Double-sided YBCO thin films

Double-sided YBCO thin films . Cleanroom for deposition. Homogeneous Tc distribution. Measured with inductive coil with 5 mm in diameter. By Michele Lorenz. 2. Homogeneous Jc distribution. Measured with Leipzig jc-scan system. J C = 2.5 ~ 2.9 MA/cm 2. Rs distribution.

garren
Download Presentation

Double-sided YBCO thin films

An Image/Link below is provided (as is) to download presentation Download Policy: Content on the Website is provided to you AS IS for your information and personal use and may not be sold / licensed / shared on other websites without getting consent from its author. Content is provided to you AS IS for your information and personal use only. Download presentation by click this link. While downloading, if for some reason you are not able to download a presentation, the publisher may have deleted the file from their server. During download, if you can't get a presentation, the file might be deleted by the publisher.

E N D

Presentation Transcript


  1. Double-sided YBCO thin films

  2. Cleanroom for deposition

  3. Homogeneous Tc distribution Measured with inductive coil with 5 mm in diameter

  4. By Michele Lorenz

  5. 2 Homogeneous Jc distribution Measured with Leipzig jc-scan system JC = 2.5 ~ 2.9 MA/cm2

  6. Rs distribution Measured at145GHz, 75K, by FZK, Germany 0.24-0.37 mW converted to 10GHz

  7. XRD results of 3 inch sample edge center

  8. Surface structure of YBCO films AFM images, the heights of the designated steps are given: A-B,1.136nm; B-C, 1.172nm; C-D, 1.131nm; E-F, 1.1609nm; F-G, 1.142nm; G-H,1.164nm.

  9. MTI CorporationLead suppler for Advanced Materials and Lab Equipmentwww.mtixtl.com • We can provide 2 to 3 inch YBCO double-sided YBCO thin films in a small batch (e.g. 10-30 pieces) in one month after substrate delivered. • The typical properties of 500 nm films are as follows: Tc ~ 90K, Delta Tc less than 1K Jc77K,0T ~2-3 MA/cm2 Rs77k,10GHz~0.2-0.8mohm