761-778, 2003.

  6. Fabrication (Alignment Marks) • Process: Piranha, YES, svgcoat, karlsuss, svgdev, inspection, 6:1 BOE, Piranha • First attempt with 3612: interference rings • Issues with 3617m: • Bubbles in the line • Coat program changed • Two more attempts with 3612 for exposure • 120 s in 6:1 BOE, measured with dektak

  7. Fabrication (Alignment Marks) • Adhesion not an issue after HMDS prime • Shipley 3612 is adequate • No frosting in Piranha or HF • 110 nm/min in 6:1 BOE, in line with Williams (130 nm/min in 5:1 BOE) • Alignment marks visible on karlsuss

  8. Fabrication • 3. Spin 5 μm SU-8 (Waiting on SU-8 2005) • 4. Expose cantilevers (Waiting on SU-8 2005)

  9. Fabrication • 6. Deposit Cr then Au • 5. Develop SU-8 • Need to have 1000 Å of Au to connect bondwire

  10. Fabrication • 7. Etch back metal (Mask 3) • Cr and Au etchant available at wbgeneral • Need to test resistance of SU-8 to etchants

  11. Fabrication • 8. Spin 300 μm SU-8 2100 • New hotplate installed in MERL Cleanshop • Hotplate has NOT been calibrated • Several tests of 300 μm SU-8 conducted • Difficult get an even coating without bubbles • Skin forms on baking SU-8 and causes non-uniformity • May need to use 2 layers each 150 μm thick

  12. Fabrication • 9. Expose pillars and spacers (Waiting) • 10. Spin 35 μm SU-8 (Waiting on SU-8 2035)

  13. Fabrication • 11. Expose top of spacers (Waiting) • 12. Develop SU-8 (Waiting)

  14. Fabrication • 13. Release cantilevers with wet HF • HF Vapor available only at wbmetal • No metal that is resistant to HF is allowed at wbmetal (Cr, Au, etc) • SU-8 may peel off Quartz in high concentration HF (49%) • Instead, use a long etch (10-15 hours) in weak HF (20:1 BOE)

  15. Fabrication • 14. Critical Point Dry wafers after HF etch to prevent stiction (Waiting on training)

  16. Fabrication • 15. Dice • Use wafer saw to dice on backside (to avoid water and stiction) • Use etched wafer saw lanes as “scores” to snap quartz • Use etched wafer saw lanes as guides for diamond scribe • Laser ablation?

  17. Questions and Suggestions