Electronic characterization of dislocations

Surf. Potential. Electronic characterization of dislocations. 0.1 V /Div. 10 nm /Div. Morphology. Potential. G. Koley and M. G. Spencer, Appl. Phys. Lett. 78 , 2873 (2001). UV light. Surface potential patterning using mask. 20 m circle quartz mask. HFET Sample

bruno
Download Presentation

Electronic characterization of dislocations

An Image/Link below is provided (as is) to download presentation Download Policy: Content on the Website is provided to you AS IS for your information and personal use and may not be sold / licensed / shared on other websites without getting consent from its author. Content is provided to you AS IS for your information and personal use only. Download presentation by click this link. While downloading, if for some reason you are not able to download a presentation, the publisher may have deleted the file from their server. During download, if you can't get a presentation, the file might be deleted by the publisher.

E N D

Presentation Transcript


  1. Goutam Koley Surf. Potential Electronic characterization of dislocations 0.1 V /Div 10 nm /Div Morphology Potential G. Koley and M. G. Spencer, Appl. Phys. Lett.78, 2873 (2001)

  2. Goutam Koley UV light Surface potential patterning using mask 20 m circle quartz mask HFET Sample (35% Al in barrier, 44 nm AlGaN layer)

  3. Goutam Koley Spatial resolution of charge storage UV exposure through a mask of 1, 2, 5, 10 and 20 m squares Spatial resolution on the order of ~1-2 m 3.5 m G. Koley et al. JAP (2004)

  4. Goutam Koley AFM scanning probe Measurements in GaN based transistors Biasing Probes

  5. Goutam Koley Drain Source Surface morphology and potential profiles in dc biased transistors Gate Vd = 2V, Vg = -1.5 V Morphology Surface Potential

  6. Goutam Koley Measurement of transients AFM scanning probe Measurement setup schematic Probe tip Drain Source Gate Gate Drain A A Source 20  resistor +ve dc bias -ve dc bias or square pulse Biasing Probes G. Koley et al. IEEE Trans. Electron Dev. 50, 886 (2003) Goutam Koley

  7. Goutam Koley Stressed at Vg = -12V, Vd = 20 V for 2 mins Maximum variation observed ~0.3 m from the gate edge Charges take a long time to reach equilibrium value Potential variation with distance and time 150 m HFET G. Koley et al. IEEE Trans. Electron Dev. 50, 886 (2003) Goutam Koley

  8. Goutam Koley Surface conductivity measurements (a) Morphology, (b) conductivity, and (c) overlap of the surface morphology and conductivity images

  9. Goutam Koley Scanned gate microscopy Scanned gate microscopy is useful to determine the variation of conductivity along a thin channel, and where direct measurement of conductivity is difficult (a) Experimental set up for SGM, (c) the SGM image of a single-walled CNT bundle for Vtip = 1 V; Black corresponds to very high resistance.

  10. Goutam Koley Scanning capacitance microscopy Scanning capacitance technique actually measures the dC/dV signal which is inversely proportional to doping. The advantages of this technique include a large measurement range (1015 – 1020 cm-3), and resolution of <10 nm For capacitance measurement a low frequency ac voltage is applied to the sample. The ac voltage periodically changes the tip-sample capacitance. The sensor produces a high frequency signal to measure very small capacitance changes.

  11. Goutam Koley Application of capacitance microscopy Cross-sectional measurement in a MOSFET under actual operation

  12. Goutam Koley The dC/dV decreases around the dislocations indicating the reduction in the background carrier concentration Applications to GaN samples Capacitance image Morphology image C-V curve