An Image/Link below is provided (as is) to download presentation Download Policy: Content on the Website is provided to you AS IS for your information and personal use and may not be sold / licensed / shared on other websites without getting consent from its author. Content is provided to you AS IS for your information and personal use only. Download presentation by click this link. While downloading, if for some reason you are not able to download a presentation, the publisher may have deleted the file from their server. During download, if you can't get a presentation, the file might be deleted by the publisher.

E N D

Presentation Transcript

  1. 第二章 扭转、弯曲和压缩

  2. §1 扭转 一、扭转应力的特点 • 应力软性系数α=0.8，比拉伸的α大，可以测定低塑性材料的性能 • 最大正应力与轴向成45°，最大切应力平行或垂直轴向 • 扭转横截面上有应力梯度，表面受到的应力最大

  3. 二、扭转变形的特点 扭转变形特点：无颈缩

  4. 三、扭转断裂特点 • （a）切断断口 • （b）正断断口 • （c）木纹状断口 塑形材料的断裂面与试样轴线垂直，断口平整，如（a）图所示 脆性材料的断裂面与试样轴向成45°角，呈螺旋状，如（b）图所示 图（c）所示的为木纹状断口，断裂面顺着试样轴线形成纵向剥层或裂纹

  5. 四、扭转试验 试样要求：主要是直径d0为10mm、标距长度L0为50mm或100mm的圆柱形试样。 τ—切应力 W—试样抗扭截面系数，圆柱形试样为πd03/16 五、扭转力学性能 1、切变模量G

  6. 2、扭转比例极限 3、扭转屈服强度 4、扭转强度极限 5、塑形

  7. §2 弯曲 一、特点 • 横截面上也存在应力梯度，上表面为压应力，下表面为拉应力 • 表面应力最大，中心的为零 • 试样简单，操作方便，试验重复性好 • 对高塑性的材料，通常不进行弯曲试验

  8. 二、弯曲试验 弯曲试验方式有三点弯曲加载和四点弯曲加载方式 三、力学性能

  9. §3 压缩 1、压缩的过程即时拉伸的反过程 具有一些和拉伸相对应的力学性能指标 2、应力软性系数α= 2 3、端面摩擦力会影响试验结果 通常h0/d0为1-3

  10. 本章完