1 / 27

Dental luting cement

Dental luting cement. Bond Strength Strength Flow (viscosity) Wetting Film thickness (<25 microns ) Solubility Working,Setting time Esthetic. *Complication. Dental luting Cement. Zinc phosphate Polycarboxylate Glass ionomer RMGI cement Resin cement. Zinc phosphate.

Download Presentation

Dental luting cement

An Image/Link below is provided (as is) to download presentation Download Policy: Content on the Website is provided to you AS IS for your information and personal use and may not be sold / licensed / shared on other websites without getting consent from its author. Content is provided to you AS IS for your information and personal use only. Download presentation by click this link. While downloading, if for some reason you are not able to download a presentation, the publisher may have deleted the file from their server. During download, if you can't get a presentation, the file might be deleted by the publisher.

E N D

Presentation Transcript


  1. Dental luting cement • Bond Strength • Strength • Flow(viscosity) • Wetting • Film thickness(<25 microns) • Solubility • Working,Setting time • Esthetic *Complication www.rxdentistry.net

  2. Dental luting Cement • Zinc phosphate • Polycarboxylate • Glass ionomer • RMGI cement • Resin cement www.rxdentistry.net

  3. Zinc phosphate • Over 100 yrs of clinical experience • Routine application • Post-op sensitivities • Low hardness • High solubility • pH • No bond with tooth www.rxdentistry.net

  4. Polycarboxylate • Molecular bonding to tooth substance (2MPa) • Cost • Low F¯release • Low post-op sensitivities • Low hardness • solubility www.rxdentistry.net

  5. Glass ionomer • Molecular bonding to tooth substance • F¯release • Cost-Eff. • Minimal dimentional change • Occa. post-op sensitivities • Sensitive to water • Limited application (ceramics) (3-5MPa) (High caries risk) www.rxdentistry.net

  6. RMGI • Molecular bonding to tooth substance • F¯release • Low solubility • Fewer post-op sensitivities • Application ? (ceramics,composite) (>10MPa) www.rxdentistry.net

  7. Resin cement • High adhesive quality (18-20MPa) • ⇧ Retention • High hardness • Low solubility • All metal, ceramic,composite(indirect) • Occa. Post-op sensitivities www.rxdentistry.net

  8. Adhesive quality • Non-adhesive (zinc phosphate) • Micromechanical bonding (resin cement) • Molecular adhesion (polycarboxylate,GI,RMGI) www.rxdentistry.net

  9. Dental Cement • Zinc phosphate • Polycarboxylate • Glass ionomer • RMGI cement • Resin cement Conventional Adhesive www.rxdentistry.net

  10. Advantage conventional cement • Easy handling • Moisture tolerance • No pre-Tx steps • Routine for metal base www.rxdentistry.net

  11. Advantage resin cement • Excellent mechanical properties • High bond strength with pre-Tx step • High aesthetics/translucency • Suitable for Ceramic, Porcelain, Composite,Metal www.rxdentistry.net

  12. Resin cement • Matrix • Primer • Filler • Coupling agent www.rxdentistry.net

  13. Resin cement • Matrix - Dimethacrylate • Primer- Dicrylate • Filler - Quartz, silica • Coupling agent- Silane dimethacrylate www.rxdentistry.net

  14. Resin cement • Total etch Rely X ARC,Variolink II ,Calibra ,C&B • Self-etch Panavia F • Self-AdhesiveRely X Unicem www.rxdentistry.net

  15. Adhesion • Dentin/enamel (micromachanical bond) • Porcelain (hydrofluoric acid,Ammoniumfluoride acid)+ silane • Metal (sandblasting)(metal bonding adhesive) • Fiber post www.rxdentistry.net

  16. Adhesion • Dentin/enamel (micromachanical bond) • Porcelain (hydrofluoric acid,Ammoniumfluoride acid)+ silane • Metal (sandblasting)(metal bonding adhesive) • Fiber post www.rxdentistry.net

  17. Adhesion • Dentin/enamel (micromachanical bond) • Porcelain (hydrofluoric acid,Ammoniumfluoride acid)+ silane • Metal (sandblasting)(metal bonding adhesive) • Fiber post www.rxdentistry.net

  18. Adhesion • Dentin/enamel (micromachanical bond) • Porcelain (hydrofluoric acid,Ammoniumfluoride acid)+ silane • Metal (sandblasting)(metal bonding adhesive) • Fiber post www.rxdentistry.net

  19. no local peak forces, no root fracture root fracture! Why are fiber post? • Clinical success rate: Less root fracture than with metal posts:Dentine-like flexural strenght avoids the “wedge” effect of stiff and hard metal posts. fiber post metal • Esthetics: the new post is translucent and does not shine through ceramic or composite restorations • 3. Easy and conservative removal with drills if endodontic re-treatment is required www.rxdentistry.net further advantages: no corrosion, easy cutting of over-length, light-translucent...

  20. Resin cement • Bond strength > Zinc phosphate 10 times • ↑ Retention • Reinforced ceramic - base Crown • Adhesive system (micromachanical bond-tooth) (chemical bond-porcelain,metal) • Low solubility • ↓ leakage www.rxdentistry.net

  21. Pre-treatment procedure www.rxdentistry.net

  22. Pre-treatment procedure www.rxdentistry.net

  23. Pre-treatment procedure www.rxdentistry.net

  24. Polymerization • Light-cured/Dual cure (2 vials - Base,Catalyst) • Self cure/auto cure • Dual cure www.rxdentistry.net

  25. Adhesion • Dentin/enamel (micromachanical bond) • Porcelain (hydrofluoric acid,Ammoniumfluoride acid)+ silane • Metal (sandblasting)(metal bonding adhesive) • Fiber post Adhesive cement bonding to tooth ,alloy structure www.rxdentistry.net

  26. Clinical Tips • Anesthetic • Isolate (pack cord) • Light cure 2-3 sec • Include 3-5 shades,silane • Remove solvent-can inhibit setting of resin cement • Excess bonding –poor fit,low strength • Temp NE www.rxdentistry.net

  27. Shade • Opaque –veneer + Tetracycline • Clear (translucent) • Vita shade www.rxdentistry.net