An Image/Link below is provided (as is) to download presentation Download Policy: Content on the Website is provided to you AS IS for your information and personal use and may not be sold / licensed / shared on other websites without getting consent from its author. Content is provided to you AS IS for your information and personal use only. Download presentation by click this link. While downloading, if for some reason you are not able to download a presentation, the publisher may have deleted the file from their server. During download, if you can't get a presentation, the file might be deleted by the publisher.

E N D

Presentation Transcript


  1. Heat extraction through cable insulation and quench limits Pier Paolo Granieri, Rob van Weelderen, Lina Hincapié (CERN) 2nd Joint HiLumi LHC-LARP Annual Meeting INFN Frascati, 14-16 November 2012 (revised version 11/1/2013)

  2. Outline • Heat transfer through cable electrical insulation: evolution • Experimental method • setup description • results • Quench limits estimation • MQXF at 1.9 K bath temperature • vs. modeling results • vs. LHC magnets and MQXF at 4.2 K P.P. Granieri - Heat extraction and quench limits

  3. Heat transfer through cable electrical insulation: evolution P.P. Granieri - Heat extraction and quench limits

  4. Heat transfer through cable electrical insulation: evolution P.P. Granieri - Heat extraction and quench limits

  5. Heat transfer through cable electrical insulation: evolution P.P. Granieri - Heat extraction and quench limits

  6. Heat transfer through cable electrical insulation: evolution * * * * unpublishedmeasurementsfrom D. Richter (5 SCheatedcables, actual MQX cables) P.P. Granieri - Heat extraction and quench limits

  7. Heat transfer through cable electrical insulation: evolution * * * * unpublishedmeasurementsfrom D. Richter (5 SCheatedcables, actual MQX cables) P.P. Granieri - Heat extraction and quench limits

  8. Experimental method • Sample: - 150 mm long rectangular stack made of 6 alternating cables • Cable: - CuNi10 - LHC cables geometry, MB inner layer • T sensors: - AuFe0.07at%/Chromel differential thermocouples - in grooves in the central cable - installed before impregnation • Heating: - Joule heating along resistive strands - steady-state - different configurations (heated cables) P.P. Granieri - Heat extraction and quench limits

  9. Experimental method Q Q 1 2 Instrumented cable 3 4 5 6 • Insulation: - fiber glass sleeve - vacuum impregn. resin: CTD-101 - thickness: 150 µm • Cooling (transversal): - He II, 1.9 K - He I, 4.2 K • Pressure: 0 MPa P.P. Granieri - Heat extraction and quench limits

  10. Experimental results Tc (mid-plane, cable center) Tc (mid-plane, cableedge) Different position in the cable, Tbath, heating configuration P.P. Granieri - Heat extraction and quench limits

  11. Heat extraction from coil inner layer(cable center T) * 3 heatedcables P.P. Granieri - Heat extraction and quench limits

  12. Heat extraction from coil inner layer(cable center T) * 3 heatedcables P.P. Granieri - Heat extraction and quench limits

  13. Quench limit estimation 88 mW/cm3 80 mW/cm3 106 • MQXF • 150 mm bore (w/o µ-channels) • 1.9 K constant bath T • uniformheatdeposit 127 mW/cm3 Heatthat must be (uniformly) deposited in the cableuntil the cable center/edgereaches Tc: 247 mW/cm3 155 mW/cm3 39 143 mW/cm3 198 mW/cm3 188 P.P. Granieri - Heat extraction and quench limits

  14. Quench limit estimation 1.96 K 1.92 K • Mid-plane and pole cable temperature for heat deposit in nominal conditions (peak of 3.78 mW/cm3) 2.13 K 2.32 K Comparison tests vs. model *, independently carried out * previous talk from H. Allain P.P. Granieri - Heat extraction and quench limits

  15. Quench limit estimation Comparison at nominal conditions in mid-plane P.P. Granieri - Heat extraction and quench limits

  16. scaled to magnet geometry •  to beconfirmed by a • dedicated test Conclusions • Heat extraction through Nb3Sn insulation was measured • worse than through LHC Nb-Ti insulation below a ΔT of 1.8 K (in the cable center), since the He II contribution is missing • better than through Enhanced Nb-Ti insulation above a ΔT of 5.7 K (in the cable center), because kNb3Sn > KNb-Ti • 3.7 K • 6.4 K • Heat extraction from the cable allows a first estimate of the quench limit: • MQXF mid-plane cable is the most critical: 155 mW/cm3, vs. 4 mW/cm3 expected • MQXF-MQXC will have a quench limit 2 to 3 times those of MB-MQXA-MQXB Numerical model of the experimental tests Thermal measurement of a short model coil Perspectives P.P. Granieri - Heat extraction and quench limits