An Image/Link below is provided (as is) to download presentation Download Policy: Content on the Website is provided to you AS IS for your information and personal use and may not be sold / licensed / shared on other websites without getting consent from its author. Content is provided to you AS IS for your information and personal use only. Download presentation by click this link. While downloading, if for some reason you are not able to download a presentation, the publisher may have deleted the file from their server. During download, if you can't get a presentation, the file might be deleted by the publisher.

E N D

Presentation Transcript

  1. Lecture 11.0 Etching

  2. Etching • Patterned • Material Selectivity is Important!! • Un-patterned

  3. Dry Etch An-isotropic dy/dt:dx/dt:6 Gas Phase Reaction with volatile products Frequent use of very reactive species in a Plasma Si Etch SiO2 Etch Metal Etch Wet Etch=Dissolution Isotropic dy/dt:dx/dt:1.2 Si Etch Strong HF SiO2 Etch Strong NH4OH not NaOH (Na ion is bad) Si3N4 Etch Phosphoric Acid Metal Etch Acid Solution (HNO3) Photoresist Solvent H2SO4 Solution x Etching y

  4. Etching • Wet and Dry Etch have very different chemical reactions! • Wet and Dry Etch have similar rate determining steps • Mass Transfer Limiting • Surface Reaction Limiting • Similar mathematics

  5. Wet Etch Chemistries • Layer Etchant • Photoresist H2SO4, H2O2 • SiO2HF, NH4F-HCl-NH4F • Si3N4 ?, HNO3 • Si HF

  6. Dissolution of Layer-Wet Etch • BL-Mass Transfer • A(l)+b B(s) ABb(l) • A= • Acid for metal (B) dissolution • redox reaction • Base for SiO2 (B) dissolution • Solvent for photoresist (B) dissolution

  7. Etch Reactions • Boundary Layer Mass Transfer • Surface Chemical Reaction • Like Catalytic reaction • Product diffusion away from surface Reactant Concentration Profile Product Concentration Profile

  8. Rate Determining Steps X

  9. Global Dissolution Rate/Time • Depends on • Mass Transfer • Diffusion Coefficient • Velocity along wafer surface • Size of wafer • Solubility • Density of film being etched

  10. Wet Etch Reaction • Wafers in Carriage • Placed in Etch Solution • How Long?? • Boundary Layer MT is Rate Determining • Flow over a leading edge for MT • Derivation & Mathcad solution Also a C for the Concentration profile

  11. Local Dissolution Rate/Time • Depends on • Mass Transfer • Diffusion Coefficient • Velocity along wafer surface • Size of wafer • Solubility • Density of film being etched • Position on the wafer • see “photoresist dissolution” example

  12. Dry Etch • Physical Evaporation • Not typically used • Heating chip diffuses dopants out of position • Sputtering from a target • Plasma reactor with volatile reaction product

  13. RF Plasma Sputtering for Deposition and for Etching RF + DC field

  14. Removal Rate • Sputtering Yield, S • S=α(E1/2-Eth1/2) • Deposition Rate  • Ion current into Target *Sputtering Yield • Fundamental Charge

  15. Plasma • Free Electrons accelerated by a strong electric field • Collide with gas molecules and eject e- • Collision creates more free electrons • Free electrons combine with ions to form free radicals • Gas Ions/Free Radicals are very reactive with materials at the wafer surface • Ions non-selective removal • Free Radicals

  16. Plasma Conditions • Reduced Pressure ~100 mtorr • Flow of gases in and out • DC or AC (rf) electric field • Parallel plate electrodes • Other geometries

  17. Dry Etch Chemistries • Gas Surface Etched • O2 Pre-clean • 95%CF4-5% O2 Si • 50%CF4-25%HBr-25%O2 Poly Si • 75%Cl2-25%HBr Metal etch • CF2 layer on side walls prevents wall etching

  18. Plasma • Temperature of Gas molecules, Tgas PVm/Rg • Temperature of Electrons, • Te=e2E2Mg/(6me2m2 kB) • Accelerated by E field between collisions with gas molecules • m= momentum collision frequency=Ng vel m(v) • Te  E/Ng  ERgTg/Ptot>> Tgas • kBTe > Gas Ionization Energy • kBTe > Molecular Dissociation Energy

  19. Plasma Gas Chemistries • Reactant Gases • Physical Etch = Sputtering from chip target • Ar • Chemical Etch • O2 • CF4 • HBr • Cl2 • CHF3 • C2F6 • Mixtures • CF2 deposition (like a teflon polymer layer) prevents side wall etch

  20. Gaseous (Volatile) Products • SiO(g), SiF4(v), SiCl4(v), SiBr4(v) • MFx(v),MClx(v), MBrx(v),

  21. 1st Ionization Energies • O 13.618 eV • Br 11.814 eV • Cl 12.967 eV • F 17.422 eV • H 13.598 eV • Ar 15.759 eV

  22. PreClean O2+ eO2+ + 2e O2+ e2O + e O + e  O- O2+ + e  2O O + s  O-s O + Si(s) s-SiO SiO-s  SiO(g) Metal (M) Etch Cl2 + e  2Cl + e Cl2 Cl2+ + e Cl + s  Cl-s x Cl-M(s)  MClx(g) Simultaneously e + CF4  CF3+ +F+ 2e e + CF3+  CF2 + F CF3+ + CF2 (CF2)n+F Polymer on wall of etch Plasma Etch Mechanism Neutrals are main reactive species!!

  23. Degree of Ionization, α • α = Ni/No= Qi N λD • N = neutral number density • N = Ni+No • λD = Characteristic Diffusion length (mean free path) • Qi= ionization collision cross section • Qi= 0.283 x 10-16(cm2) Pi(E) • Pi(E)= ionization probability

  24. Plasma Transport Equations • Flux, J

  25. Etch Reactions • Boundary Layer Mass Transfer • Surface Chemical Reaction • Like Catalytic reaction • Product diffusion away from surface Reactant Concentration Profile Product Concentration Profile

  26. Etch Reaction • A(g)+bB(s) ABb(g) • -(1/A) dNB/dt= -(1/A)(/MwB)dVB/dt= -(/MwB) dy/dt = - JB • JB= b JA =b Kg(CAg-CAs) BL-MT of A • JB= b JA= b ks CagSurface Reaction • may be catalytic • JB= b JABb = Kg(CABb-s-CABb-g) BL-MT of Abb • JB= b q/Hrxn • q = h (Ts – Tg) BL-HT • q = k dT/dy Conduction in wafer

  27. Rate Determining Steps X

  28. Plasma Etch Rate of Polymers Residue Build-up

  29. Plasma Etch Rate of Polymers

  30. Clean developed Photoresist off of wafer • Wet-chemical stripping agents (solvents) • Incomplete wetting at small scale • Supercritical CO2.-new technology • Zero surface tension • Complete wettability • Good for small line widths