Demir – Sementit ( Fe -Fe 3 C) Sistemi

Demir – Sementit ( Fe -Fe 3 C) Sistemi. 0,3. Demir – Sementit ( Fe -Fe 3 C) Sistemi—Ana Fazlar. Fe -Fe 3 C Sistemindeki Fazlar. α - F errit – HMK Demir ve Karbonun katı çözeltisi • Oda sıcaklığında demirin kararlı yapısıdır.

hedley-hewitt
Download Presentation

Demir – Sementit ( Fe -Fe 3 C) Sistemi

An Image/Link below is provided (as is) to download presentation Download Policy: Content on the Website is provided to you AS IS for your information and personal use and may not be sold / licensed / shared on other websites without getting consent from its author. Content is provided to you AS IS for your information and personal use only. Download presentation by click this link. While downloading, if for some reason you are not able to download a presentation, the publisher may have deleted the file from their server. During download, if you can't get a presentation, the file might be deleted by the publisher.

E N D

Presentation Transcript

  1. Demir – Sementit (Fe-Fe3C) Sistemi 0,3

  2. Demir – Sementit (Fe-Fe3C) Sistemi—Ana Fazlar

  3. Fe-Fe3C Sistemindeki Fazlar • α-Ferrit– HMK Demir ve Karbonun katı çözeltisi • • Oda sıcaklığında demirin kararlı yapısıdır. • • Maksimum karbon (C)çözünürlüğüağırlıkça % 0,022dir. • • 912 °C’ nin üzerine ısıtıldığında YMK(γ)-östenit fazına dönüşür. • γ-Östenit–YMK Demir ve Karbonun katı çözeltisi • • Maksimum karbon (C)çözünürlüğüağırlıkça %2,1 dir. • • 1395 °C’nin üzerine ısıtıldığında HMK δ-ferritfazına dönüşür. • • Ötektoid sıcaklığın (727 ° C) altında kararlı değildir.

  4. Fe3C– Sementit (Demir Karbür) • • Bir intermetalik bileşik olup yarı kararlı yapıdadır. Oda sıcaklığında yapısını korur ancak 650 oC’nin üzerinde temperlendiğinde çözünerek α-Fe ve grafit’e dönüşür. • Fe-C Sıvı Çözeltisi • (γ) Östenit

  5. Ötektoid dönüşüm , % 0,8 C ve 723 oC (γα+ Fe3C) Östenit Perlit