Discrete Dynode Structures Using ALD and Other Techniques for MCPs

Discrete Dynode Structures Using ALD and Other Techniques for MCPs. June 10 th , 2010 LAPPD meeting Qing Peng, Anil U. Mane, Jeffrey W. Elam Energy Systems, Argonne National Laboratory. Traditional Discrete Dynode Structures. Traditional discrete dynode structures:

gordonnicole
Download Presentation

Discrete Dynode Structures Using ALD and Other Techniques for MCPs

An Image/Link below is provided (as is) to download presentation Download Policy: Content on the Website is provided to you AS IS for your information and personal use and may not be sold / licensed / shared on other websites without getting consent from its author. Content is provided to you AS IS for your information and personal use only. Download presentation by click this link. While downloading, if for some reason you are not able to download a presentation, the publisher may have deleted the file from their server. During download, if you can't get a presentation, the file might be deleted by the publisher.

E N D

Presentation Transcript

  1. Discrete Dynode Structures Using ALD and Other Techniques for MCPs June 10th, 2010 LAPPD meeting Qing Peng, Anil U. Mane, Jeffrey W. Elam Energy Systems, Argonne National Laboratory

  2. Traditional Discrete Dynode Structures • Traditional discrete dynode structures: • Each stage is biased separately with well-controlled voltage drop • Each stage could have its own SEE materials

  3. Traditional Discrete Dynode Structures Functionalized MCP • Traditional discrete dynode structures: • Each stage is biased separately with well-controlled voltage drop • Each stage could have its own SEE materials Can we make a MCP have similar structure as discrete dynode?

  4. Motivation • To achieve well-defined strike, especially the first and 2nd strikes, in the operation of MCPs, which could significantly decrease the widths of the transition time spread and single photon charge distributions.

  5. Concept I Discrete dynode: Continuous resistive layer then discrete SEE layer Electrode coating could be putted on before SEE layer High SEE layer Resistive layer Low SEE layer MCP Substrate Electrode

  6. Schematic to Achieve Stripe Coating by ALD • Principle • Reactants diffuse into the pore and react with along the pore • The growth of materials could be selectively blocked by choosing different chemistry, as shown in following scheme. direction into pore XL XL XL XL Diffusion controlled A deposition XLn OH OH OH OH OH OH OH OH O O O O OH OH OH OH Diffusion control A deposition YLn OH OH OH OH OH OH OH OH XL XL YL YL XL XL YL YL X X Y Y X X Y Y X Y O O O O O O O O O O O O O O O O H2O

  7. Previous Work of Stripe Coating Results ZnO Owing to large library of ALD chemistry: Stripes of other materials such as MgO could be formed through this method. AAO: aspect ratio >1000. Pore size: <60nm Al2O3 Al2O3 Al2O3 EDAX elemental maps for Zn L following deposition of ZnO stripes in AAO varying only the TMA exposure time J. W. Elam, J. A. Libera, M. J. Pellin etc APPLIED PHYSICS LETTERS 91, 243105 2007

  8. Requirement and Challenge for ALD to form Stripes of SEE • Requirement for good stripe coating by ALD • The process needs to be in the diffusion controlled region: • Reaction rate has to be very fast (sticking coefficient >> diffusion coefficient) • Collision rate of molecules to the wall need to be high • Diffusion rate has to be slow (Knudson mode) • Challenges: • It is difficult to control the reaction and diffusion process for the pore size of >10 um, because the mean free path is comparable with the pore size. The diffusion rate is expected to be higher. • L/D ratio of glass MCP is ~60, which is small for controlling the diffusion of precursor • Due to the concentration gradient along the tube, it is very difficult to form sharp interface between stripe coatings and uncoated parts.

  9. More Effective Way: fabrication of Two Discrete Structure through ALD/PVD or CVD ALD SEE layer Resistive layer High SEE layer By CVD or PVD MCP substrate

  10. Candidate Materials for High SEE • Materials with Negative electron affinity, including activated GaP, GaN, GaAs, Diamond, and such. • Diamond coating (SEE: <80) • Highly crystallized MgO by PVD process (SEE:<25) • High quality NaCl, CsI, MgF2, CaF2 (SEE 5-15) Single crystal MgO MgO film

  11. Diamond as High SEE candidate by PECVD Ultrananocrystal Diamond by CNM-ANL At 400C J. Appl. Phys., Vol. 96, No. 4, 15 August 2004, O. Auciello, ANL-MSD www.photek.co.uk

  12. ALD MgF2 and CaF2 APPLIED OPTICS Vol. 47, No. 13 1 May 2008

  13. Proposed Scheme for Dynodes Structure Formation • Test SEE of UNCD film by PECVD on Si • Test MCPs with • UNCD layer only at the top • MgO by ALD/PVD/CVD • ALD coating for 2 stripes of SEE layers on glass MCP and testing the feasibility for > 2 stripes of SEE layers • ALD coating of CaF2 and MgF2 for applications of SEE