环氧涂层 / 碳钢间的界面化学键合研究

环氧涂层 / 碳钢间的界面化学键合研究. 背 景： 涂层 / 金属间附着力过低是导致涂层失效的主要原因之一，这主要源于现役涂层 / 金属间界面结合多为物理作用，附着力过小。故可以寻求化学键合的方法增加界面附着力以提高涂层的寿命。. FTIR 结果 ： 1760 cm -1 处为羰基的伸缩振动峰， 910 cm -1 处为环氧特有的伸缩振动峰，该图证明 E44-AC 既含有可与金属键合的羰基基团，又含有可与环氧树脂互容和固化的环氧基团。. 活性树脂 E44-AC 的制备. 实验材料：环氧树脂（ E44 ）、酒石酸（ AC ）、 TDI. -1. -1. 910cm.

zaza
Download Presentation

环氧涂层 / 碳钢间的界面化学键合研究

An Image/Link below is provided (as is) to download presentation Download Policy: Content on the Website is provided to you AS IS for your information and personal use and may not be sold / licensed / shared on other websites without getting consent from its author. Content is provided to you AS IS for your information and personal use only. Download presentation by click this link. While downloading, if for some reason you are not able to download a presentation, the publisher may have deleted the file from their server. During download, if you can't get a presentation, the file might be deleted by the publisher.

E N D

Presentation Transcript

  1. 环氧涂层/碳钢间的界面化学键合研究 背 景：涂层/金属间附着力过低是导致涂层失效的主要原因之一，这主要源于现役涂层/金属间界面结合多为物理作用，附着力过小。故可以寻求化学键合的方法增加界面附着力以提高涂层的寿命。 FTIR结果：1760 cm -1处为羰基的伸缩振动峰，910 cm-1处为环氧特有的伸缩振动峰，该图证明E44-AC既含有可与金属键合的羰基基团，又含有可与环氧树脂互容和固化的环氧基团。 活性树脂E44-AC的制备 实验材料：环氧树脂（E44）、酒石酸（AC）、TDI -1 -1 910cm 1760cm AC 透过率 % E-44 TDI E44+AC E44-AC 4000 3000 2000 1000 0 波数 / cm-1 -1 E44-AC树脂/碳钢间键合研究 实验材料: 碳钢(907A)、 E44、 E44-AC FTIR结果：1 740 cm-1处为游离的羰基，1 680 cm-1处为与碳钢发生化学反应的羰基，该图证实了E44-AC与碳钢发生了化学键合。 打磨 除油 除锈 E44-AC 907A 环氧涂层 E44 AFE照片可见：E44-AC在907A表面形成的薄膜较为致密，但起伏较大、且厚度不均，可能是E44-AC分子与钢表面键合的界面附着力以及E44-AC分子链段的重排和堆积引起的内聚力综合作用的结果。 附着力测试：相对于E44涂层，E44-AC预处理涂层与钢表面的粘接强度提升幅度可达307.53%。 SEM照片可见：E44-AC可均匀地分布在907A的表面，表明其与碳钢较好的浸润性和亲和力 。 结 论 1、酒石酸成功接枝在环氧树脂分子上，制备出E44-AC分子 ；2、E44-AC分子可以在碳钢表面形成较为均匀的薄膜涂层；3、经过E44-AC预处理的环氧涂层粘接强度明显优于未处理的涂层。

More Related