CHAPTER 4: POLYMER STRUCTURES

CHAPTER 4: POLYMER STRUCTURES. ISSUES TO ADDRESS. • What are the basic microstructural features ?. • How do these features dictate room T tensile response ?. • Hardening, anisotropy, and annealing in polymers . 1. POLMER MICROSTRUCTURE. • Poly mer = many mers.

lucius
Download Presentation

CHAPTER 4: POLYMER STRUCTURES

An Image/Link below is provided (as is) to download presentation Download Policy: Content on the Website is provided to you AS IS for your information and personal use and may not be sold / licensed / shared on other websites without getting consent from its author. Content is provided to you AS IS for your information and personal use only. Download presentation by click this link. While downloading, if for some reason you are not able to download a presentation, the publisher may have deleted the file from their server. During download, if you can't get a presentation, the file might be deleted by the publisher.

E N D

Presentation Transcript


  1. CHAPTER 4:POLYMER STRUCTURES ISSUES TO ADDRESS... • What are the basic microstructural features? • How do these features dictate room T tensile response? • Hardening, anisotropy, and annealing in polymers. 1

  2. POLMER MICROSTRUCTURE • Polymer = many mers Adapted from Fig. 14.2, Callister 6e. • Covalent chain configurations and strength: Direction of increasing strength Adapted from Fig. 14.7, Callister 6e. 2

  3. THERMOPLASTICS VS THERMOSETS • Thermoplastics: --little cross linking --ductile --soften w/heating --polyethylene (#2) polypropylene (#5) polycarbonate polystyrene (#6) • Thermosets: --large cross linking (10 to 50% of mers) --hard and brittle --do NOT soften w/heating --vulcanized rubber, epoxies, polyester resin, phenolic resin Adapted from Fig. 15.18, Callister 6e. (Fig. 15.18 is from F.W. Billmeyer, Jr., Textbook of Polymer Science, 3rd ed., John Wiley and Sons, Inc., 1984.) 3

  4. MOLECULAR WEIGHT & CRYSTALLINITY • Molecular weight, Mw: Mass of a mole of chains. • Tensile strength (TS): --often increases with Mw. --Why? Longer chains are entangled (anchored) better. • % Crystallinity: % of material that is crystalline. --TS and E often increase with % crystallinity. --Annealing causes crystalline regions to grow. % crystallinity increases. Adapted from Fig. 14.11, Callister 6e. (Fig. 14.11 is from H.W. Hayden, W.G. Moffatt, and J. Wulff, The Structure and Properties of Materials, Vol. III, Mechanical Behavior, John Wiley and Sons, Inc., 1965.) 4

  5. At right, the common mer elements. Mer weights are calculated by the number of each element times its molecular weight. For example, polytetrafluoroethylene is: 2(carbon)*12.011g/mol * 4(flourine)*19.00 g/mol = 100.022 g/mol

  6. Number average and weight average molecular weight, Mn and Mw Number average and weight average degree of polymerization, nn and nw