1 / 11

Vacuum Evaporation

Vacuum Evaporation. Lecture 8 G.J. Mankey gmankey@mint.ua.edu. Monolayer Time. The monolayer time is the time for one atomic layer to adsorb on the surface: t = 1 / (SZA).

Download Presentation

Vacuum Evaporation

An Image/Link below is provided (as is) to download presentation Download Policy: Content on the Website is provided to you AS IS for your information and personal use and may not be sold / licensed / shared on other websites without getting consent from its author. Content is provided to you AS IS for your information and personal use only. Download presentation by click this link. While downloading, if for some reason you are not able to download a presentation, the publisher may have deleted the file from their server. During download, if you can't get a presentation, the file might be deleted by the publisher.

E N D

Presentation Transcript


  1. Vacuum Evaporation Lecture 8 G.J. Mankey gmankey@mint.ua.edu

  2. Monolayer Time • The monolayer time is the time for one atomic layer to adsorb on the surface: t = 1 / (SZA). • At 3 x 10-5 Torr, it takes about one second for a monolayer to adsorb on a surface assuming a sticking coefficient, S = 1. • At 10-9 Torr, it takes 1 hour to form a monolayer for S = 1. • For metals at room temperature S = 1, so the vapor pressure should be >10-6 Torr. Sticking Coefficient S = # adsorbed / # incident Impingement rate for air: Z = 3 x 1020P(Torr) cm-2 s-1 Area of an adsorption site: A » 1 Å2 = 10-16 cm2

  3. Vapor Pressure Curves • The vapor pressures of most materials follow an Arrhenius equation behavior: PVAP = P0 exp(-EA/kT). • Most metals must be heated to temperatures well above 1000 K to achieve an appreciable vapor pressure. • For PVAP = 10-4 mbar, the deposition rate is approximately 10 Å / sec.

  4. Physical Evaporation Substrate • A current, I, is passed through the metal boat to heat it. • The heating power is I2R, where R is the electrical resistance of the boat (typically a few ohms). • For boats made of refractory metals (W, Mo, or Ta) temperatures exceeding 2000º C can be achieved. • Materials which alloy with the boat material cannot be evaporated using this method. Flux Evaporant Boat High Current Source

  5. Limitation of Physical Evaporation • Most transition metals, TM, form eutectics with refractory materials. • The vapor pressure curves show that they must be heated to near their melting points. • Once a eutectic is formed, the boat melts and the heating current is interrupted.

  6. Electron Beam Evaporator Substrate • The e-gun produces a beam of electrons with 15 keV kinetic energy and at a variable current of up to 100 mA. • The electron beam is deflected 270º by a magnetic field, B. • The heating power delivered to a small (~5mm) spot in the evaporant is 15 kV x 100 mA = 1.5 kW. • The power is sufficient to heat most materials to over 1000 ºC. • Heating power is adjusted by controlling the electron current. e-beam Flux Evaporant Crucible B cooling e-gun

  7. Wire Evaporator substrate • This is a "mini" version of the electron beam evaporator. • The entire assembly fits through a 2 3/4 " OD Flange. • Electrons from the heated filament bombard a 2 mm wire that is held at a large positive bias. • The power supply is operated in a current limiting mode and the heating power is P = VbiasIemission. filament cooling shroud 1-2 kV 0-12V

  8. Wire Basket • Direct or alternating current is passed through a pre-fabricated helical wire container. • Evaporant placed in the helix is heated by contact and irradiation. • Heating power is of the order of 100 W or more with a refractory helix with 0.1 - 0.5 mm diameter wire. • Works for Ag, Au, Cu, Cr, Mn, etc. cooling shroud 1-20 V

  9. Knudsen Cell • The crucible is heated by a coil or heater surrounding it. • Crucibles are usually made of boron nitride, alumina, or graphite. • Since there is a large amount of heat, the device is constructed of low outgassing materials and a large amount of cooling is necessary. cooling shroud 1-20 V

  10. ? Measuring and Calibrating Flux • Many fundamental physical properties are sensitive to film thickness. • In situ probes which are implemented in the vacuum system include a quartz crystal microbalance, BA gauge, quadrupole mass spectrometer, Auger / XPS, and RHEED. • Ex situ probes which measure film thickness outside the vacuum system include the stylus profilometer, spectroscopic ellipsometer, and x-ray diffractometer. • Measuring film thickness with sub-angstrom precision is possible.

  11. Frequency Measurement Conversion to Thickness Display Substrate Quartz Crystal Flux Quartz Crystal Microbalance • The microbalance measures a shift in resonant frequency of a vibrating quartz crystal with a precision of 1 part in 106. • fr = 1/2p sqrt(k/m) » f0(1-Dm/2m). • For a 6 MHz crystal disk, 1 cm in diameter this corresponds to a change in mass of several nanograms. • d = m / (rA), so for a typical metal d » 10 ng / (10 g/cm3*1 cm2) = 0.1 Angstroms.