1 / 27

Radiation tolerance of commercial 130nm CMOS technologies for High Energy Physics Experiments

Radiation tolerance of commercial 130nm CMOS technologies for High Energy Physics Experiments. Federico Faccio for the CERN(PH/MIC)-DACEL * collaboration. * DACEL is an INFN project involving the INFN sections of Bari, Bergamo, Bologna, Firenze, Padova, Pavia and Torino. Outline.

linus
Download Presentation

Radiation tolerance of commercial 130nm CMOS technologies for High Energy Physics Experiments

An Image/Link below is provided (as is) to download presentation Download Policy: Content on the Website is provided to you AS IS for your information and personal use and may not be sold / licensed / shared on other websites without getting consent from its author. Content is provided to you AS IS for your information and personal use only. Download presentation by click this link. While downloading, if for some reason you are not able to download a presentation, the publisher may have deleted the file from their server. During download, if you can't get a presentation, the file might be deleted by the publisher.

E N D

Presentation Transcript


  1. Radiation tolerance of commercial 130nm CMOS technologies for High Energy Physics Experiments Federico Faccio for the CERN(PH/MIC)-DACEL* collaboration * DACEL is an INFN project involving the INFN sections of Bari, Bergamo, Bologna, Firenze, Padova, Pavia and Torino

  2. Outline • Past, present and future: • 250nm CMOS with HBD approach for the LHC experiments • Motivation for moving to 130nm CMOS • Irradiation results (TID) for 3 different manufacturers (Foundries) • SEE results • Conclusion F.Faccio

  3. TID effects in CMOS technologies (1) Parasitic MOS 2. Effects in the thick lateral isolation oxide (STI) between source and drain of a transistor Parasitic channel Field oxide Bird’s beak Source Drain 1. Effects in the thin gate oxide F.Faccio

  4. TID effects in CMOS technologies (2) Metal 1 Metal 1 STI OXIDE STI OXIDE STI OXIDE N+ diffusion N+ diffusion N+ diffusion STI STI N+ diffusion N+ diffusion N+ diffusion + + + + + + + + + + + + + + SUBSTRATE SUBSTRATE 3. Effects in the isolation oxide (STI), in between n-well or diffusions F.Faccio

  5. Past and present: 250nm CMOS G S D Hardness By Design (HBD) approach has been used: ELT transistors F.Faccio

  6. Past and present: 250nm CMOS G V V V SS SS DD OXIDE + + + + + + N+ DRAIN + + P+ GUARD N+ SOURCE + + + + p+ guardring S D SUBSTRATE Hardness By Design (HBD) approach has been used: guardrings F.Faccio

  7. HEP Foundry Service in 250nm CMOS • MPW service organized for more than 100 different ASICs • More than 20 different designs in production (some are multi-ASIC) • More than 2000 wafers (8-inch) produced! F.Faccio

  8. Motivation to move to 130nm • LHC upgrades & SLHC will require higher-performance ICs, tolerant to larger TID levels • 250nm is already an old process and will not stay around much longer • More-modern CMOS processes have the potential of higher TID tolerance and much better performance • What is the radiation tolerance? HBD needed? F.Faccio

  9. Outline • Past, present and future • Irradiation results (TID) for 3 different manufacturers (Foundries) • Experimental details • Core transistors, linear layout • Core transistors, ELT • I/O transistors • Need for guardrings… • SEE results • Conclusion F.Faccio

  10. Test structures and measurement setup • 3 commercial 130nm CMOS processes: foundries A,B and C • Some are PMDs from foundry, some custom-designed test ICs • NMOS and PMOS transistors, core and I/O devices (different oxide thickness), FOXFETs • Testing done at probe station – no bonding required • Irradiation with X-rays at CERN up to 100-200Mrad, under worst case static bias • Further studies (p source, reliability, SEGR, noise, …) are under way F.Faccio

  11. Core NMOS transistors, linear layout (1) • Narrow transistors (W < 0.8mm): • An apparent Vth shift (decrease) for narrow channel transistors • The narrower the transistor, the larger the Vth shift (RINCE) Foundry A, 0.16/0.12 • Wide transistors (W > 1mm): • When the transistor is off or in the weak inversion regime: • Leakage current appears (for all transistor sizes) • Weak inversion curve is distorted Foundry A, 2/0.12 F.Faccio

  12. Core NMOS transistors, linear layout (2) annealing pre-rad pre-rad • Effect on the leakage current • Peak in leakage at a TID of 1-5Mrad • Peaking dependent on dose rate and temperature, difficult to estimate in real environment Foundry A Foundry B Foundry C F.Faccio

  13. Core NMOS transistors, linear layout (3) • Effect on the threshold voltage • Peak in Vth shift at a TID of 1-5Mrad (A and C) • The narrower the transistor, the larger the Vth shift (RINCE) • Peaking dependent on dose rate and temperature, difficult to estimate in real environment Foundry A Foundry B Foundry C F.Faccio

  14. Radiation-induced edge effects - NMOS E field lines E field lines Polysilicon Polysilicon gate gate - - + + + + ID - - + + + + STI STI - + + - + + STI STI Oxide trapped charge Interface states Depletion region Depletion region Main transistor Lateral parasitic transistor 0 VGS F.Faccio

  15. Core PMOS transistors, linear layout (1) Foundry A, 0.16/0.12 • No change in the weak inversion regime, no leakage • An apparent Vth shift (decrease) for narrow channel transistors • The narrower the transistor, the larger the Vth shift Foundry B, 0.14/0.13 Foundry C, 0.28/0.12 F.Faccio

  16. Radiation-induced edge effects - PMOS E field lines E field lines Polysilicon Polysilicon gate gate - + + + + + ID - + + + + + STI STI + + + + + + STI STI Oxide trapped charge Interface states Depletion region Depletion region Main transistor Lateral parasitic transistor 0 VGS F.Faccio

  17. Core NMOS transistors, enclosed layout (ELT) Example: Foundry A • The radiation hardness of the gate oxide is such that practically no effect is observed – verified for 2 foundries (A up to 140Mrad, B up to 30Mrad) F.Faccio

  18. I/O transistors, linear layout Foundry A, NMOS 0.36/0.24 • Large effect for all sizes, but more important for narrow channel transistors • Results different with Foundry, but for all enclosed layout is required already for TID levels of the order of 50-100krad (NMOS) • Effect is not negligible also for ELTs: relevant Vth shift! Foundry A, PMOS 2/0.24 F.Faccio

  19. Are guardrings systematically needed? (1) • FoxFETs are “Field Oxide Transistors” • Good to characterize isolation properties with TID • Structures available in only 1 technology (1 only Foundry) 1. N+diffusion to N+diffusion (source/drain of two neighbor NMOS transistors) F.Faccio

  20. Are guardrings systematically needed? (2) G G D D D S S S Metal 1 Metal 1 STI OXIDE STI OXIDE STI OXIDE N+ WELL CONTACT N+ WELL CONTACT N+ WELL CONTACT N+ diffusion STI oxide STI oxide + + + + + + + + + + N WELL N WELL N WELL SUBSTRATE SUBSTRATE Vg=2.5V Vg=2.5V 2. N+diffusion to Nwell (Nwell with PMOS logic to drain/source of NMOS logic) F.Faccio

  21. Are guardrings systematically needed? (3) Vdd Vdd Vdd N-well N-well N-well Realistic test structure with series of Inverters + DFF along 350um, and with different separation between n-well (PMOS logic) and NMOS: Without guardring Partial guardring Full guardring F.Faccio

  22. Are guardrings systematically needed? (4) F.Faccio

  23. Outline • Past, present and future • Irradiation results (TID) for 3 different manufacturers (Foundries) • SEE results • Conclusion F.Faccio

  24. SEE results: the SRAM circuit • 16kbit SRAM test circuit designed using the SRAM generator from a commercial library provider – not dedicated rad-tolerant design! • Test performed with Heavy Ions at the Legnaro National Laboratories accelerator in June 2005 F.Faccio

  25. Heavy Ion irradiation results • Test at Vdd=1.5 and 1.25 V, results very similar • Sensitivity to very low LET values (threshold below 1.6 MeV/cm2mg) • Comparison with 0.25mm memory (rad-tol design!!): • Cross-section 15-30 times larger in LHC environment F.Faccio

  26. Challenges for 130nm • Technology more expensive than ¼ micron: • Strong push for first working silicon • Strong push for common solutions to similar problems • Technology more complex than ¼ micron: • Reduced Vdd, difficult for analog • Physical effects can not be ignored: proximity effects, filling requirements, “cheesing”, … • As a consequence, design rules are considerably more complex (impressive growth of the design manual) • Larger number of tools is needed • Competence in radiation effects are also required • If non-enclosed transistors are used • To protect circuits from SEEs • All competences in technology, design techniques and tools necessary for a successful project are more difficult to gather in a group of small size F.Faccio

  27. Conclusion • HBD in quarter micron has made LHC electronics possible/affordable: large scale application of HBD is a reality! • Natural radiation tolerance of 130nm better than for the quarter micron technology (not for I/O transistors), but Mrad-level still requires HBD for reliable tolerance • Large effort required to develop library, acquire tools, master the technology: • Working with 130nm is MUCH more complex and expensive; pressure to get quickly to working silicon • CERN is preparing a frame contract with 1 selected Foundry, to develop library/design kit/design flow serving the whole HEP community F.Faccio