第十四章鋁及鋁合金. 改進教學計畫編號：教改進 -97C-003 計畫主持人：楊慶彬. 14-2 鋁之性質及用途. 一、 鋁之物理性質 鋁為銀白色金屬，重量輕、導熱度、導電度及耐蝕性良好、富延展性、易加工。 二、 鋁之機械性質 鋁的機械性質因純度、加工度及熱處理情形而異。 三、 鋁之用途. 鋁之物理性質. 鋁之機械性質. 14-3 鋁合金之時效硬化. 鋁合金平衡圖及時效硬化 所謂 時效硬化 及硬化作用有隨時間而增加之效用。在常溫下放置經久，會有 θ 相逐漸析出： α ( 過飽和 ) → α ( 安定 ) + θ

lave
Download Presentation

第十四章鋁及鋁合金

An Image/Link below is provided (as is) to download presentation Download Policy: Content on the Website is provided to you AS IS for your information and personal use and may not be sold / licensed / shared on other websites without getting consent from its author. Content is provided to you AS IS for your information and personal use only. Download presentation by click this link. While downloading, if for some reason you are not able to download a presentation, the publisher may have deleted the file from their server. During download, if you can't get a presentation, the file might be deleted by the publisher.

E N D

Presentation Transcript

  1. 第十四章鋁及鋁合金 改進教學計畫編號：教改進-97C-003 計畫主持人：楊慶彬

  2. 14-2鋁之性質及用途 一、鋁之物理性質 鋁為銀白色金屬，重量輕、導熱度、導電度及耐蝕性良好、富延展性、易加工。 二、鋁之機械性質 鋁的機械性質因純度、加工度及熱處理情形而異。 三、鋁之用途

  3. 鋁之物理性質

  4. 鋁之機械性質

  5. 14-3鋁合金之時效硬化 鋁合金平衡圖及時效硬化 所謂時效硬化及硬化作用有隨時間而增加之效用。在常溫下放置經久，會有θ相逐漸析出： α(過飽和) → α (安定) + θ 隨時間增加，析出物漸多，合金愈硬化，此即時效硬化之現象。

  6. 14-3鋁合金之時效硬化

  7. 14-3鋁合金之時效硬化

  8. 14-3鋁合金之時效硬化

  9. 14-3鋁合金之時效硬化

  10. 14-3鋁合金之時效硬化 過飽合固溶體在室溫會慢慢發生強化現象，這種自然的強化現象叫做自然時效。 為加速強化效果而將合金加熱之處理叫做人工時效。

  11. 鋁合金之分類

  12. 鑄造用鋁合金 一、鑄造用鋁合金 1.Al-Cu系合金 2.Al-Cu-Si系合金 3.Al-Si系合金 4.Al-Cu-Ni-Mg系合金 5.Al-Mg系合金

  13. 鑄造用鋁合金

  14. 鋁合金之分類 二、壓鑄用鋁合金 • 所謂壓鑄法是把熔融狀態的金屬加以壓力鑄入金屬模內。 三、鍛造用鋁合金 (1)Al-Mn系合金 (2)Al-Mn-Mg系合金 (3)Al-Mg系合金

  15. 杜拉鋁及其性質