Carbon Nanotubes as Injection Electrodes for TFTs

Kevin Wang Nanofabrication Seminar 2008/4/27. Carbon Nanotubes as Injection Electrodes for TFTs. Concept. Aguirre, C.M., Martel, R. et al. Engineering Physics, EP Montréal Chemistry, U. of Montréal Backgated. Thin Film. Pentacene Island. Fabrication – Island. Double-wall nanotubes

dylan
Download Presentation

Carbon Nanotubes as Injection Electrodes for TFTs

An Image/Link below is provided (as is) to download presentation Download Policy: Content on the Website is provided to you AS IS for your information and personal use and may not be sold / licensed / shared on other websites without getting consent from its author. Content is provided to you AS IS for your information and personal use only. Download presentation by click this link. While downloading, if for some reason you are not able to download a presentation, the publisher may have deleted the file from their server. During download, if you can't get a presentation, the file might be deleted by the publisher.

E N D

Presentation Transcript

  1. Kevin Wang Nanofabrication Seminar 2008/4/27 Carbon Nanotubes as Injection Electrodes for TFTs

  2. Concept • Aguirre, C.M., Martel, R. et al. • Engineering Physics, EP Montréal • Chemistry, U. of Montréal • Backgated • Thin Film • Pentacene Island

  3. Fabrication – Island • Double-wall nanotubes • Form gaps - electrical breakdown • Contacts – optical lithography • Ti and Pd by e-beam evaporation • Anneal (vacuum) 550°C, 1h • Post-Breakdown

  4. Fabrication – Island (cont.) • Spin-coat precursor • 2 mg/mL chloroform solution • 13,6-N-sulfinylacetamido- pentacene • Converts to pentacene (170-200°C) • Asymmetric CNT – Pd

  5. Fabrication – TFT • SWNTs (10 nanotubes/μm2) • Ti contacts, optical • Lithography, liftoff • Sonicate free nanotubes • Anneal (vacuum) 550°C, 1h • Pentacene (50nm) • Vacuum sublimation (0.2nm/s)

  6. Fabrication – TFT (cont.) • W/L = 200μm/20μm • Au or Ti, 30 nm thick

  7. Performance – Island • 40 nm gap device • Ion/Ioff = 100 • Ion = 2nA (Vds = 8V) • Superlinear IV • Poor gate control • tox = 20 nm • Subthreshold Swing • 1.3V/dec

  8. Asymmetric CNT-Pd • Injection from CNT side • 21x more current • CNT good emitter, poor collector?

  9. Performance - TFT • CNT array – ideal linear behavior • Au, Ti – nonlinear, large contact barriers • Barrier at CNT lowered by • E-field enhancement • Molecular energy shift

  10. Performance – TFT (cont.)

  11. Conclusion • Carbon nanotubesenhance transistor current • Effective barrier lowering at CNT-Pentacene interface

  12. Additional • Ti contacts