Advisor : R u -Li Lin Advisee :Shih-Min Chen

Detection of allergies using a silver nanoparticle modified nanostructured biosensor. Advisor : R u -Li Lin Advisee :Shih-Min Chen Southern Taiwan University of Science and Technology, Department of Mechanical Engineering , Tainan , TAIWAN Date ﹕2013/4/1. Outline. Paper Survey

teresa
Download Presentation

Advisor : R u -Li Lin Advisee :Shih-Min Chen

An Image/Link below is provided (as is) to download presentation Download Policy: Content on the Website is provided to you AS IS for your information and personal use and may not be sold / licensed / shared on other websites without getting consent from its author. Content is provided to you AS IS for your information and personal use only. Download presentation by click this link. While downloading, if for some reason you are not able to download a presentation, the publisher may have deleted the file from their server. During download, if you can't get a presentation, the file might be deleted by the publisher.

E N D

Presentation Transcript


  1. Detection of allergies using a silver nanoparticle modified nanostructured biosensor Advisor : Ru-Li Lin Advisee :Shih-Min Chen Southern Taiwan University of Science and Technology,Department of Mechanical Engineering, Tainan, TAIWAN Date ﹕2013/4/1

  2. Outline • Paper Survey • Introduction • Experimental setup • Results and discussion • Conclusions • References

  3. Introduction • The symptoms of the allergic response are determined by the types and concentrations of antigens in the ambient environment. • There are reportedly 21 allergen components in dust mite allergens.The group 2 allergen, Der p2, has been reported to be the key allergen. • It has been found that IgE, which is a useful index for allergy detection, is present in the serum of 80% of asthma patients, and can chemically bind with the carboxylterminal sequences of the Der p2 allergen. • Therefore, the Der p2 allergen can be used for the detection of the IgE concentration in a patient’s serum.

  4. Experimental setup • Preparation of an AAO barrier-layer • Sputtering of Au thin film • Annealing • Packaging • Deposition of GNPs • Deposition of SNPs

  5. Experimental setup-Schematic illustration of the proposed nanostructured biosensor

  6. Experimental setup- Electrophoretic : The space uniform electric field, the phenomenon of dispersed particles in the fluid moving. Affect its deposition parameters generally include: the distance between the two electrodes (d), the drive voltage (V), electrophoresis time (t) and the concentration of the solution

  7. Experimental setup-Sample preparation Immobilization of IgE.

  8. Experimental setup-Sample preparation • The surface of the nanostructured sensor was cleansed bydrenching it in ethanol,acetoneand deionized (DI) water in turn,followedby an ultrasonic wave shaking for 5 min. • 30 μL of a 5 mM 11-MUA (11-mercaptoundecanoic acid) solutionwas then dispensed onthe sensor to create a self-assembled11-MUA monolayer as an anchor membrane. • Coating the sensor chip with a 30 μ L mixture of NHS and EDC (1-ethyl-3-(3-dimethyl-aminopropyl)-carbodiimide) (molar ratio,1:2) for 50 min. The sensor was rinsed twice with a PBS buffersolution (pH 7.4).

  9. The sensor chip was coated with a 25 μL (50 μg/mL) dust miteallergen Der p2 solution and then incubated for 30 min. The sensorwas again washed twice with a PBS buffer solution. A 20 μ L1% BSA solution was used as the blocking layer to the bindingsites of those Der p2 which were not tied to the 11-MUA layer.Thesample was then washed twice with a PBS buffer solution. • Coated with 25μL of a patient’s serum that had been dilutedusing a PBS solution at a ratio of 1:5. The sensor was incubatedfor 30 min before being washed twice in a PBS buffer solution. • Coating a 25μL diluted solution of the affinity purified goat antihumanIgEantibody. The diluted solution was prepared using aPBS solution at a ratio of 1:2000. The sensor was incubated for30 min and then rinsed twice with a PBS buffer solution.

  10. Thirteen patient serum samples which had already beenexamined by ImmunoCAP (CAP; Pharmacia Diagnostics, Uppsala,Sweden) were provided by the Taichung Veterans GeneralHospital,Taichung, Taiwan.

  11. Results and discussion - Device fabrication results (a) 3D electrode (b) flat electrode with a sodium citrate solution as the stabilizer.

  12. Results and discussion - Conductivity enhancement analysis results Nyquist plots for the bare electrodes subjected to different applied voltages for SNP deposition

  13. Results and discussion - Blood serum detection results Blood serum detection results

  14. Results and discussion - Linear regression: △Ret and Immuno CAP Linear regression between △Ret and Immuno CAP detected value (1+≤scale≤4+)

  15. Results and discussion - Measurement of the detection limit of the proposed device △ Ret as a function of the logarithmic concentration of IgE.

  16. Conclusions • In this study, a nanostructured biosensor with uniformly deposited GNPs as the sensing electrode was implemented for the detection of a patient’s allergy level. • To enhance the charge transfer efficiency of the biosensor, SNPs were deposited on the GNP layer. • The blood serum detection results confirm that the proposed nanostructured biosensor can detect allergy diseases with small sample consumption, short sample preparation time, and little detection time.

  17. References [1]Yi-Fen Liu , Jaw-Ji Tsai , Yu-Ting Chin, En-Chih Liao , Chia-Che Wu , and Gou-Jen Wang, Sensors and Actuators , "Detection of allergies using a silver nanoparticle modified nanostructured biosensor , " Sensors and Actuators B , vol 171– 172 , pp. 1095– 1100 ,2012 [2]Electrophoretic: http://brc.se.fju.edu.tw/protein/purify/sdspage.htm