1 / 11

By: Brian Ambrosini Matt Spence Waldon Wong

By: Brian Ambrosini Matt Spence Waldon Wong. Engineering 45 Younes Ataiiyan Santa Rosa Junior College 12/06/04. Applications. Circuit Boards Connecting copper pipes Light bulbs Alternators 1 Stained Glass. Soldering Techniques & Future Products. Soldering Iron Blow Torch

thor
Download Presentation

By: Brian Ambrosini Matt Spence Waldon Wong

An Image/Link below is provided (as is) to download presentation Download Policy: Content on the Website is provided to you AS IS for your information and personal use and may not be sold / licensed / shared on other websites without getting consent from its author. Content is provided to you AS IS for your information and personal use only. Download presentation by click this link. While downloading, if for some reason you are not able to download a presentation, the publisher may have deleted the file from their server. During download, if you can't get a presentation, the file might be deleted by the publisher.

E N D

Presentation Transcript


  1. By: Brian Ambrosini Matt Spence Waldon Wong Engineering 45 Younes Ataiiyan Santa Rosa Junior College 12/06/04

  2. Applications • Circuit Boards • Connecting copper pipes • Light bulbs • Alternators1 • Stained Glass

  3. Soldering Techniques & Future Products • Soldering Iron • Blow Torch • Solder Wave Machine • Cold Heat2

  4. Experiment Procedure • Cut up solder • Heat solder in crucible • Cool • Slowly cool in furnace (100°F/20 min) • Air Cooled • Ice cooled

  5. Procedure Continued • Cast the cooled solder in plastic • Bakelite would melt the solder (thanks Younes) • Sand and Polish sample • Etch with Nitric acid • View/compare microstructure

  6. Lead-Tin Phase Diagram3

  7. Results – Ice Cooled • Small eutectic structures (dark areas) • Less ductile then the other specimens4 • Most susceptible to fatigue • Possible reduction in life

  8. Results – Air Cooled • Standard sized eutectic structure (dark areas)

  9. Results – Slow Cooled • Large eutectoid structures (dark areas) • By cooling the sample slowly, it looks similar to steel • Most ductile sample • Best commercial use • Not cost effective

  10. Air cooled specimen had a medium amount of eutectic structures The furnace cooled specimen had large eutectic structures More ductile Not as strong Ice cooled specimen had very small eutectic structures Less ductile (more brittle) All three samples have the same composition Electrical properties are similar Conclusions

  11. References • 1: http://www.seas.ucla.edu/eThinFilm/Pb-freeWorkshop/abs/pan.html • 2: http://www.coldheat.com/ • 3: http://www2.umist.ac.uk/material/research/intmic/phase/pbsndiag.htm • 4: http://technology.open.ac.uk/emsuite/prj7.html