An Image/Link below is provided (as is) to download presentation Download Policy: Content on the Website is provided to you AS IS for your information and personal use and may not be sold / licensed / shared on other websites without getting consent from its author. Content is provided to you AS IS for your information and personal use only. Download presentation by click this link. While downloading, if for some reason you are not able to download a presentation, the publisher may have deleted the file from their server. During download, if you can't get a presentation, the file might be deleted by the publisher.

E N D

Presentation Transcript

  1. VOJNOTEHNIČKI INSTITUTSEKTOR ZA MATERIJALE I ZAŠTITU UTICAJ MIKROSTRUKTURE PRIPREMKA NA MEHANIČKE OSOBINE ROTACIONO VALJANE BEŠAVNE ČELIČNE CEVI VISOKE ČVRSTOĆE M.Nikačević, Lj.Radović, M.Hršum VII Savetovanje metalurga

  2. VOJNOTEHNIČKI INSTITUTSEKTOR ZA MATERIJALE I ZAŠTITU CILJ: • da se ispita mogućnost izrade tankozidne bešavne čelične cevi od čelika Č.4131 postupkom hladnog rotacionog valjanja • ispita uticaj strukturno-mehaničkih osobina pripremka za oblikovanje na efekte deformacionog ojačavanja i deformacionog starenja pri rotacionom valjanju VII Savetovanje metalurga

  3. VOJNOTEHNIČKI INSTITUTSEKTOR ZA MATERIJALE I ZAŠTITU SADRŽAJ • specifičnosti tehnologije RV • eksperimentalni rad • rezultati • zaključak VII Savetovanje metalurga

  4. VOJNOTEHNIČKI INSTITUTSEKTOR ZA MATERIJALE I ZAŠTITU TEHNOLOGIJA ROTACIONOG VALJANJA (SPINNING) • RV konusa (shear forming) • RV cilindara (flow forming) VII Savetovanje metalurga

  5. VOJNOTEHNIČKI INSTITUTSEKTOR ZA MATERIJALE I ZAŠTITU Šematski prikaz procesarotacionog valjanja konusa cilindara VII Savetovanje metalurga

  6. VOJNOTEHNIČKI INSTITUTSEKTOR ZA MATERIJALE I ZAŠTITU Specifičnosti tehnologije RV uska zona deformacije • relativno mala instalisana snaga mašine • mali prostor za smeštaj mašine VII Savetovanje metalurga

  7. Komparativne prednosti tehnologije RV • bolje mehaničke osobine (čvrstoča, žilavost -otpornost ka lomu) i smanjenje anizotropije • značajno kraće vreme osvajanja i izrade delova • minimalan gubitka materijala • dimenziona tačnost (±0.02-0,13 mm za delove prečnika manjih od 0.6 m i 0,13- 0,64 mm kod prečnika do 3 m) • mali broj alata • niža cena izrade i u fazi probnih komada i serijske proizvodnje (do 4 puta) VII Savetovanje metalurga

  8. VOJNOTEHNIČKI INSTITUTSEKTOR ZA MATERIJALE I ZAŠTITU VII Savetovanje metalurga

  9. VOJNOTEHNIČKI INSTITUTSEKTOR ZA MATERIJALE I ZAŠTITU Mašine za rotaciono valjanje VII Savetovanje metalurga

  10. VOJNOTEHNIČKI INSTITUTSEKTOR ZA MATERIJALE I ZAŠTITU AS 34.60 VII Savetovanje metalurga

  11. VOJNOTEHNIČKI INSTITUTSEKTOR ZA MATERIJALE I ZAŠTITU Eksperimentalni rad Materijal Pripremak Rotaciono valjana cev

  12. Materijal Bešavna toplo valjana i normalizovana cev ø39.7x20 mm Čelik Č.4131 (JUS); 41Cr4 (DIN) Hemijski sastav čelika Č.4131, (mas.%)

  13. Tehnologija izrade pripremka normalizacija debelozidne toplovaljane bešavne cevi mehanička obrada na zadate dimenzije (133/115 mm ) završna termička obrada 1. žarenje (700°C/3h) (1 grupa) 2. kaljenje i otpuštanje na tri nivoa tvrdoće (tri grupe) (Tk=870°C/70 min, Totp=520-580°C/3h) (HB =260-295) VOJNOTEHNIČKI INSTITUTSEKTOR ZA MATERIJALE I ZAŠTITU VII Savetovanje metalurga

  14. VOJNOTEHNIČKI INSTITUTSEKTOR ZA MATERIJALE I ZAŠTITU Mehaničke osobine pripremka

  15. Mikrostruktura pripremaka 035: Totp=520°C, 295HB 017: Totp=580°C, 260HB 092: Totp=550°C, 280HB

  16. Oblik i mere pripremka

  17. Hladno rotaciono valjanje bešavne čelične cevi i termička obrada • na mašini sa tri rolne • sa dva prolaza • procesni parametari: brzina rotacije trna 200 o/min brzina aksijalnog kretanja rolni 180 mm /min • redukcija debljine zida 72,2% (120/115 mm) • žarenje: 250, 280 i 300°C /3h VII Savetovanje metalurga

  18. Rotaciono valjana cev

  19. Mehaničke osobine rotaciono valjanih cevi R122-PK1

  20. nastavak

  21. Dijagrami zatezanja RV cevi (pripremak 280HB) RV RV +250°C RV +280°C RV +300°C

  22. VOJNOTEHNIČKI INSTITUTSEKTOR ZA MATERIJALE I ZAŠTITU Zaključak • Potvrđena je mogućnost hladnog rotacionog valjanja bešavne cevi od Č.4131 i u žarenom i poboljšanom stanju i to bez pojave prskotina. • Mehaničke osobine RV cevi su bolje od onih koje se mogu ostvariti termičkom obradom. • Efekat ojačavanja deformacijom pri RV je izraženiji kod pripremaka sa nižim mehaničkim osobinama (za HB=200 Rm=344 MPa; za HB=295 Rm=295 MPa) VII Savetovanje metalurga

  23. Deformaciono starenje je intenzivnije sa porastom tempereture i ono ima veliki uticaj na granicu tečenja i minoran na zateznu čvrstoću (za HB=200 na T= 300°C R0.2=314 MPa, Rm=46 MPa ) Uticaj deformacionog starenja cevi na granicu tečenjaje veći što je čvrstoća pripremka niža (za HB=200 T= 300°C, R0.2=314 MPa za HB=295 T= 300°C, R0.2=167MPa) Niskotemperaturnio žarenje RV cevi povoljno utiče i na stabilnost dimenzija u toku i nakon završne mehaničke obrade krajeva (izrada navoja i dr.) VOJNOTEHNIČKI INSTITUTSEKTOR ZA MATERIJALE I ZAŠTITU VII Savetovanje metalurga