Speciation of 14 C in Irradiated Graphite Mary Lou Dunzik-Gougar Idaho State University and Idaho National Laboratory

Speciation of 14 C in Irradiated Graphite Mary Lou Dunzik-Gougar Idaho State University and Idaho National Laboratory INGSM-14, Seattle, WA, USA September 2013. Due recognition of student researchers, consultants and startup funding. Students James Cleaver, MS Dec 2011

erik
Download Presentation

Speciation of 14 C in Irradiated Graphite Mary Lou Dunzik-Gougar Idaho State University and Idaho National Laboratory

An Image/Link below is provided (as is) to download presentation Download Policy: Content on the Website is provided to you AS IS for your information and personal use and may not be sold / licensed / shared on other websites without getting consent from its author. Content is provided to you AS IS for your information and personal use only. Download presentation by click this link. While downloading, if for some reason you are not able to download a presentation, the publisher may have deleted the file from their server. During download, if you can't get a presentation, the file might be deleted by the publisher.

E N D

Presentation Transcript


  1. Speciation of 14C in Irradiated Graphite Mary Lou Dunzik-Gougar Idaho State University and Idaho National Laboratory INGSM-14, Seattle, WA, USA September 2013

  2. Due recognition of student researchers, consultants and startup funding • Students • James Cleaver, MS Dec 2011 • ShiloMcCrory, MS Dec 2011 • Tara Smith, MS Dec 2012 • Dan LaBrier, PhD 2013 • Kathy Nelson, MS 2014 • Ted Pollock, MS 2014 • Consultants • Johannes Fachinger, FNAG • Will Windes, INL • Abbie Jones, U of Manchester • Tony Wickham, Nuclear Technology Consultancy

  3. The Objective is to . . . . . . determine the chemical nature of 14C on irradiated graphite surfaces • Characterize unirradiated and irradiated graphite surfaces with respect to 14C • Thermally treat irradiated graphite for removal of surface 14C

  4. The graphite irradiation

  5. The characterization • Characterize pre- and post-irradiated graphite • Focus on 14C and precursor 14N • XPS, Raman – Bond Information • ToF-SIMS – Speciation • SEM/EDS – Morphological Features, Chemical Environment

  6. Surface Analyses Completed

  7. Characterization SEM and EDS

  8. SEM N cluster N cluster

  9. SEM Nitrogen Nucleation Poco 50000 x • Nitrogen clusters preferentially nucleate at edges and activation sites Poco 1500 x NBG-18 35000 x

  10. Energy Dispersive X-Ray Carbon (red), oxygen (blue) and nitrogen (green) on surface of irradiated graphite

  11. SEM: Nitrogen Clusters in Irradiated NBG-25 (FIB surface)

  12. Characterization X-ray Photoelectron and Raman Spectroscopy

  13. XPS Survey Scans: POCOFoam C1s O1s Unirradiated C1s O1s LN2 immersed N1s O1s C1s Irradiated C1s Thermally Treated

  14. XPS Survey Scans: NBG-18 C1s O1s Unirradiated C1s O1s LN2 immersed N1s O1s C1s Irradiated C1s O1s Thermally Treated

  15. XPS Survey Scans: NBG-25

  16. XPS: NBG-25 Surface Scans Trace amounts of nitrogen present in unirradiatedsamples Some bound oxygen (~2%) to graphite surfaces UNIRRADIATED IRRADIATED No discernible presence of nitrogen in irradiated samples Amount of bound oxygen increases (to ~7%) due to irradiation

  17. XPS: Irradiated NBG-18 & POCOFoam® Surface Scans Significant increase in the amount of surface nitrogen and oxygen present NBG-18 POCOFoam® Attributed to exposure to air and excess LN2 during irradiation

  18. XPS: NBG-25 C 1s Peak Deconvolution Broadening of C 1s peak in irradiated NBG-25 (along with increased oxygen presence) suggests the formation of additional surface oxides

  19. XPS: C 1s Peak for All Irradiated Graphites Significant amounts of oxides are observed on the surfaces of all graphites and are directly attributed to neutron irradiation.

  20. Raman: Unirradiated vs. Irradiated NBG-25 D (sp3) peak G (sp2) peak

  21. Characterization Secondary Ion Mass Spectroscopy (SIMS)

  22. ToF-SIMS: Species of Interest

  23. ToF-SIMS: Surface Concentration of 14C (NBG-25) Surface 14C, N 5 nm 14C, N • Sputtering of surface layers removes substantial amount (~90%) of suspected 14C • Indicates that 14C is concentrated on graphite surface

  24. ToF-SIMS: Positive Ion Spectra

  25. ToF-SIMS: Negative Ion Spectra

  26. ToF-SIMS: m/z = 26 (CN-) Conundrum Surface 5 nm Lack of substantial surface (and sub-surface) presence of N in irradiated NBG-25 suggests m/z=26 signal is predominantly 14CC (some CN possible) Strength of sub-surface signal further suggests that 14C is bound within the graphite lattice Possible correlation between 14CC and elevated sp3 bonding just below surface

  27. XPS: C 1s Analysis for All Irradiated Graphites Surface species dominated by oxides for irradiated NBG-18 & POCOFoam® Significant amount of surface oxides for irradiated NBG-25

  28. XPS: C 1s Analysis for All Thermally Treated Graphites Removal of significant portions of surface oxides and sp3 bonding for all irradiated graphite Removal of 14C?

  29. ToF-SIMS: Removal of 14C via Thermal Treatment of NBG-25 Pre-Thermal Treatment Pre-Thermal Treatment 14C, N Post-Thermal Treatment 14C, N • Amount of 14C on the surface of irradiated NBG-25 is reduced by 85-90% due to thermal treatment

  30. ToF-SIMS: Removal of 14C via Thermal Treatment of NBG-18 Pre-Thermal Treatment 14C, N Post-Thermal Treatment 14C, N • Amount of 14C removed via thermal treatment: • NBG-18: ~95%

  31. Pathways of Release for 14C • 14CO and 14CO2 are the main desorption species released during thermal treatment • Dependent on surface chemistry (C-O functional groups) • 14CO2 – dominant at lower (< 600 oC) temperatures • 14CO – dominant at higher (> 600 oC) temperatures • Complexity of species formed on surface will be affected by duration of irradiation, coolant, gamma radiation • Based on XPS results, most likely surface functional groups: • 14CO2 – aldehydes, carboxylics, lactones • 14CO – ethers, ketones, quinones

  32. Temperature Dependency of 14C Removal CO2 is prominently removed at lower temperatures (with limited desorption at higher temperatures) 150-400 oC 350-650 oC 600-950 oC 600-700 oC CO is removed at higher temperatures (> 600 oC) ~700 oC 700-950 oC Figueiredo, 1999

  33. Conclusions • Presence of 14C is confirmed on surfaces of irradiated graphite • Species containing 14C (or 14N) were identified using SIMS • XPS and Raman analysis eliminates substantial presence of 14N • Relative concentration of 14C is ~10 times higher on graphite surfaces than below (< 10 nm) the surface • Carbon-oxygen functional groups identified on irradiated graphite surfaces • Bond information surmised using XPS; confirmed by Raman • Chemical species identified using SIMS • Temperature dependency based on thermal treatment data

  34. Thank You!

  35. SEM of NBG-25 (1/2) Unirradiated(1000x) Thermally Treated (1000x) Irradiated (2000x)

  36. SEM: Surface Morphology