USINABILIDADE DOS MATERIAIS. USINABILIDADE DOS MATERIAIS. USINABILIDADE. GRAU DE DIFICULDADE DE SE USINAR UM DETERMINADO MATERIAL. GRANDEZA TECNOLÓGICA . EXPRESSA UM CONJUNTO DE PROPRIEDADES DE USINAGEM DE UM MATERIAL EM RELAÇÃO A OUTRO TOMADO COMO PADRÃO, POR MEIO DE UM ÍNDICE COMPARATIVO.

mahon
Download Presentation

USINABILIDADE DOS MATERIAIS

An Image/Link below is provided (as is) to download presentation Download Policy: Content on the Website is provided to you AS IS for your information and personal use and may not be sold / licensed / shared on other websites without getting consent from its author. Content is provided to you AS IS for your information and personal use only. Download presentation by click this link. While downloading, if for some reason you are not able to download a presentation, the publisher may have deleted the file from their server. During download, if you can't get a presentation, the file might be deleted by the publisher.

E N D

Presentation Transcript


  1. USINABILIDADE DOS MATERIAIS

  2. USINABILIDADE DOS MATERIAIS

  3. USINABILIDADE • GRAU DE DIFICULDADE DE SE USINAR UM DETERMINADO MATERIAL. • GRANDEZA TECNOLÓGICA. • EXPRESSA UM CONJUNTO DE PROPRIEDADES DE USINAGEM DE UM MATERIAL EM RELAÇÃO A OUTRO TOMADO COMO PADRÃO, POR MEIO DE UM ÍNDICE COMPARATIVO.

  4. PROPRIEDADES DA USINAGEM INFLUENCIAM: • VIDA DA FERRAMENTA • ACABAMENTO SUPERFICIAL • ESFORÇOS DE CORTE • TEMPERATURA DE CORTE • TEMPO DE CORTE • PRODUTIVIDADE • CARACTERÍSTICAS DO CAVACO

  5. PROPRIEDADES DA USINAGEM

  6. USINABILIDADE DEPENDE: • CONDIÇÕES DE CORTE • CARACTERÍSTICAS DA FERRAMENTA • CONDIÇÕES DE REFRIGERAÇÃO • RIGIDEZ DO SISTEMA MÁQ.-FERRAMENTA-PEÇA • TIPOS DE TRABALHO NÃO DEPENDE SÓ DO MATERIAL DA PEÇA

  7. USINABILIDADE EM RELAÇÃO AO MATERIAL DA PEÇA: • ESTADO METALÚRGICO • DUREZA • PROPRIEDADES MECÂNICAS • COMPOSIÇÃO QUÍMICA • OPERAÇÕES ANTERIORES • ENCRUAMENTO

  8. ENSAIOS DE USINABILIDADE • MATERIAL ENSAIADO E PADRÃO SÃO USINADOS ATÉ O FIM DE VIDA DA FERRAMENTA PARA DIVERSAS VELOCIDADES DE CORTE. • PADRÃO: AISI B1112 É O MAIS UTILIZADO. • VC PARA UMA VIDA DETERMINADA DA FERRAMENTA.

  9. ENSAIOS DE USINABILIDADE • V20 - VELOCIDADE PARA A VIDA DE 20 MINUTOS. • V60 - VELOCIDADE PARA A VIDA DE 60 MINUTOS. • ÍNDICE DE USINABILIDADE (IU):

  10. ENSAIOS DE USINABILIDADE • O ENSAIO DE LONGADURAÇÃO LEVAM EM CONTA A PROPRIEDADE DE USINAGEM - VIDA DA FERRAMENTA. • EXISTEM ENSAIOS DE CURTA DURAÇÃO, USANDO ALÉM DO CRITÉRIO DE VIDA DA FERRAMENTA, OUTROS CRITÉRIOS TAIS COMO A FORÇA DE USINAGEM OU ACABAMENTO POR EXEMPLO.

