Hardened Concrete Properties

Hardened Concrete Properties. Strength compressive strength 2000-8000 psi tensile strength 200-800 psi flexural strength compression >> tension since concrete is notch sensitivite. Factors Affecting Strength. Curing conditions, humidity temperature w/c , (inversely related) Abram’s law

Download Presentation

Hardened Concrete Properties

An Image/Link below is provided (as is) to download presentation Download Policy: Content on the Website is provided to you AS IS for your information and personal use and may not be sold / licensed / shared on other websites without getting consent from its author. Content is provided to you AS IS for your information and personal use only. Download presentation by click this link. While downloading, if for some reason you are not able to download a presentation, the publisher may have deleted the file from their server. During download, if you can't get a presentation, the file might be deleted by the publisher.

E N D

Presentation Transcript


  1. Hardened Concrete Properties • Strength • compressive strength 2000-8000 psi • tensile strength 200-800 psi • flexural strength • compression >> tension since concrete is notch sensitivite

  2. Factors Affecting Strength • Curing conditions, humidity • temperature • w/c , (inversely related) Abram’s law • air content, (inversely related), short and long term • aggregate characteristics, roughness,grading, minerological. • cement type, composition, fineness, type I vs. type III • cement content (directly related) • Strength porosity relationship • mixing water

  3. Strength and Curing moist cured entire time Strength in air after 7 days 100% in air after 3 days in air entire time 28 time

  4. Factors Affecting Concrete Strength

  5. Durability • Resistance to freezing and thawing • Cracking • Internal Problems • Rebar Corrosion

  6. Resistance to freezing and thawing-Major factors • Air Entrainment • w/c, low water -cement ratio/ water content • volume stability, stiff aggregates with low coefficient of thermal expansion

  7. Air Entrainment • Water gains 9% in volume upon freezing • nighttime freezing followed by daytime thawing, • approximately 40 cycles per year, average. max of 200 cycles per year. • fatigue loading of ice formation within pores • Air Entraining Admixture (AEA) Must provide: • Pore size • Pore spacing • Pore specific surface area

  8. Internal voids

  9. Durability-Cracking • path for harmful material to get into concrete • sulfates- soils • cause severe expansion, and deterioration • chlorides -deicing salts • initiate corrosion • Excessive shrinkage

  10. Durability-internal problems • Alkali-silica reaction • excessive sulfates

  11. Rebar corrosion NaCl - +

  12. Mechanism of corrosion

  13. Corrosion Protection • Proper cover of at least 2” • lower w/c • denser concrete • avoid using chlorides

  14. Review • Strength • Durability • Water Tightness • water cement ratio • Permeability • Volume Stability • shrinkage deformation with no load applied • creep deformation under sustained loading

  15. Load Induced Volume Changes Tangent modulus • Instantaneous, 1D Secant modulus

  16. Load Induced Volume Changes • Time dependant Deformation Creep deformation Time

  17. Creep in Concrete

  18. Creep in Concrete water Creep

  19. Consequences of creep • Loss in pre-stress • possibility of excessive deflection • stressing of non load bearing members

  20. Economy • Cement Content • 50-60$/ton • Aggregates • 5-6 $/ton • minimum cement required at the minimum water cement ratio, with the maximum strength and durability