An Image/Link below is provided (as is) to download presentation Download Policy: Content on the Website is provided to you AS IS for your information and personal use and may not be sold / licensed / shared on other websites without getting consent from its author. Content is provided to you AS IS for your information and personal use only. Download presentation by click this link. While downloading, if for some reason you are not able to download a presentation, the publisher may have deleted the file from their server. During download, if you can't get a presentation, the file might be deleted by the publisher.

E N D

Presentation Transcript


  1. Utilizing Carbon Nanotubes to Improve Efficiency of Organic Solar Cells ENMA 490 Spring 2006

  2. Motivation • Problem: Lack of power in remote locations • Possible solution: Organic solar cells are less expensive and more portable than conventional solar cells • Main issue: Inadequate efficiency

  3. What We Did • Focus: Increase the efficiency through the addition of carbon nanotubes • Research Goal: Model a basic device and propose an ideal structure for more efficient power generation • Experimental Goal: Build selected devices to test parameters

  4. Research Team Erik Lowery Nathan Fierro Adam Haughton Richard Elkins Project Organization Experimental Team Erin Flanagan Scott Wilson Matt Stair Michael Kasser

  5. How Organic Solar Cells Work • Photon absorption, excitons are created • Excitons diffusion to an interface • Charge separation due to electric fields at the interface. • Separated charges travel to the electrodes. High Work Function Electrode Donor Material E Acceptor Material Low Work Function Electrode

  6. Critical Design Issues • Exciton creation via photon absorption • Material absorption characteristics • Exciton diffusion to junction • Interfaces within exciton diffusion length (nanoscale structure) • Charge separation • Donor/Acceptor band alignment • Transport of charge to electrodes • High charge mobility

  7. The Active Layer • Composed of an electron donor and electron acceptor • 3 types of junctions • Bilayer • Diffuse Bilayer • Bulk heterojunction • Usually the excitons from the electron donor are responsible for the photocurrent

  8. Electron Acceptor • MEH-PPV-CN • Electron acceptor • CN group • Increased band alignment • Higher electron affinity • Electrical Properties • Poor charge mobility • Optical Properties • Peak emission at 558 nm • Peak absorption at 405 nm (~3eV) Solar Spectrum MEH-PPV-CN Irradiance (W/m^2) Absorption (arb. Units) Energy, eV

  9. Electron Donor • Carbon Nanotubes • Orders of magnitude better conductance than polymers • Our nanotubes specifications (Zyvex) • Functionalized • Diameter: 5-15 nm • Length: 0.5-5 microns • MWNT (60% metallic 40% semiconducting) AFM Amplitude Scan

  10. Electron Donor (cont.) • Carbon Nanotubes • Optical Properties • Diameter • SW vs. MW • Chirality (Semi-conducting vs metallic)

  11. Modeling • Model Geometry • Photogeneration of Excitons • Exciton Transport to Junction • Electron Hole Separation • Charge Transport to Electrode

  12. Model Geometry Incoming Light X=0 X=L ITO CNT MEH-PPV-CN Al Define A to be the area perpendicular to the incoming light.

  13. Photogeneration of Excitons

  14. Photogeneration of Excitons • Start with Beer-Lambert absorption equation: • Arrive at expression for # Photons absorbed per unit area, per unit time • Use either blackbody approximation or numerical data for the solar spectrum (Sinc)

  15. Exciton Transport to Junction • Diffusion Model • Initial and Boundary Conditions Decay Term, simple time-dependent model Source Term, accounts for exciton generation Diffusion Term Excitons destroyed at CNT/Electrode Interface Excitons destroyed at CNT/Polymer Junction Initially, assume ground state, no excitons anywhere.

  16. Charge Transport to Electrode • Holes move along CNTs • Hole Mobility ~ 3000 cm2/Vs • Electrons move along MEH-PPV-CN • Electron Mobility ~ 3.3x10-7 cm2/Vs • Current density is directly related to mobility; Increased mobility leads to higher current densities.

  17. Modeling Summary • CNT/MEH-PPV junctions within diffusion length of exciton generation points • Thickness Optimization Problem: • Maximizing thickness gives more excitons • Minimizing thickness leads to higher current

  18. Ideal Structure ITO Nanotubes Nanoscale mixing MEH-PPV-CN Al Nanoscale mixing allows excitons to charge separate before they recombine Structure allows for the bulk heterojunction and minimizes the travel distance to the electrodes

  19. Experimental Design • Experimental design parameters • CNT concentration • Method of mixing • Spin Parameters • Solvents

  20. Device Process Flow ITO .4 mm .7 mm 2.5 mm .2 mm

  21. Device Process Flow PEDOT ~100nm Al contacts ~600 Å

  22. Active Layer

  23. Device Process Flow LiF ~ 20 Å Al contacts

  24. Final Product

  25. Nanotube

  26. Experimental Results Pure polymer devices acted like diodes. Light emission was observed at higher currents (8 mA)

  27. Experimental Results Pure CNT acted like a resistor, R >350Ω.

  28. Experimental Design Issues We Addressed • Nanotube Processing • Method of dispersion • Type of solvent • Concentration CNT • amount of CNT in solvent • CNT to Polymer • Diffused junction vs. bulk heterojunction

  29. Results Summary • Absorption spectra measured • AFM to check spatial distribution of nanotubes • No successful devices made • Possible causes: • CNT shorting • Functionalized CNTs might be a problem

  30. Conclusions • Experimental: • Device process recipe needs to be refined • Solve experimental design problems to work on successful device • Modeling: • Diffusion model considerations point towards improving efficiency by creating nanoscale structure • Need to consider charge transport in more detail

  31. Acknowledgements • We would like to thank the following people/organizations: • Dr. Gary Rubloff • Dr. Danilo Romero • Laboratory for Physical Sciences • Zyvex