  11. ENSAIOS DE USINABILIDADE • SÃO CHAMADOS DE CURTADURAÇÃO, PORQUE SÃO UTILIZADAS CONDIÇÕES FORÇADAS DE USINAGEM E/OU MATERIAIS DE FERRAMENTAS POUCO RESISTENTES AO DESGASTE. • ASSIM A VIDA DA FERRAMENTA TERMINA RAPIDAMENTE PARA QUE O ENSAIO POSSA SER REALIZADO EM UM CURTO ESPAÇO DE TEMPO.

  12. ENSAIOS DE USINABILIDADE

  13. RESISTÊNCIA MECÂNICA E DUREZA USINABILIDADE USINABILIDADE DUCTILIDADE CONDUTIBILIDADE TÉRMICA USINABILIDADE TAXA DE ENCRUAMENTO USINABILIDADE A USINABILIDADE E AS PROPRIEDADES

  14. 1/3 DA DENSIDADE DO AÇO ALUMÍNIO USINABILIDADE DO ALUMÍNIO • DEVIDO A SUA BAIXADENSIDADE O ALUMÍNIO É UM MATERIAL POTENCIAL PARA ECONOMIA DE PESO NA FABRICAÇÃO DE PRODUTOS, PRINCIPALMENTE NA INDÚSTRIA AERONÁUTICA, AEROESPACIAL E AUTOMOBILÍSTICA.

  15. 3 VEZES A CONDUTIVIDADE TÉRMICA DO AÇO ALUMÍNIO USINABILIDADE DO ALUMÍNIO • AS LIGAS DE ALUMÍNIO, POR POSSUÍREM ALTACONDUTIVIDADETÉRMICA ATRAEM PARA A PEÇA BOA PARTE DO CALOR GERADO, OCASIONANDO UMA ELEVAÇÃO NA TEMPERATURA. ESTE FATO FAVORECE A USINAGEM DESTAS LIGAS, JÁ QUE AS MESMAS POSSUEM UMA RESISTÊNCIA BASTANTE REDUZIDA EM TEMPERATURAS ELEVADAS.

  16. 2 VEZES MAIOR QUE O COEFICIENTE DE DILATAÇÃO DO AÇO ALUMÍNIO USINABILIDADE DO ALUMÍNIO • O COEFICIENTE DE DILATAÇÃO TÉRMICA DO ALUMÍNIO, POR SER MAIOR QUE O DO AÇO E DO LATÃO, PODE GERAR DIFICULDADE NA OBTENÇÃO DE TOLERÂNCIAS APERTADAS.

  17. USINABILIDADE DO ALUMÍNIO

  18. USINABILIDADE DO ALUMÍNIO

  19. USINABILIDADE DO ALUMÍNIO • O ALUMÍNIO EM GERAL PODE SER FACILMENTE USINADO. A ENERGIA CONSUMIDA POR UNIDADE DE VOLUME DO METAL REMOVIDO É MUITO BAIXA. APENAS O MAGNÉSIO E SUAS LIGAS PODEM SER USINADAS COM A MESMA TAXA DE ENERGIA CONSUMIDA. • TOMADAS COMO BASE AS PROPRIEDADES MECÂNICAS DO ALUMÍNIO, A FORÇA DE CORTE, E POR ESSA RAZÃO A POTÊNCIA, REQUERIDA PARA USINAGEM É MENOR DO QUE A ESPERADA PARA ESSES MATERIAIS.

  20. USINABILIDADE DO ALUMÍNIO • O EFEITO DO AVANÇO NA TAXA DE REMOÇÃO DE MATERIAL SOBRE A POTÊNCIA PARA UM AÇO DE BAIXO CARBONO E UMA LIGA DE ALUMÍNIO 2017-T4 COM PROPRIEDADES MECÂNICAS COMPARÁVEIS.

