100 nm

100 nm. Együtt porlasztott 30 at% Mn + 70 at% Cu minta (CM77) – Árpi bácsi vékonyítása. Nagy Cu többletes szemcsék – körülötte vélhetően a második fázis.  szemcsehatár vizsgálata. HREM kép :. Image: 000. Nagyobb nagyítás Nehéz kivenni a szemcse-szemcsehatár részeket

jaser
Download Presentation

100 nm

An Image/Link below is provided (as is) to download presentation Download Policy: Content on the Website is provided to you AS IS for your information and personal use and may not be sold / licensed / shared on other websites without getting consent from its author. Content is provided to you AS IS for your information and personal use only. Download presentation by click this link. While downloading, if for some reason you are not able to download a presentation, the publisher may have deleted the file from their server. During download, if you can't get a presentation, the file might be deleted by the publisher.

E N D

Presentation Transcript

  1. 100 nm Együtt porlasztott 30 at% Mn + 70 at% Cu minta (CM77) – Árpi bácsi vékonyítása Nagy Cu többletes szemcsék – körülötte vélhetően a második fázis  szemcsehatár vizsgálata

  2. HREM kép: Image: 000

  3. Nagyobb nagyítás • Nehéz kivenni a szemcse-szemcsehatár részeket • vélhetően átfedések vannak, ill. a második fázis (egyéb ismeretek alapján) valószínűsíthetően amorf! Image: 002

  4. STEM – HAAD felvétel • Z kontraszt • (+ vastagság is ad kontrasztot) Image: 007 stem

  5. Image int. 635-655 eV - Mn 931-951 eV - Cu Image: 011 stem 7 nm-es vonal mentén EELS spektrum felvétel  Sötét kontrasztot a Mn adja

  6. Másik mintán (65 at% Mn) hordozó határfelület vizsgálata: amorf CuMn réteg „barrier” réteg SiO2

  7. EELS mérés a határrétegen keresztül: