实验三 乙酸乙烯酯的溶液聚合

实验三 乙酸乙烯酯的溶液聚合. 实验 3 乙酸乙烯酯的溶液聚合. 一、 基本原理. 溶液聚合是将单体和引发剂溶于适当的溶剂中，在溶液状态下进行的聚合反应。 根据聚合产物是否溶于溶剂可分为均相溶液聚合和沉淀溶液聚合。 溶液聚合优点 ：体系粘度小，传质和传热容易，聚合反应温度容易控制，不易发生自动加速现象，而且由于高分子浓度低，不易发生向高分子的链转移反应，因而支化产物少，产物分子量分布较窄。.

lucita
Download Presentation

实验三 乙酸乙烯酯的溶液聚合

An Image/Link below is provided (as is) to download presentation Download Policy: Content on the Website is provided to you AS IS for your information and personal use and may not be sold / licensed / shared on other websites without getting consent from its author. Content is provided to you AS IS for your information and personal use only. Download presentation by click this link. While downloading, if for some reason you are not able to download a presentation, the publisher may have deleted the file from their server. During download, if you can't get a presentation, the file might be deleted by the publisher.

E N D

Presentation Transcript

  1. 实验三 乙酸乙烯酯的溶液聚合

  2. 实验3 乙酸乙烯酯的溶液聚合 一、 基本原理 溶液聚合是将单体和引发剂溶于适当的溶剂中，在溶液状态下进行的聚合反应。 根据聚合产物是否溶于溶剂可分为均相溶液聚合和沉淀溶液聚合。 溶液聚合优点：体系粘度小，传质和传热容易，聚合反应温度容易控制，不易发生自动加速现象，而且由于高分子浓度低，不易发生向高分子的链转移反应，因而支化产物少，产物分子量分布较窄。

  3. 溶液聚合缺点：单体被稀释，聚合反应速率慢，产物分子量较低，而且如果产物不能直接以溶液形式应用的话，还需增加溶剂分离与回收后处理工序，加之溶液聚合的设备庞大，利用率低，成本较高。 溶液聚合在工业上常用于合成可直接以溶液形式应用的聚合物产品，如胶粘剂、涂料、油墨等，而较少用于合成颗粒状或粉状产物。

  4. 二 、主要药品与仪器 乙酸乙烯酯50 mL 甲醇30 mL AIBN 0.21g 装有搅拌器、冷凝管、温度计的三颈瓶1套 恒温水浴1套 10、20、100mL 量筒各1支 抽滤装置1套

  5. 三、实验步骤 实验装置图

  6. （1）在装有搅拌器、冷凝管、温度计的250 mL三颈瓶（如上图）中分别加入50 mL乙酸乙烯酯、10 mL 溶有0.21g AIBN的甲醇。 （2）开动搅拌，加热升温，将反应物逐步升温至62±2℃，反应约3h后，升温至65±1℃，继续反应0.5h后，冷却结束聚合反应。 （3）称取2-3g产物在烘箱中烘干，计算固含量与单体转化率。用甲醇将剩余的产物稀释至25%（PVAc含量）留待实验四使用。

  7. 四、思考题 溶液聚合反应的溶剂应如何选择？本实验采用甲醇作溶剂是基 于何种考虑？