Thermosetting resins

Thermosetting resins. John Summerscales. Thermosets - outline of lecture. phenol-formaldehyde (phenolic resin) epoxides (generally diglycidyl ethers) polyurethanes bismaleimides (BMI) unsaturated polyesters (UP or UPE) vinyl esters methacrylics . Thermosets.

ted
Download Presentation

Thermosetting resins

An Image/Link below is provided (as is) to download presentation Download Policy: Content on the Website is provided to you AS IS for your information and personal use and may not be sold / licensed / shared on other websites without getting consent from its author. Content is provided to you AS IS for your information and personal use only. Download presentation by click this link. While downloading, if for some reason you are not able to download a presentation, the publisher may have deleted the file from their server. During download, if you can't get a presentation, the file might be deleted by the publisher.

E N D

Presentation Transcript


  1. Thermosetting resins John Summerscales

  2. Thermosets - outline of lecture phenol-formaldehyde (phenolic resin) epoxides (generally diglycidyl ethers) polyurethanes bismaleimides (BMI) unsaturated polyesters (UP or UPE) vinyl esters methacrylics

  3. Thermosets • generally supplied as a liquid • cross-linked (cured) by chemicals (and heat) • heat reduces the instantaneous viscosity • heat increases the rate of cure • cure decreases the viscosity over time • product is a 3D molecular network • whereas a thermoplastic is usually a 2D chain

  4. Total Flow (------) Ease of Flow Progress of cure Temperature

  5. Stages of cure • A-stage: soluble and fusible • aka. resol in phenolics • B-stage: may be swollen but not dissolved by a variety of solvents • aka resitol in phenolics • C-stage: rigid, hard, insoluble, infusible • aka resit in phenolics

  6. Phenolic resins • first truly synthetic resins to be exploited. • Butlerov (1859) formaldehyde polymers. • Adolf Bayer (1872) phenols and aldehydes reacted to form resinous substances. • Arthur Smith (1879) first British Patent (16274) for phenol-aldehyde resins as an ebonite substitute in electrical insulation. • Baekeland (1907) controlled and modified the reaction to produce useful products

  7. Phenolic resins • can be broadly divided into three groups: • resol(e) resins • typically 1 : 1.5-2 phenol : formaldehyde • novolac resins • typically 1 : 0.8 phenol : formaldehyde • Friedel-Crafts polymers

  8. Phenol (C6H5OH) • naming reactive sites: OH ortho- meta- para-/tere- iso-

  9. Phenolic resins • Phenol ...and... formaldehyde sites react first OH H O C H

  10. Phenolic resin: methylolation • using Φ to represent phenol • Φ + CH2O Φ CH2OH • Φ CH2OH + CH2O Φ (CH2OH)2 • Φ (CH2OH)2 + CH2O Φ (CH2OH)3

  11. Resoles • alkaline catalyst and excess formaldehyde • methylene bridge formationmay result in the release of water: • HO~CH2~Φ~CH2~OH + HO~CH2~Φ • HO~CH2~Φ~CH2~O~CH2~Φ,  or •  HO~CH2~Φ~CH2~Φ~CH2~OH • continued reaction to network • first product may lose formaldehyde: • HO~CH2~Φ~CH2~O~CH2~Φ  HO~CH2~Φ~CH2~Φ  +  CH2O

  12. Novolacs • acid catalyst and excess of phenol: Φ~CH2~OH + ΦΦ~CH2~Φ + H2O • further condensationand methylene (-CH2-)bridge formation results in fusible and solublelinear low MW polymers (novolacs): ~Φ~CH2~Φ~CH2~Φ~CH2~Φ~CH2~Φ~

  13. Crosslinking novolacs I • add paraform or further formaldehyde • more usually add HMT hexamethylenetetramine: (CH2)6N4 • 2 (CH3)2Φ [(CH3)2ΦCH2]2NH • 3 (CH3)2Φ[(CH3)2ΦCH2~]3N

