1 / 14

Preparation of the Bi 12 SiO 20 thin films by the sol-gel method

Preparation of the Bi 12 SiO 20 thin films by the sol-gel method. Š. Kunej , A. Veber and D. Suvorov Advanced Materials Jožef Stefan Institute. Outline. Introduction Aim of work Experimental Results Sapphire Si/SiO 2 /TiO 2 /Pt Spinel MgAl 2 O 4 Conclusions.

Download Presentation

Preparation of the Bi 12 SiO 20 thin films by the sol-gel method

An Image/Link below is provided (as is) to download presentation Download Policy: Content on the Website is provided to you AS IS for your information and personal use and may not be sold / licensed / shared on other websites without getting consent from its author. Content is provided to you AS IS for your information and personal use only. Download presentation by click this link. While downloading, if for some reason you are not able to download a presentation, the publisher may have deleted the file from their server. During download, if you can't get a presentation, the file might be deleted by the publisher.

E N D

Presentation Transcript


  1. Preparation of the Bi12SiO20 thin films by the sol-gel method Š. Kunej, A. Veber and D. Suvorov Advanced Materials Jožef Stefan Institute

  2. Outline • Introduction • Aim of work • Experimental • Results • Sapphire • Si/SiO2/TiO2/Pt • Spinel MgAl2O4 • Conclusions

  3. “Bulk” Bi12SiO20* (5.5GHz): ’ = 37.6 Qxf = 8100 GHz f = -20 ppm/K Tsint. = 850°C Microwave technology (LTCC) Ag MINITURIZATION THIN FILMS Introduction SILLENITE * M. Valant, D. Suvorov; J. Am. Ceram. Soc., 84[12], 2900-904, 2001

  4. Aim of work • Preparing Bi12SiO20 (BSO) thin films using sol-gel method • Determining microstructure and thickness of BSO thin films deposited on substrates: • Sapphire • Si/SiO2/TiO2/Pt • Spinel MgAl2O4

  5. TEOS + 2-ethoxyethanol Experimental: SOL-GEL Synthesis Bi(NO3)3·5H2O Vacuum drying 60°C/96h • Used chemicals: • Bismuth (III) nitrate • [Bi(NO3)3·5H2O] • Tetraethly orthosilicate • (TEOS) [Si(OC2H5)5] • Acetic acid • [CH3COOH] • Ethanolamine • [H2NCH2CH2OH] • 2-ethoxyethanol • [C2H5OCH2CH2OH] Acetic acid + Ethanolamine Bi(NO3) Bismuth complex solution Sol Spin-coating (5000 rpm) 4x Analytical methods: XRD  SEM  AFM Firing: 300-700°C/1h Pyrolysis: 220°C/2min

  6. C / ( mol/l ) t / h 1.20 5 1.12 48 0.98 168 0.76 456 0.67 - Results Influence of solvent on gelation time :

  7. Results: Sapphire Results: Sapphire Spin-coating: 4 x 5000 rpm Firing: 700°C/1h

  8. d  400nm Results: Sapphire

  9. Results: Si/SiO2/TiO2/Pt Spin-coating: 4 x 5000 rpm Firing: 700°C/1h

  10. d  230nm Results: Si/SiO2/TiO2/Pt

  11. Results: Spinel Spin-coating: 4 x 5000 rpm Firing: 700°C/1h

  12. d  300nm Results: Spinel

  13. Conclusions • The Bi12SiO20 (BSO) thin films were successfully prepared by the sol-gel method • The BSO thin film obtained on sapphire substrate is porous with rough surface • Homogeneous BSO thin film of thickness  230nm was obtained for the thin film deposited on Si/SiO2/TiO2/Pt substrate • Thin film deposited on the spinel substrate shows homogeneous microstructure with grain size of 200-500nm. Future work: • Optimization of BSO sol-gel precursor • Obtaining “denser” BSO thin films • Dielectric measurements of BSO thin films

  14. Thank you for your attention!