INFLUENCES DE DIVERS MODES DE PHOTO-POLYMERISATION (HALOGENE, LED, LASER) SUR LA MICRO-DURETE VICKERS DE DEUX RESINES COMPOSITES POSTERIEURES. E . LEFORESTIER , M. GAUDARD, O. GENOVESE, E. MEDIONI, M. BOLLA L.A.S.I.O - Université de Nice Sophia-Antipolis - U.F.R d’Odontologie.

norman-kemp
Download Presentation

E . LEFORESTIER , M. GAUDARD, O. GENOVESE, E. MEDIONI, M. BOLLA

An Image/Link below is provided (as is) to download presentation Download Policy: Content on the Website is provided to you AS IS for your information and personal use and may not be sold / licensed / shared on other websites without getting consent from its author. Content is provided to you AS IS for your information and personal use only. Download presentation by click this link. While downloading, if for some reason you are not able to download a presentation, the publisher may have deleted the file from their server. During download, if you can't get a presentation, the file might be deleted by the publisher.

E N D

Presentation Transcript

  1. INFLUENCES DE DIVERS MODES DE PHOTO-POLYMERISATION (HALOGENE, LED, LASER) SUR LA MICRO-DURETE VICKERS DE DEUX RESINES COMPOSITES POSTERIEURES E. LEFORESTIER, M. GAUDARD, O. GENOVESE, E. MEDIONI, M. BOLLA L.A.S.I.O-Université de Nice Sophia-Antipolis - U.F.R d’Odontologie Jeudi 26 et Vendredi 27 Mai 2005 Faculté d’Odontologie de Nancy

  2. OBJECTIFS Évaluer l’apport des nouvelles technologies en matière de photo-polymérisation Analyse du taux de conversion de deux résines composites postérieures insolées par plusieurs types de sources Étude de micro-dureté Vickers de surface et de profondeur (A.D.A)

  3. MATERIELS Composite QuixFil de DENTSPLY DETREY Composite Filtek P60 de 3M ESPE

  4. MATERIELS

  5. MATERIELS Halogène Degulux de DEGUSSA DENTAL LED 1°G Elipar Freelight de 3M 3ESPE

  6. MATERIELS LED 2°G Elipar Freelight 2 de 3M ESPE Laser Dental 300 de HGM Medical Laser

  7. MATERIELS

  8. METHODE 12 échantillons par couple matériau/source

  9. METHODE 5 mesures de micro-dureté par faces Stockage dans de l’eau distillée et placement dans une étuve à 37°C pendant 24heures. Puis conservation au sec et à l’abri de la lumière pendant 6 jours.

  10. RESULTATS - DISCUSSION • Étude statistique: • Test de KRUSKAL-WALLIS. • Test ANOVA. • -Test de BONFERRONI.

  11. N.S. N.S. Faces non insolées Faces insolées S S RESULTATS - DISCUSSION 100 90,43 89,09 80 75,29 65,63 78,33 76,04 60 59,76 58,12 Hv 40 20 0 Degulux Freelight 1 Freelight 2 Dental 300 Hv MOYENNE PAR LAMPE

  12. RESULTATS - DISCUSSION

  13. CONCLUSIONS LAMPES A FORTE DENSITE DE PUISSANCE Augmentation de la profondeur de polymérisation Diminution du temps de polymérisation INTERET CLINIQUE

  14. CONCLUSIONS MATERIAUX COMPOSITES POSTERIEURS Propriétés mécaniques améliorées Propriétés esthétiques satisfaisantes Manipulation clinique aisée INTERET CLINIQUE

  15. CONCLUSIONS Matériaux et sources lumineuses performants  Respect des données fabricants et des indications MATERIAUX SOURCES SITUATION CLINIQUE

  16. MERCI DE VOTRE ATTENTION