New high resolution spectrometer for nanometer level elemental depth profiling

New high resolution spectrometer for nanometer level elemental depth profiling. M. Laitinen, M. Rossi, P. Rahkila, H. J. Whitlow and T. Sajavaara. Department of Physics, P.O.B 35, FIN-40014 University of Jyväskylä, Finland email: mikko.i.laitinen@jyu.fi.

jerrod
Download Presentation

New high resolution spectrometer for nanometer level elemental depth profiling

An Image/Link below is provided (as is) to download presentation Download Policy: Content on the Website is provided to you AS IS for your information and personal use and may not be sold / licensed / shared on other websites without getting consent from its author. Content is provided to you AS IS for your information and personal use only. Download presentation by click this link. While downloading, if for some reason you are not able to download a presentation, the publisher may have deleted the file from their server. During download, if you can't get a presentation, the file might be deleted by the publisher.

E N D

Presentation Transcript


  1. New high resolution spectrometerfor nanometer levelelemental depth profiling M. Laitinen, M. Rossi, P. Rahkila, H. J. Whitlow and T. Sajavaara Department of Physics, P.O.B 35, FIN-40014 University of Jyväskylä, Finland email: mikko.i.laitinen@jyu.fi

  2. The New Spectrometer:What does it look like and how does it works ?

  3. The new spectrometer:How does it look like and how it works ? • In principleallsampleelementscanbequantified M. Putkonen, T. Aaltonen, M. Alnes, T. Sajavaara, O. Nilsen, and H. Fjellväg, Atomic layer deposition of lithium containing thin films, J. Mater. Chem. 19 (2009) 8767.

  4. Time-of-Flight – Elastic Recoil Detection (ToF-ERD) • Quantitative method: • Energy from well known kinematics • Time-resolution better than E-detector resolution • Element (mass) from ToF and E signals • Scattering propability to detectors • Coulombic interaction potential • Depth information • Semi-empiric parametrization for energy loss

  5. TOF detection efficiency • All sample elements, also H, can be detected • Can get better only by getting more electrons out of the carbon foils • -> coating the carbon foils with Atomic Layer Deposition, ALD • Better than 98% for C • and heavier masses • ~ 90 % for 4He • ~ 10-60% for H Sample holder backwall Measured with 1600 V MCP voltage, 3000 V mirror voltage and 200x preamplifier

  6. Time-of-flight resolution • Timing with external 200x preamplifier, CFD and TDC • Current resolution timing resolution 300 ps for 4.5 MeV incident He ions scattered from 1 nm Au film on Si substrate • Timing:300 ps equals ~ 4mm for 4.4 MeV He • Upgrade:fastpreamplifiers inside the chamber 300 ps

  7. Diamond-like carbon films • 2.3 µm thick diamond-like-carbon film on Si • Measured with 9 MeV 35Cl • All isotopes can be determined for light masses • Light elements can be well quantified (N content 0.05±0.02 at.%)

  8. First results: 8.6 nm Al2O3 • Atomic layer deposited Al2O3 film on silicon (Prof. Ritala, U. of Helsinki) • Density of 2.9 g/cm3 and thickness of 8.6 nm determined with XRR (Ritala) • Elemental concentrations in the film bulk as determined with TOF ERDA are O 60±3 at.%, Al 35±2 at.%, H 4±1 at.%. and C 0.5±0.2 at.%.

  9. Example with high mass element • AtomiclayerdepositedRufilm on HF cleanedSi(Dr. Kukli, U. of Helsinki) • Bulkdensity of 12 g/cm3used in the depthprofiles • Monte Carlo simulationsneeded for gettingreliablevalues for lightimpurities

  10. Future improvements: New TOF-gate • ALD-coated thin C-foils for high electron yields (coming) • Timing from backwards emitted electrons • Position (scattering angle) from forward emitted electrons and delay line anode • Anodes made on PCB Commercial MCP stacksby TECTRA

  11. Future improvements: Gas ionization detector TOF-E results from Paul Scherrer Institute Incident ion 12 MeV 127I and borosilicate glass target Nucl. Instr. and Meth. B248 (2006) 155-162

  12. Conclusions • New high resolution spectrometer has been built in JYFL • ToF-ERDA provides unique capabilities for quantitative depth profiling of all the sample elements, including hydrogen • Depth resolution of <2 nm at the surface has been reached in Jyväskylä, further improvements coming within months 2nd timing detector, 10 μg/cm2 C-foil 1st timing detector, 3 μg/cm2 C-foil

  13. Acknowledgements Mikko Ritala, U. of Helsinki Matti Putkonen, Beneq Oy and Aalto University Kaupo Kukli, U. of Helsinki TEKES-EU Regional Funds Academy of Finland TEKES Accelerator based materials physics goup in JYFL

  14. 1st timing detector, 3 μg/cm2 C-foil 2nd timing detector, 10 μg/cm2 C-foil