1 / 5

SSL-UCB, ALD/Incom MCP Test

SSL-UCB, ALD/Incom MCP Test. Incom substrate 40µm pores, 8 deg bias, 40:1 L/D Sent to Arradiance for resistive and emissive layer application + electrode Resistance approx 750 MΩ in vacuum Arradiance tests show 50,000 gain @ 1000v UV - bright image, no light - black!

elijah
Download Presentation

SSL-UCB, ALD/Incom MCP Test

An Image/Link below is provided (as is) to download presentation Download Policy: Content on the Website is provided to you AS IS for your information and personal use and may not be sold / licensed / shared on other websites without getting consent from its author. Content is provided to you AS IS for your information and personal use only. Download presentation by click this link. While downloading, if for some reason you are not able to download a presentation, the publisher may have deleted the file from their server. During download, if you can't get a presentation, the file might be deleted by the publisher.

E N D

Presentation Transcript

  1. SSL-UCB, ALD/Incom MCP Test • Incom substrate • 40µm pores, 8 deg bias, 40:1 L/D • Sent to Arradiance for resistive and emissive layer application + electrode • Resistance approx 750 MΩ in vacuum • Arradiance tests show 50,000 gain @ 1000v • UV - bright image, no light - black! • Tested as a single MCP + Phosphor • It works! We have a functional, uniform, and stable (1hr) MCP using borosilicate and ALD. • Project milestone under 5.1 year 1 deliverable

  2. SSL-UCB, ALD/Incom MCP Test Arradiance gain curve for Incom 40µm coated substrate

  3. SSL-UCB, ALD/Incom MCP Test It works! 700v 800v Bright scratch on phosphor UV light 1000v 900v

  4. SSL-UCB, ALD/Incom MCP Test Multifiber pattern is bad due to crushing of pores at the multifiber interfaces

  5. SSL-UCB, ALD/Incom MCP Test Multifiber pattern fades as the MCP gain is increased Gain is quite uniform Need todetermine cause of black spots Multifiber lines <100µm 2mm