Seminar on Irreversible Hydrocolloid Impression Techniques and Cast Pouring

This seminar will cover the techniques for taking irreversible hydrocolloid impressions and pouring casts, including proper mixing, tray selection, and evaluation of the impressions. It also includes instructions for handling and storing impressions, as well as disinfection and pouring techniques for stone casts.

lopresti
Download Presentation

Seminar on Irreversible Hydrocolloid Impression Techniques and Cast Pouring

An Image/Link below is provided (as is) to download presentation Download Policy: Content on the Website is provided to you AS IS for your information and personal use and may not be sold / licensed / shared on other websites without getting consent from its author. Content is provided to you AS IS for your information and personal use only. Download presentation by click this link. While downloading, if for some reason you are not able to download a presentation, the publisher may have deleted the file from their server. During download, if you can't get a presentation, the file might be deleted by the publisher.

E N D

Presentation Transcript


  1. AM:Seminar (50 min) • Irreversible hydrocolloid impression Quiz (30 min, 20 min Discussion = 50 min) • 11:00 Sign out SKU-1 and SKU-2 typodonts(Marjorie – Pre-Clinical Lab 3218) • Ensure typodont intact, have screwdrivers • Keep boxes, all materials with typodonts to return in December • Do not Print on Boxes • Irreversible hydrocolloid experiments • Demo of mixing irreversible hydrocolloid impressions/pouring casts • Have bowls, spatulas, Whip Mix vacuum mixing bowls • PM Lab: Typodont impression & Pour Max. cast • Evaluate impression/cast yourself, then assessed by instructors, sign formative evaluations

  2. Student ____________________ Preliminary Alginate Impressions Date / / Initials_______ Instructor #_____ q Unacceptable q Correctable q Acceptable Student q Unacceptable q Correctable q Acceptable Instructor __________ q Accurate recording of all critical anatomy q Material properly mixed as indicated by impressions q Minimum of voids q Trays properly selected and centered over the ridges q Minimal areas where trays have contacted tissues Diagnostic Cast Evaluation Date / / Initials_______ Instructor #_____ q Unacceptable q Correctable q Acceptable Student q Unacceptable q Correctable q Acceptable Instructor __________ q No significant bubbles or flaws in stone q Base approximately parallel to ridge and approximately l/2 inches thick (minimum) q Evidence of a dense stone surface q Clean and well trimmed q Includes all anatomical surfaces

  3. Today • Questions from last day • Course Outline - online • Manuals Page 97-103 • Readings - excellent • Questions about irreversible hydrocolloid or trimming casts?

  4. Next Week • Surveying • Readings in VS, Manual • In class, sort yourself by row, depending on your seminar leader

  5. Selection of a Stock Tray • 5 -7 mm between tray & tissues • Bulk for strength & accuracy of material • Just short of vestibule • Slightly beyond vibrating line

  6. Stock Tray Selection • Compound on peripheries if needed • Extension only to provide coverage of critical anatomy • Not for displacing vestibular tissues

  7. Pre-Measure Material • Infection control • Do not take containers to your operatory • Do not handle containers with contaminated gloves/hands

  8. Handling the Material • Do not leave containers open in a humid environment • Humidity & high temperatures cause deterioration

  9. Use Separate Bowls Alginate • Gypsum can cause acceleration of setting of alginate • Alginate contamination can decrease strength of casts Stone

  10. Measuring Alginate • Fluff the powder before measuring • Ensure no large voids

  11. Measuring Alginate • Do not tap the scoop more than once or twice • Compacts the powder • Thicker mix

  12. Preparations • Measuring by weight is more accurate than by volume • Ratio of 1 scoop powder : 1 measure water • 3 scoops of powder is sufficient for most arches

  13. Regulating Set Time • Regulate with water temperature • Water/powder ratio can affect tear strength & viscosity

  14. Mixing Alginate • Mix for up to 45 seconds • Smooth creamy consistency • No lumps or powder should remain

  15. Mixing

  16. Fill Tray

  17. Making the Impression • Wipe alginate onto the occlusal surfaces of any teeth

  18. Making the Impression • Don't bottom out on the teeth or the residual ridge • Distort the tissue or move teeth • Stone leaks between alginate & tray & produces distorted cusp

  19. Making the impression • Wait to remove impression until the material is firm • Approximately one minute after initial set

  20. Removal • Lift lip up to break the seal against tissues • Several drops of water • Remove rapidly, to prevent significant permanent deformation

  21. Impression Storage • Wrap in a damp towel • Wring to eliminate excess water • Pour within 12 minutes • Minimizes distortion • Support impression by handle or tray until cast poured

  22. Evaluating Irreversible Hydrocolloid Impressions • Properly mixed • Smooth surface

  23. Evaluating Irreversible Hydrocolloid Impressions • Tray centered over ridge

  24. Evaluating Irreversible Hydrocolloid Impressions • No significant tissue/tooth contact

  25. Evaluating Irreversible Hydrocolloid Impressions • No-large voids in the impression

  26. Evaluating Irreversible Hydrocolloid Impressions • All critical anatomy recorded • Hamular notches • Retromolar pads • Vestibules, etc.

  27. Disinfection • Rinse the impression • Place in zip lock bag, pour in disinfectant to cover all surfaces • Seal for 10 minutes • Remove and rinse prior to pouring stone

  28. Mixing Stone • Weigh powder • Measure water • Vacuum mix • Less time to complete than hand mixing • Stronger cast

  29. Two pour technique • Pour stone into impression • Wait for stone to set (~ 30 minutes) • Invert impression with set first pour onto base stone • Superior surface strength

  30. Two Pour Technique • Use vibrator & flow the stone into the impression slowly • Modulate speed of pouring by tilting the tray back and forth

  31. Two Pour Technique • If impression fills too quickly-voids • To delay filling: • Tilt impression in opposite direction of the flow of the stone • Reduce speed of vibrator • Press impression less firmly against vibrator

  32. Two Pour Technique • Leave rough areas on the exposed surface of the stone • Helps attach base

  33. Two Pour Technique • Make a patty of stone • Invert impression with the first pour onto the base • Adapt new stone to the existing stone

  34. Two Pour Technique • Trim excess stone from the base with the spatula while the stone is still soft

  35. Two Pour Technique • Separate impression from cast after 30 minutes

  36. Trimming Casts • Model moist for trimming • Debris from trimmer will not attach

  37. Trimming Casts • Soak the model by immersing • in slurry water • just base of cast contacting tap water

  38. Trimming Casts • Prolonged immersion in tap water can lead to erosion of the cast

  39. Trimming Diagnostic Casts • Cast should be minimum of 10-12mm (.5 inch) in thinnest part • Trim the base on the model trimmer parallel to ridges • Leave the mucous membrane reflection intact for making a custom tray

  40. Trimming Master Casts • Boxed and trimmed with a 3mm wide by 3mm deep land area • Aids in processing of acrylic • Diagnostic casts (no land area) • Used for making custom trays • Land area omitted so material is easier to trim & remove from the cast

  41. Outline of Bases for Trimmed Casts • Follow the contour of the ridges, with rounded angles