  14. Crosslinking novolacs II • when the benzylamines areheated at 180-190°Cin the presence of phenol,ammonia or methylamine are evolved: • [(CH3)2ΦCH2]2NH(CH3)2ΦCH2Φ(CH3)2 + NH3 • [(CH3)2ΦCH2]3N(CH3)2ΦCH2Φ(CH3)2 + CH3NH2

  15. Phenolics • Generally brittledue to moisture released during curing • Exceptional FST properties when burning: • low spread of FLAME • low emission of SMOKE • low TOXICITY: only CO2 and H2O released • Key markets: • underground railways • mining • submarines

  16. Epoxy resins

  17. Epoxy (glycidyl) groups O CH2 CH CH2 CH2(O)CH-CH2- Epoxy Glycidyl NB: bond angles of 60°, rather than 109°28´ of sp3 hybrid: highly strained,  highly reactive

  18. Epoxy resin O OH O OH CH3 -C- CH3 -O-CH2CH-CH2 CH2CH-CH2-O- • Epichlorohydrin: CH2(O)CH-CH2-O-Cl • Bisphenol-A: HOΦ-C(CH3)2-ΦOH  CH2(O)CH-CH2-OΦ-C(CH3)2-ΦOH + HCl Di Glycidyl Ether of Bisphenol-A (DGEBA)

  19. DGEBA • methylene (-CH2-) and ether (-O-) groupsgive free movement of atoms before cure: • less steric hindrance and higher reactivity for terminal rather than internal epoxy (oxirane) • terminal epoxy groups mean crosslink sites are free of mobile chain endsso higher Tg achieved.

  20. Cure of epoxy resins • Reactive site is the 3-atom epoxy ring • which may yield an hydroxyl group • Curing agents include: • amines • amides • carboxylic acids • anhydrides: 2 carboxylic acids with water removed

  21. Epoxy cure temperatures • low temperature • ambient to 60°C • medium temperature • up to 120°C • high temperature • up to 180°C • pot-life: time from mixing to 1500 mPas • fibres stick to the brush during lamination • only tow surfaces are wetted.

  22. Gel time of epoxy resin

  23. Post-cure • full cure uses 100% of reactive sites • but constrained movement of polymer chain may lead to incomplete cure: • lower glass transition temperature • lower resin density • fewer bonds/m3 lower moduli and strengths • additional free volume • easier diffusion of chemicals  reduced durability • to achieve optimum high-performance composites, post-cure at higher temp’ shortly after production: • unreacted sites may become inactive over time.

  24. Tg for high-performance epoxy • DGEBA/DICY Tg ~180-190ºC • di glycidyl ether of bis phenol A • aliphatic dicyandiamide • TGDDM/DDS Tg ~240-260ºC • tetra glycidyl-4,4‘-diamino diphenyl methane • aromatic diamino diphenyl sulphone • advantages: • low cure reactivity … long storage times • strength retention after time at temperature • disadvantages • low strain to failure • high moisture absorption • poor hot/wet performance

  25. Epoxy (vs polyester) resin • outstanding adhesion • excellent static and fatigue strengths • outstanding corrosion protection • excellent chemical resistance • excellent weather resistance • very low shrinkage on curing • good toughness • good heat resistance from AB Strong “Fundamentals of Composites Manufacturing” (1989)

  26. Epoxy (vs polyester) resin • medium to high cost • relatively difficult to handle • potential toxicity of uncured material • poor appearance after weathering from AB Strong “Fundamentals of Composites Manufacturing” (1989)

  27. Polyurethanes primarily for RIM processes

  28. Bismaleimide (imide group) O C N C O Note: delocalisation across • benzene ring • both C=O groups • p-orbital on N  stiff molecule

  29. Unsaturated polyesters

  30. Curing of polyester resin - A - B - A - B - A - B - | | | S S S | | | - A - B - A - B - A - B - | | | S S S | | | - A - B - A - B - A - B - -A-B-A-B-A-B- plus styrene (ΦCH=CH2) reactive diluent where B block contains unsaturation (double bonds) in backbone of polymer chain, leads to 3D network

  31. Curing of polyester resin

  32. Vinyl esters • epoxy backbone • addition-type curing Methacrylics • methylmethacrylate instead of styrene as reactive diluent

  33. Summary (key polymers)