An Image/Link below is provided (as is) to download presentation Download Policy: Content on the Website is provided to you AS IS for your information and personal use and may not be sold / licensed / shared on other websites without getting consent from its author. Content is provided to you AS IS for your information and personal use only. Download presentation by click this link. While downloading, if for some reason you are not able to download a presentation, the publisher may have deleted the file from their server. During download, if you can't get a presentation, the file might be deleted by the publisher.

E N D

Presentation Transcript


  1. Fig.: 12.1 Chapter 12: Michel, B.: Testing of Microcomponents. In: Grellmann, W., Seidler, S. (Eds.): Polymer Testing. Carl Hanser Verlag, Munich (2013) 2. Edition

  2. a F b 1 strength or N yield criterion nominal strength s D LEBM D' specimen dimension (log D) Fig.: 12.2 Chapter 12: Michel, B.: Testing of Microcomponents. In: Grellmann, W., Seidler, S. (Eds.): Polymer Testing. Carl Hanser Verlag, Munich (2013) 2. Edition

  3. a b d c Fig.: 12.3 Chapter 12: Michel, B.: Testing of Microcomponents. In: Grellmann, W., Seidler, S. (Eds.): Polymer Testing. Carl Hanser Verlag, Munich (2013) 2. Edition

  4. MODEL 1362 IN TRON load cell adapter micro-tensile testing device internal load cell 2 0.1 specimen 17.6 0.1 2 1.172 0.1 Fig.: 12.4 Chapter 12: Michel, B.: Testing of Microcomponents. In: Grellmann, W., Seidler, S. (Eds.): Polymer Testing. Carl Hanser Verlag, Munich (2013) 2. Edition

  5. 60 standard specimen l = 50 mm 0 50 25 °C 100 °C 40 175 °C 225 °C s (MPa) 30 microspecimen l = 10 mm 20 0 25 °C 10 100 °C 175 °C 0 0 0.2 0.4 0.6 0.8 1.0 e (%) Fig.: 12.5 Chapter 12: Michel, B.: Testing of Microcomponents. In: Grellmann, W., Seidler, S. (Eds.): Polymer Testing. Carl Hanser Verlag, Munich (2013) 2. Edition

  6. b 0.50 0.45 e 0.40 l 0.35 0.30 0.25 0.20 e (%) 0.15 a 0.10 0.05 0.00 -0.05 -0.10 e q -0.15 -0.20 specimen correlated video image data aquisition Fig.: 12.6 Chapter 12: Michel, B.: Testing of Microcomponents. In: Grellmann, W., Seidler, S. (Eds.): Polymer Testing. Carl Hanser Verlag, Munich (2013) 2. Edition

  7. 0.50 EP + filler (SiO )  = 0.27 2 0.45 PP + chalk  = 0.20 PVC + filler  = 0.22 0.40 0.35  0.30 0.25 0.20 0.15 0.10 0 0.1 0.2 0.3 0.4 e (%) l Fig.: 12.7 Chapter 12: Michel, B.: Testing of Microcomponents. In: Grellmann, W., Seidler, S. (Eds.): Polymer Testing. Carl Hanser Verlag, Munich (2013) 2. Edition

  8. 100 80 60 F (N) 40 standard CT 20 mini CT 0 0 20 40 60 80 100 120 v (µm) Fig.: 12.8 Chapter 12: Michel, B.: Testing of Microcomponents. In: Grellmann, W., Seidler, S. (Eds.): Polymer Testing. Carl Hanser Verlag, Munich (2013) 2. Edition

  9. 150 120 PEI PC 90 PSU PF 60 ceramics PMMA 30 epoxy resin ceramics 0 0 30 60 90 120 150 1/2 K (MPamm ) for mini CT Q 1/2 K (MPamm ) for standard CT Q Fig.: 12.9 Chapter 12: Michel, B.: Testing of Microcomponents. In: Grellmann, W., Seidler, S. (Eds.): Polymer Testing. Carl Hanser Verlag, Munich (2013) 2. Edition

  10. a b load B D A PMMA indenter F (mN) C PS glass interface crack E 0 h (nm) Fig.: 12.10 Chapter 12: Michel, B.: Testing of Microcomponents. In: Grellmann, W., Seidler, S. (Eds.): Polymer Testing. Carl Hanser Verlag, Munich (2013) 2. Edition

  11. a b Fig.: 12.11 Chapter 12: Michel, B.: Testing of Microcomponents. In: Grellmann, W., Seidler, S. (Eds.): Polymer Testing. Carl Hanser Verlag, Munich (2013) 2. Edition

  12. a b Fig.: 12.12 Chapter 12: Michel, B.: Testing of Microcomponents. In: Grellmann, W., Seidler, S. (Eds.): Polymer Testing. Carl Hanser Verlag, Munich (2013) 2. Edition

  13. F optical device scan device a CT specimen loading module F Fig.: 12.13 Chapter 12: Michel, B.: Testing of Microcomponents. In: Grellmann, W., Seidler, S. (Eds.): Polymer Testing. Carl Hanser Verlag, Munich (2013) 2. Edition

  14. a b crack crack line of height profile evaluation 0.28 0.36 10 10 10 10 crack polishing trace height profile height profile 200 180 nm 140 160 nm 100 120 0 10 20 30 0 10 20 30 µm µm Fig.: 12.14 Chapter 12: Michel, B.: Testing of Microcomponents. In: Grellmann, W., Seidler, S. (Eds.): Polymer Testing. Carl Hanser Verlag, Munich (2013) 2. Edition

  15. b a 30 crack flank rigth 25 20 0.1 displacement perpendicular to the crack µm µm 0.0 15 -0.1 10 30 30 25 25 20 5 20 15 15 µm µm 10 10 0 5 5 0 5 10 15 20 25 30 crack flank left µm Fig.: 12.15 Chapter 12: Michel, B.: Testing of Microcomponents. In: Grellmann, W., Seidler, S. (Eds.): Polymer Testing. Carl Hanser Verlag, Munich (2013) 2. Edition

  16. y u r u (x) y r u (x) q y x l u (x) y Fig.: 12.16 Chapter 12: Michel, B.: Testing of Microcomponents. In: Grellmann, W., Seidler, S. (Eds.): Polymer Testing. Carl Hanser Verlag, Munich (2013) 2. Edition

  17. displacement u (µm) y . -4 7 10 4.5 b a . -4 4.0 6 10 . . -4 -4 y = 2.1 10 x + 6.9 10 3.5 . -4 5 10 3.0 . -4 4 10 2.5 y coordinate (µm) . -4 3 10 2.0 . 1.5 -4 2 10 1.0 . -4 1 10 0.5 0 0 1 2 3 4 0 1 2 3 4 x coordinate (µm) x coordinate (µm) 2 2 u l ((u − u )/2) (µm ) y y Fig.: 12.17 Chapter 12: Michel, B.: Testing of Microcomponents. In: Grellmann, W., Seidler, S. (Eds.): Polymer Testing. Carl Hanser Verlag, Munich (2013) 2. Edition