Chapter 31 – STRUCTURE FACTORS FOR POLYMER SYSTEMS

Chapter 31 – STRUCTURE FACTORS FOR POLYMER SYSTEMS. 31:5. THE ZERO CONTRAST METHOD. 31:6. THE RANDOM PHASE APPROXIMATION. dPEO. D 2 O. hPEO. H 2 O. 31:5. THE ZERO CONTRAST METHOD. -- Consider deuterated and hydrogenated polymers of same M w -- Mix them in solution

akasma
Download Presentation

Chapter 31 – STRUCTURE FACTORS FOR POLYMER SYSTEMS

An Image/Link below is provided (as is) to download presentation Download Policy: Content on the Website is provided to you AS IS for your information and personal use and may not be sold / licensed / shared on other websites without getting consent from its author. Content is provided to you AS IS for your information and personal use only. Download presentation by click this link. While downloading, if for some reason you are not able to download a presentation, the publisher may have deleted the file from their server. During download, if you can't get a presentation, the file might be deleted by the publisher.

E N D

Presentation Transcript


  1. Chapter 31 – STRUCTURE FACTORS FOR POLYMER SYSTEMS 31:5. THE ZERO CONTRAST METHOD 31:6. THE RANDOM PHASE APPROXIMATION

  2. dPEO D2O hPEO H2O 31:5. THE ZERO CONTRAST METHOD -- Consider deuterated and hydrogenated polymers of same Mw -- Mix them in solution -- Keep polymer volume fraction constant, but vary deuterated fraction -- Mix deuterated and hydrogenated solvent fraction to obtain zero contast Scattering cross section: Contrasts: Partial scattering factors:

  3. SOME DETAILS Scattering cross section (cm-1): single-chain inter-chain Defined standard deviation: Defined average squared: When contrast is zero, the inter-chain term does not contribute and the scattering cross section is proportional to single-chain form factor only

  4. MORE DETAILS Derivations: Cross section: Zero contrast condition:

  5. 31:6. THE RANDOM PHASE APPROXIMATION Derivations: Single-chain scattering factor: Flory-Huggins interaction parameter: Single-chain form factor: Incompressibility condition: Cross section: Spinodal condition:

  6. COMMENTS -- The zero contrast method and the Random Phase Approximation (RPA) method are useful methods for analyzing SANS data from polymers. -- The zero contrast method measures single-chain properties even in concentrated polymer mixtures. -- The RPA is a single method to calculate the structure factor for polymer mixtures in the mixed phase (homogeneous) region.