An Image/Link below is provided (as is) to download presentation Download Policy: Content on the Website is provided to you AS IS for your information and personal use and may not be sold / licensed / shared on other websites without getting consent from its author. Content is provided to you AS IS for your information and personal use only. Download presentation by click this link. While downloading, if for some reason you are not able to download a presentation, the publisher may have deleted the file from their server. During download, if you can't get a presentation, the file might be deleted by the publisher.

E N D

Presentation Transcript

  1. 烷烃氧化数据分析 黄宇 2012-11-21

  2. Pt/Al2O3体系

  3. Pt/Al2O3体系 1.1 老化后Pt/Al2O3 1.2 氧气浓度关系 1.3 小结 1

  4. 因为老化后Pt-AL2O3的Pt颗粒变大（XRD出现Pt的峰，计算得大约17.8nm），而大颗粒的Pt不容易被氧化，从而促进活性的提高。因为老化后Pt-AL2O3的Pt颗粒变大（XRD出现Pt的峰，计算得大约17.8nm），而大颗粒的Pt不容易被氧化，从而促进活性的提高。 Pt/W/Al样品老化后活性降低 0.2g 催化剂，总流量：1L/min，空速：36,000 h-1，800ppm C3H8，0.8% O2； 3 Yazawa, Y., H. Yoshida, et al. (2002). Applied Catalysis A: General.

  5. 1.1 老化后Pt/AL2O3与Pt/W/AL2O3的对比 猜想：Pt-W-AL2O3老化后活性变差不是因为W的状态发生变化，而是与Pt颗粒的长大有关。 5

  6. Pt/W/Al新鲜活性比Pt/Al新鲜样品活性好很多 W的加入促进了Pt-AL2O3的活性，这是因为Pt与其附近的WOx相互作用，使得Pt处于缺电子状态，形成了更多的具有高丙烷氧化活性的亚稳态的Pta+. 2 Wu, X., L. Zhang, et al. (2012). Journal of Hazardous Materials

  7. 1.1 老化后Pt/AL2O3与Pt/W/AL2O3的对比 在老化后的Pt-AL2O3上负载了W活性并没有恢复到新鲜 Pt-W-AL2O3的活性 4 Yazawa, Y., H. Yoshida, et al. (2002). Applied Catalysis A: General.

  8. 1.2 氧气抑制作用 6

  9. 1.2 Pt颗粒大小与氧气抑制作用的关系 老化后的Pt-AL2O3（红线），氧气的抑制作用更加明显。 8

  10. 1.3 小结 丙烷氧化机理研究 Pt/AL2O3体系 老化后变差的原因 Pt与氧气抑制作用的关系 9

  11. 谢谢 9