Weekly Group Meeting Report. Renjie Chen Supervisor: Shadi A. Dayeh. HfO 2. InGaAs. 1. Ni-InGaAs Solid - state Reaction. Previous Design. Bonding. Etch Back. Etch InP. Remaining Problems. InP. HfO 2. InGaAs. SiO 2. Membrane broken during fabrication.

finnea
Download Presentation

Weekly Group Meeting Report

An Image/Link below is provided (as is) to download presentation Download Policy: Content on the Website is provided to you AS IS for your information and personal use and may not be sold / licensed / shared on other websites without getting consent from its author. Content is provided to you AS IS for your information and personal use only. Download presentation by click this link. While downloading, if for some reason you are not able to download a presentation, the publisher may have deleted the file from their server. During download, if you can't get a presentation, the file might be deleted by the publisher.

E N D

Presentation Transcript


  1. Weekly Group Meeting Report Renjie Chen Supervisor: Shadi A. Dayeh

  2. HfO2 InGaAs 1. Ni-InGaAs Solid-stateReaction • PreviousDesign Bonding Etch Back Etch InP • RemainingProblems InP HfO2 InGaAs SiO2 Membranebrokenduringfabrication PoorHRTEMImagingduetoHfO2layer HfO2 Ni Si Aperture Frame

  3. NewDesign Directly fabricate Fins on top Spin-coatPMMA Deposit Ni Imbedded CopperTEMgrids BondtoCarrierwafer Si InPLap&etch WithPMMA PMMArelease

  4. CopperTEMAperture • MicroscopeimagebeforeInPetchng

  5. 2. NeuralProbes 1.PhotolithographyprocessinCINT • Innano3 UCSD, the photolithography on sapphire wafer was performed with NR7-1500 photoresist • In CINT, there’s no NR7 resist. The resist I used, AZ-5214 for image reverse, doesn’t work well for sapphire (transparent wafer) • This morning, Don helped me try the resist 5510 which gives a good resolution, however, it does not still stick to sapphire quite well. • I’ll take a look at the data sheet and some literatures to modify the 5510 process.

  6. 300’C 5min + 400’C 10min 300’C 5min + 400’C 20min 300’C 5min + 400’C 30min 2.Nickel silicide bonding test on Sapphire wafer

  7. Thank youQ&A