1 / 23

可生物降解 高分子材料的改性

可生物降解 高分子材料的改性. 报告人：陈郁栋 日 期：201 3 . 4 . 11. 研究背景. 改进方案. 共聚改性. 共混改性. 协同改性. 研究背景. 1907 年 酚醛塑料问世. 1934 年 高分子理论提出. 合成高分子材料逐渐取代传统材料. 2007 年我国塑料制品累计工业产值： 8000 亿. 改进方案. 可生物降解聚合物. 淀粉基生物降解材料. 脂肪族聚酯. 聚乳酸（ PLA). 聚碳酸丙烯酯（ PPC). 聚己内酯（ PCL). 聚丁二酸丁二醇酯（ PBS ）. 聚羟基脂肪酸（ PHAs). 耐水性、机械强度、热性能、成本.

stella
Download Presentation

可生物降解 高分子材料的改性

An Image/Link below is provided (as is) to download presentation Download Policy: Content on the Website is provided to you AS IS for your information and personal use and may not be sold / licensed / shared on other websites without getting consent from its author. Content is provided to you AS IS for your information and personal use only. Download presentation by click this link. While downloading, if for some reason you are not able to download a presentation, the publisher may have deleted the file from their server. During download, if you can't get a presentation, the file might be deleted by the publisher.

E N D

Presentation Transcript

  1. 可生物降解 高分子材料的改性 报告人：陈郁栋 日 期：2013.4.11

  2. 研究背景 改进方案 共聚改性 共混改性 协同改性

  3. 研究背景 1907年 酚醛塑料问世 1934年 高分子理论提出 合成高分子材料逐渐取代传统材料 2007年我国塑料制品累计工业产值：8000亿

  4. 改进方案

  5. 可生物降解聚合物 淀粉基生物降解材料 脂肪族聚酯 聚乳酸（PLA) 聚碳酸丙烯酯（PPC) 聚己内酯（PCL) 聚丁二酸丁二醇酯（PBS） 聚羟基脂肪酸（PHAs) 耐水性、机械强度、热性能、成本

  6. 共聚改性

  7. 嵌段共聚改性PLA *马晓妍等，聚乳酸及其共聚物的制备和降解性能

  8. -CH2-

  9. 接枝共聚、共混改性PLA *Suming Ye, Rubber Toughening of Poly(lactic acid): Effect of Stereocomplex Formation at the Rubber-Matrix Interface

  10. 共混改性 PPC/PBS，PPC/PBS/DAOP 聚碳酸丙烯酯（PPC） *周庆海等,聚碳酸1,2-丙二酯/聚琥珀酸丁二酯/邻苯二甲酸二烯丙酯共混体系的研究

  11. PBS结晶温度高于玻璃化温度，故Tg难以观察。 加入PBS后Tg无明显变化，佐证PPC与PBS体系相分离 DAOP加入后Tg改善明显，体现其塑化作用

  12. 协同改性 封端： 用酸酐、酰氯、异氰酸酯等(封端剂)， 将CO2共聚物的端基变成不活泼的基团

  13. PPC与p(St-co-MAH) 的共混 纯PPC的Tg=37.5℃

  14. PPC/PBS/PVPh共混研究

  15. PPC/PBS/p(St-co-MAH)共混研究

  16. 总结