Polypropylene bottle. Funnel. Filter paper. pH-7HEPES buffered saline (HBS-7) or pH-6HEPES buffered saline (HBS-6). (20 ml, 36.5 ℃ ). Y 2 O 3 microspheres (0.05 g). 3 cm, 120 strokes·min -1. ICP analysis (Y). Calculation of dissolution ratio of Yttrium.

niran
Download Presentation

Polypropylene bottle

An Image/Link below is provided (as is) to download presentation Download Policy: Content on the Website is provided to you AS IS for your information and personal use and may not be sold / licensed / shared on other websites without getting consent from its author. Content is provided to you AS IS for your information and personal use only. Download presentation by click this link. While downloading, if for some reason you are not able to download a presentation, the publisher may have deleted the file from their server. During download, if you can't get a presentation, the file might be deleted by the publisher.

E N D

Presentation Transcript

  1. Polypropylene bottle Funnel Filter paper pH-7HEPES buffered saline (HBS-7) or pH-6HEPES buffered saline (HBS-6) (20 ml, 36.5℃) Y2O3 microspheres (0.05 g) 3 cm, 120 strokes·min-1 ICP analysis (Y) Calculation of dissolution ratio of Yttrium molar quantity of Y released from microspheres to HBS total molar quantity of Y contained in 0.05g of microspheres Test of chemical durability of Y2O3 microspheres.

  2. 1.0 YAS - HBS-6 Dissolution ratio of Y / mol% 0.5 Y2O3 - HBS-6 YAS - HBS-7 Y2O3 - HBS-7 0 0 5 10 15 20 25 Time / d Dissolution ratio of YAS glass microspheres, as-prepared Y2O3 and acid-treated Y2O3 microspheres soaked in HBS-6 at 36.5ºC for various periods. （Acid treatment : soaking in HBS-6 at 36.5ºC for 5 d.）

  3. Motor (0.5ml∙min-1) Imaging agent Catheter Liver Y2O3 microspheres Catheter Injection of Y2O3 microspheres.

  4. Y2O3 microspheres Micro X-ray transmission image of the rabbit liver section.

  5. Hyperthermia • Cancer cell are perished at 43ºC • Normal cells are not destroyed up to about 48ºC. Hyperthermia of cancer

  6. Conventional hyperthermia • Hot water • Infrared ray • Ultrasound • Microwave External energy source Difficulty in heating deep-seated tumors locally

  7. Heat generation under alternating magnetic field.

  8. B P : heat generation (W･g-1) f : frequency (Hz) B: magnetization (emu･g-1) H : magnetic field (Oe) H Hysteresis loop Heat generation (P) by magnetic hysteresis loss.

  9. Bioactive matrix of glassy or crystalline CaO∙SiO2 Ferrimagnetic magnetite (Fe3O4) Fe2+ Fe3+ Heattreatment Fe3+ Fe2+ Fe2+ Fe3+ Fe3+ Fe3+ Fe2+ Fe2+ CaO∙SiO2 Glass Glass-ceramic Preparation of bioactive and ferrimagnetic glass-ceramic.

  10. TEM photograph of the glass (composition: Fe2O3 40, CaO∙SiO2 60, B2O3 3, P2O5 3 wt ratio) heat-treated up to 1050ºC; M: magnetite, W: wollastonite

  11. 30 Magnetization / emu∙g-1 20 10 3 -1 -10 -3 1 10 Magnetic field / kOe -10 -20 -30 Magnetization curve of the glass (composition: Fe2O3 40, CaO 40, SiO2 60, B2O3 3, P2O10 3 wt ratio) heat-treated up to 10100ºC.

  12. Bioactive and ferrimagnetic glass-ceramic. (powder 100 - 1100 µmf)

  13. Magnetic Pole 100mm Max Max 100KHz 300 Oe 2100mm 210KW Magnetic Pole Generation of alternating magnetic field