石墨在滚压振动磨作用下的形态变化

石墨在滚压振动磨作用下的形态变化. 汇报人 ：顾森伟. 实验方法. 将高定向热解石墨和原料锌粉均匀混合后，放入滚压振动磨中研磨 5 小时。取出研磨后石墨少量，置于 30 m l 乙醇溶液中超声分散 30 分钟后，取上层清液！. SEM 图片. 产物分析. 从 sem 图片的形貌判断，葡萄球形的碳球颗粒其粒径在 300 n m 左右。对比于中科院硅酸盐研究所利用化学法制备出来的碳球，其形貌，粒径相似。 从在华理分析测试中心所作的拉曼来看，研磨 5 小时的产物中，出现极少数的 d 峰消失现象，这说明在机械研磨过程中，石墨晶体的长程有序结构被打破，出现的无定性碳的特征。

kerem
Download Presentation

石墨在滚压振动磨作用下的形态变化

An Image/Link below is provided (as is) to download presentation Download Policy: Content on the Website is provided to you AS IS for your information and personal use and may not be sold / licensed / shared on other websites without getting consent from its author. Content is provided to you AS IS for your information and personal use only. Download presentation by click this link. While downloading, if for some reason you are not able to download a presentation, the publisher may have deleted the file from their server. During download, if you can't get a presentation, the file might be deleted by the publisher.

E N D

Presentation Transcript

  1. 石墨在滚压振动磨作用下的形态变化 汇报人：顾森伟

  2. 实验方法 • 将高定向热解石墨和原料锌粉均匀混合后，放入滚压振动磨中研磨5小时。取出研磨后石墨少量，置于30ml乙醇溶液中超声分散30分钟后，取上层清液！

  3. SEM图片

  4. 产物分析 • 从sem图片的形貌判断，葡萄球形的碳球颗粒其粒径在300nm左右。对比于中科院硅酸盐研究所利用化学法制备出来的碳球，其形貌，粒径相似。 • 从在华理分析测试中心所作的拉曼来看，研磨5小时的产物中，出现极少数的d峰消失现象，这说明在机械研磨过程中，石墨晶体的长程有序结构被打破，出现的无定性碳的特征。 • 关于碳球的拉曼光谱特征还在查找资料，因为C60,C70,C76,C80的拉曼特征峰各不相同，定性还需要其它表征手段！

  5. 特点 • 从现在所掌握的文献看，这种制备出来的碳球应该属于利用机械物理法制备出来的首例。

  6. 碳球形成成因推测 • 在滚压振动磨的研磨过程中，锌粉颗粒更容易细化，它与石墨晶体存在相互正向挤压作用。 • 石墨层的边缘存在不饱和的五元环和七元环，本身特别容易形成稳定的六元环而发生弯曲。 • 单层石墨的二维表面为波纹状，及其容易包覆其它的颗粒！

  7. 接下来需要进行的研究 • 确定碳球是单层的还是多层的； • 确定碳球是中空的还是包覆有锌颗粒的； • 对碳球进行分离和提纯； • 碳球的结构分析和性能分析！