实验四 苯乙烯 - 顺丁烯二酸酐的共聚及共聚组成测定. 1. 目的和要求. 了解共聚合反应的基本原理和实验方法 了解高分子化学反应的特点 测定苯乙烯 — 顺丁烯二酸酐共聚物的组成. 2. 实验原理. 自由基聚合实施方法 ? 共聚反应类型 ? 交替共聚原理 a ．单体结构特点 (CTC) b ．共聚组成方程 (4) 共聚物组成的测定 ① 测定方法：反向滴定法（为什么？） ②原因：高分子化学反应的特点. F 1 =( r 1 f 1 2 + f 1 f 2 )/( r 1 f 1 2 +2 f 1 f 2 + r 2 f 2 2 ).

lizina
Download Presentation

实验四 苯乙烯 - 顺丁烯二酸酐的共聚及共聚组成测定

An Image/Link below is provided (as is) to download presentation Download Policy: Content on the Website is provided to you AS IS for your information and personal use and may not be sold / licensed / shared on other websites without getting consent from its author. Content is provided to you AS IS for your information and personal use only. Download presentation by click this link. While downloading, if for some reason you are not able to download a presentation, the publisher may have deleted the file from their server. During download, if you can't get a presentation, the file might be deleted by the publisher.

E N D

Presentation Transcript

  1. 实验四 苯乙烯-顺丁烯二酸酐的共聚及共聚组成测定

  2. 1. 目的和要求 • 了解共聚合反应的基本原理和实验方法 • 了解高分子化学反应的特点 • 测定苯乙烯—顺丁烯二酸酐共聚物的组成

  3. 2. 实验原理 • 自由基聚合实施方法? • 共聚反应类型? • 交替共聚原理 a．单体结构特点(CTC) b．共聚组成方程 (4) 共聚物组成的测定 ① 测定方法：反向滴定法（为什么？） ②原因：高分子化学反应的特点 F1=(r1f12+f1f2)/( r1f12+2f1f2+r2f22) r1->0, r2->0时，F1=1/2

  4. 3. 实验部分 (1) 共聚物的合成 装置：250mL四口瓶，搅拌器，温度 计，球形冷凝管，氮气导管 加料顺序：先加Mah和苯，加热溶解后再加St和AIBN（为什么？） 反应条件：75～77oC（后期80 oC），1小时 现象：变稠，搅拌困难 后处理：洗至中性，抽滤，烘干，测产率

  5. (2) 共聚物组成测定 称量：0.5克聚合物，20mL 0.5mol/L的NaOH溶液 加热：约1小时，完全溶解 滴定：平行滴定两组 计算：WMAH%=98.06X(NNaOHXVNaOH-NHClXVHCl) /(2XWtotalX1000)X100%

  6. 4. 注意事项 (1) 注意安全，按规定操作 (2) 抽滤时苯倒入回收桶，严禁把苯倒入水槽 (3) 公用药品和仪器用后放回原位 (4) 节约药品 (5) 保持卫生

  7. 5. 思考题 • 合成苯乙烯—顺丁烯二酸酐共聚物，及测定该共聚物组成的基本原理是什么？ • 对所得共聚物的产率及共聚物组成的实验值与计算值进行比较，并请分析原因。 • 苯乙烯—顺丁烯二酸酐共聚物与氢氧化钠溶液的反应是高分子化学反应，试比较高分子化学反应与低分子化学反应的异同点。