WP 3 status and follow up

WP 3 status and follow up. Yong Dai Paul Scherrer Institut, 5232 Villigen PSI, Switzerland. WP 11 Meeting, ESS, Lund, 2012.05.08. Outline. Material issues for the target Present status of WP-3 Short term plan Long term plan. Be. Al6061. SS316LN. W. Material issues.

lynn-vang
Download Presentation

WP 3 status and follow up

An Image/Link below is provided (as is) to download presentation Download Policy: Content on the Website is provided to you AS IS for your information and personal use and may not be sold / licensed / shared on other websites without getting consent from its author. Content is provided to you AS IS for your information and personal use only. Download presentation by click this link. While downloading, if for some reason you are not able to download a presentation, the publisher may have deleted the file from their server. During download, if you can't get a presentation, the file might be deleted by the publisher.

E N D

Presentation Transcript


  1. WP 3 status and follow up Yong Dai Paul Scherrer Institut, 5232 Villigen PSI, Switzerland WP 11 Meeting, ESS, Lund, 2012.05.08

  2. Outline • Material issues for the target • Present status of WP-3 • Short term plan • Long term plan

  3. Be Al6061 SS316LN W Material issues

  4. Material issues Operation parameters of various components (to be updated)

  5. Material issues Operation parameters of various components (to be confirmed)

  6. Material issues Operation parameters of various components (to be confirmed)

  7. Material issues Operation parameters of various components (to be updated)

  8. Material issues Materials issues of various components (to be updated)

  9. Present activities • Collect existing data, prepare TDR

  10. Present activities • Collect existing data, prepare TDR Severe cracking of the tungsten due to the thermal gradients. Nelson et al. IWSMT-10, JNM, in press.

  11. Present activities • Start experiments on reference tungsten and W-alloys Tungsten alloy: IT180 in helium with 5% oxygen for 2.5 hours. S. Iyengar, E. Malm, Lund Technical University

  12. Short term (2012-13) plan • Investigations on reference tungsten material Characterization of as-received materials Density, Metallurgy, Hardness Mechanical testing at ESS relevant temperatures Tensile, Fatigue, Bend Microstructural analyses TEM: as-received, after testing SEM: fracture behaviour Erosion experiments at KIT( tbd) Oxidation experiments at LTU (tbd)

  13. Short term (2012-13) plan • Investigations on irradiated tungsten material Mechanical testing and Microstructural analyses of STIP-II (@JAEA) and STIP-V (@PSI) samples Tensile, Hardness, Metallurgy, TEM, SEM, gamma-measurements etc.

  14. Overview of materials irradiated in STIP PIE has been partially done.

  15. Short term (2012-13) plan • Investigations on irradiated tungsten material Mechanical testing and Microstructural analyses of STIP-II (@JAEA) and STIP-V (@PSI) samples Tensile, Hardness, Metallurgy, TEM, SEM, gamma-measurements etc. • Investigations on irradiated structural materials Fatigue testing on irradiated SS 316LN samples

  16. Long term (2014-) plan • Irradiate W samples for ESS, CSNS, etc Irradiate W samples in the next SINQ target Irradiation: 2013-2014, PIE: 2016 - W samples considered: R1: 10 W bullets with Ta, Zy-2, SS cladding, HIP’ed R2: 10 W bullets with Ta, Zy-2, SS cladding, caned R3: 1 W rod with Zy-2 cladding, canned, with 2 TCs R4: Bend, Tensile, TEM samplesin 2 surface conditions, in He R5: Bend, Tensile, TEM samples in 2 surface conditions, in He-5%H