  21. USINABILIDADE DO ALUMÍNIO • PARA A USINAGEM DAS LIGAS DE ALUMÍNIO É NECESSÁRIO QUE A DUREZA DAS MESMAS SEJA MAIOR QUE 80 HB PARA QUE POSSA APRESENTAR UMA BOA USINABILIDADE. • JÁ QUE SE A DUREZA FOR MENOR QUE ESTE VALOR, A TENDÊNCIA À FORMAÇÃO DE ARESTA POSTIÇA DE CORTE É MUITO ALTA E SE TORNA MUITO DIFÍCIL À OBTENÇÃO DE RUGOSIDADES BAIXAS DA PEÇA EM USINAGEM.

  22. USINABILIDADE DO ALUMÍNIO

  23. USINABILIDADE DOS AÇOS • O FATOR METALÚRGICO PREDOMINANTE COM RESPEITO À USINABILIDADE DOS AÇOS É CERTAMENTE A DUREZA. • UM VALOR MÉDIO SERIA DE 200 HB. • DIMINUINDO ESTE VALOR A TENDÊNCIA À FORMAÇÃO DA APC AUMENTA. • QUANDO E AUMENTA A DUREZA, O DESGASTE DA FERRAMENTA VIA ABRASÃO E DIFUSÃO PASSA A AFETAR NEGATIVAMENTE A USINABILIDADE.

  24. USINABILIDADE DOS AÇOS

  25. USINABILIDADE DOS AÇOS • OUTRO FATOR METALÚRGICO QUE AFETA A USINABILIDADE DOS AÇOS É A MICROESTRUTURA. • UM TERCEIRO FATOR METALÚRGICO DE INFLUÊNCIA NA USINABILIDADE DOS AÇOS É A PRESENÇA DE INCLUSÕES: MACRO-INCLUSÕES E MICRO-INCLUSÕES. • O ÚLTIMO FATOR METALÚRGICO NA USINABILIDADE É A PRESENÇA DE ELEMENTOS DE LIGA.

  26. USINABILIDADE DOS FERROS-FUNDIDOS • LIGAS Fe-C ENTRE 2 E 4% DE CARBONO (Si, Mn, S, P). • PRINCIPAIS PROPRIEDADES: BOA RIGIDEZ, RESISTÊNCIA À COMPRESSÃO E BAIXO PONTO DE FUSÃO. • CARBONO NA FORMA DE CARBETOS OU DE GRAFITA. TIPOS: BRANCO, CINZENTO, MALEÁVEL, NODULAR E VERMICULAR.

  27. USINABILIDADE DOS FERROS-FUNDIDOS

  28. USINABILIDADE DOS FERROS-FUNDIDOS

  29. USINABILIDADE DOS FERROS-FUNDIDOS

  30. USINABILIDADE AÇOSXFERROS-FUNDIDOS

  31. USINABILIDADE DOS AÇOS INOXIDÁVEIS • OS AÇOS INOXIDÁVEIS AUSTENÍTICOS SÃO OS QUE APRESENTAM A MAIOR DIFICULDADE PARA SEREM USINADOS: • FORMAÇÃO DE CAVACOS LONGOS • ALTA TAXA DE ENCRUAMENTO • BAIXA CONDUTIVIDADE TÉRMICA • ALTO COEFICIENTE DE ATRITO • ALTO COEFICIENTE DE DILATAÇÃO TÉRMICA

  32. USINABILIDADE DOS AÇOS INOXIDÁVEIS • A - ALTA TAXA DE DESGASTE DE CRATERA • B - DEFORMAÇÃO PLÁSTICA EXCESSIVA • C - FORMAÇÃO DE APC • D - ALGUMA DEFORMAÇÃO PLÁSTICA • E - ALGUM DESGASTE DE CRATERA

  33. USINABILIDADE • Grau de dificuldade de se usinar um determinado material. • GrandezaTecnológica. • Expressa um conjunto de propriedades de usinagem de um material em relação a outro tomado com padrão, por meio de um índicecomparativo.