An Image/Link below is provided (as is) to download presentation Download Policy: Content on the Website is provided to you AS IS for your information and personal use and may not be sold / licensed / shared on other websites without getting consent from its author. Content is provided to you AS IS for your information and personal use only. Download presentation by click this link. While downloading, if for some reason you are not able to download a presentation, the publisher may have deleted the file from their server. During download, if you can't get a presentation, the file might be deleted by the publisher.

E N D

Presentation Transcript


  1. Chapter 27 Synthetic Polymers Paula Yurkanis Bruice University of California, Santa Barbara

  2. Polymerization A polymer is a large molecule made by linking together repeating units of small molecules called monomers.

  3. A Chain-Growth Polymer (polystyrene) Chain-growth polymers (also known as addition polymers), are made by chain reactions.

  4. Step-Growth Polymer (Dacron) Step-growth polymers (also called condensation polymers), are made by combining two molecules while removing a small molecule.

  5. Chain-Growth Polymers Chain-growth polymers are formed by one of three mechanisms. • Radical polymerization • Cationic polymerization • Anionic polymerization

  6. Radical Polymerization The initiator is a radical.

  7. Propagation Steps

  8. Termination Steps

  9. Chain Transfer The molecular weight of the polymer can be controlled by a process known as chain transfer.

  10. Head-to-Tail Linkage Chain-growth polymerization of monosubstituted ethylenes exhibits a marked preference for head-to-tail addition.

  11. Poly(vinyl chloride) Head-to-tail addition forms a polymer with a substituent on every other carbon.

  12. Stabilization of the Propagating Site Head-to-tail addition is favored for steric reasons. Head-to-tail addition is favored by groups that stabilize radicals.

  13. Alkenes Used in Radical Polymerization

  14. Radical Initiators

  15. Branching of the Polymer Chain

  16. Branched Polymers are More Flexible

  17. Recycling Symbols

  18. Cationic Polymerization The initiator is an electrophile.

  19. Propagating Steps

  20. Three Ways to Terminate the Chain

  21. A Carbocation Monomer Can Undergo Carbocation Rearrangement

  22. Alkenes Used in Cationic Polymerization Monomers with electron-donating substituents undergo cationic polymerization.

  23. Anionic Polymerization The initiator is a nucleophile.

  24. Propagating Steps Nonterminated chains are called “living polymers”and remain active until they are “killed.”

  25. Alkenes Used in Anionic Polymerization Monomers with electron-withdrawing substituents undergo anionic polymerization.

  26. Super Glue(an example of anionic polymerization)

  27. What Determines the Mechanism? Alkenes with substituents that can stabilize radicals undergo radical polymerization. Alkenes with electron-donating substituents that can stabilize cations undergo cationic polymerization. Alkenes with electron-withdrawing substituents that can stabilize anions undergo anionic polymerization. Some alkenes undergo polymerization by more than one mechanism.

  28. Ring-Opening Polymerization (anionic)

  29. Ring-Opening Polymerization(cationic)

  30. Stereochemistry of Polymerization Long, unbranched polymers with either isotactic or the syndiotactic configuration can be prepared using an aluminum–titanium initiator (a Ziegler–Natta catalyst).

  31. Mechanism for Ziegler–Natta-Catalyzed Polymerization

  32. Polymerization of Dienes These rubbers have cis double bonds.

  33. Neoprene(a synthetic rubber) Neoprene has trans double bonds.

  34. Disulfide Bonds in Rubber The more sulfur used in vulcanization, the more rigid the polymer.

  35. Four Types of Copolymers

  36. Step-Growth Polymers The monomer can have two different functional groups. The monomer can be two different bifunctional compounds.

  37. Step-Growth Polymerization Requires High Yields for Long Chains

  38. Nylon is a Polyamide Nylon 6 is an example of a step-growth polymer formed by a monomer with two different functional groups.

  39. Commercial Synthesis of Nylon 6

  40. Nylon is a Polyamide Nylon 66 is an example of a step-growth polymer formed by two different bifunctional monomers.

  41. Aromatic Polyamides are Called Aramides The incorporation of aromatic rings into polymers improves the physical strength of the polymers.

  42. Kevlar

  43. Dacron is a Polyester Polyesters are step-growth polymers in which the monomer units are joined together by ester groups.

  44. Kodel is a Polyester

  45. Lexan is a Polycarbonate Polycarbonates have two ester groups bonded to the same carbon.

  46. An Epoxy Resin is a Cross-Linked Polymer(it is the strongest adhesive known)

  47. A Urethane A urethane has an OR and an NHR bonded to the same carbonyl carbon.

  48. A Polyurethane