5.4 反应扩散

5.4 反应扩散. 反应扩散. 概念 :通过 扩散 使固溶体内的溶质组元超过固溶极限而不断形成 新相 的扩散过程,称为 反应扩散 或 相变扩散 。 过程 :一是 扩散过程 ;二是界面上达到一定浓度所发生相变的 反应 过程。. 第五章 材料中的 扩散. 特点 :二元系中扩散区域 不存在双相区 ,只能形成不 同的单相区; 。. 举例 :纯铁棒在两相区的渗碳过程。. 5.4 反应扩散. Fe-Fe 3 C 相图与反应扩散. 举例. 纯铁棒 若在 912℃ 以下 α+γ 两相区 温度进行渗碳:.

monet
Download Presentation

5.4 反应扩散

An Image/Link below is provided (as is) to download presentation Download Policy: Content on the Website is provided to you AS IS for your information and personal use and may not be sold / licensed / shared on other websites without getting consent from its author. Content is provided to you AS IS for your information and personal use only. Download presentation by click this link. While downloading, if for some reason you are not able to download a presentation, the publisher may have deleted the file from their server. During download, if you can't get a presentation, the file might be deleted by the publisher.

E N D

Presentation Transcript


  1. 5.4 反应扩散 反应扩散 概念:通过扩散使固溶体内的溶质组元超过固溶极限而不断形成新相的扩散过程,称为反应扩散或相变扩散。过程:一是扩散过程;二是界面上达到一定浓度所发生相变的反应过程。 第五章 材料中的 扩散 特点:二元系中扩散区域不存在双相区,只能形成不 同的单相区; 。 举例:纯铁棒在两相区的渗碳过程。

  2. 5.4 反应扩散 Fe-Fe3C相图与反应扩散 举例 纯铁棒若在912℃以下α+γ两相区温度进行渗碳: 当α-Fe中浓度为C1时,便已饱和,铁素体已不稳定,α→γ, γ成分为C2,即发生了反应扩散,在α/γ相界处 平衡; 第五章 材料中的 扩散 当碳浓度C>C2后,铁棒表层变为奥氏体(A),且端部A的浓度可达到C3,离端面越远,A中浓度越低; 由图可见,γ/α相界处,有成分突变:C2→C1, 在一定温度下进行的反应扩散,其表面渗层随保温时间的延长,通过新相界面的推移而不断向纵深发展。反应扩散速度取决于化学反应和原子扩散两个因素。

More Related