1 / 32

Solár R., Mamoň M., Hudec J., Reinprecht L.

Effect of biotic and a -b iotic pre-treatments of hornbeam wood on its properties important from viewpoint of kraft and organosolv pulping. Solár R., Mamoň M., Hudec J., Reinprecht L. Faculty of Wood Sciences and Technology. Technical University of Zvolen,

briana
Download Presentation

Solár R., Mamoň M., Hudec J., Reinprecht L.

An Image/Link below is provided (as is) to download presentation Download Policy: Content on the Website is provided to you AS IS for your information and personal use and may not be sold / licensed / shared on other websites without getting consent from its author. Content is provided to you AS IS for your information and personal use only. Download presentation by click this link. While downloading, if for some reason you are not able to download a presentation, the publisher may have deleted the file from their server. During download, if you can't get a presentation, the file might be deleted by the publisher.

E N D

Presentation Transcript


  1. Effect of biotic and a-biotic pre-treatments of hornbeam wood on its properties important from viewpoint of kraft and organosolv pulping. Solár R., Mamoň M., Hudec J., Reinprecht L. Faculty of Wood Sciences and Technology. Technical University of Zvolen, T.G. Masaryka 24, 96053 Zvolen, Slovakia.

  2. Introduction • Production of chemical pulps is an expensive matter connected with high consumption of energies, chemicals and water, and the product contains residual lignin requesting tedious bleaching steps. • From the above reasons an extensive research concerning also pre-treatment of wood by white-rot fungi has been carried out in the last decades. The achieved results, however were not always positive - alkaline pulping. • For fungal pre-treatment is characteristic so called „bio-pulping” effect, based on the release in the structure and partial delignification of wood.

  3. Introduction • Similar effect on the structure, chemical composition and physical propertiesof wood might have also alkaline/oxidative sequencesof chemical pre-treatment. • Advantage of a-bioticagents might be inmore uniform effect,shorter time of action and un-necessity of chips sterilisation.

  4. Aim • The estimation of some physical and chemical changes of hornbeam wood pre-treated by white-rot fungi and chemical agents, as well, related to kraft and organosolv pulping and the pulps properties.

  5. Material, selection of specimens • The hornbeam wood test specimensof dimensions 2.5x2.5x1 cm were made from two sections taken from middle part of thetreetrunk in age of 90 years. • Shorter dimension of each specimen was parallel, and the longer ones perpendicular to grain. From the specimens a comparable series, each comprising 8 specimens, were prepared.

  6. Pre-treatments • For 30-day bio-degradations of hornbeam wood, the following white-rot fungi were used: Trametes versicolor - erosive fungus Phanerochaete chrysosporium - erosive fungus Ceriporiopsis subvermispora - lignin-selective strain. • Chemical pre-treatments were as follows: - 48 h alkaline (2.5 % NaOH) step followed by 48 h oxidationwith7.5 % H2O2 (with, or without dicyandiamide activator), - 48 h alkaline (2.5 % NaOH) step followed by 48 h oxidationwith 8 and 4 %per-acetic acid, as well. Pre-treatments were carried out at the ambient temperature (22-23 oC).

  7. Pre-treatments • Bio-mimetic pre-treatment: Bio-mimetic system, similar to low-molecular complexes generated by lignin-selective fungi, has been used as a control of delignification efficacy of the applied biotic and a-biotic agents. Composition: 4-aminopyridine/TBH peroxide/Cu2+ complexproposed by Messner et al. (2003); molar ratios were increased for 50 %. Hydromodul was 1:16, and delignification at 50 oC lasted 72 h.

  8. Measurements and analyses • Weight loss • Facial swelling after 48 h dipping in H2O or pre-treatment • Coefficients of axial permeability • Kinetics of facial swelling in water • Extract (ethanol/toluene) • Lignin determination (ASTM 13 m) • Cellulose determination (Kürschner-Hoffer) • Bleaching - activated H2O2 at 33 and 62 oC (1 + 1h) • DP - from intrinsic viscosity of bleached pulps in FETNA soln.

  9. Pulping • Kraft pulping: • sulfidity of liquor 21.5 %; active alkali 16.0 %, • time to reach the pulping temperature of 170 oC- 75 min, • pulping at the temperature – 60 min; hydromodul 1:4.1 . • Organosolv pulping: • liquor - 0.03 M (COOH)2 in ethanol/water 1:1 v/v, • time to reach the pulping temperature of 160 oC - 75 min, • pulping at the temperature 60 min; hydromodul 1:5.2 . • Note: pulping in small scale autoclaves without stirring, dimensions of chipscut from the specimenswere 3x3x10mm (longer dimension parallel to grain), their moisture content before pulping - 6.4 %.

  10. Results and discussion • All pre-treatments resulted in theweight lossof hornbeam wood, changes inphysical properties and inits altered chemical composition, as well (Figs. 1-5, Tabs. 1 and 2).

  11. Results - weight lossFig. 1 Weight loss of hornbeam wood due to biotic and a-bioticpre-treatments (%)

  12. Results - facial swellingFig. 2 Final value of facial swelling of sound and pre-treated hornbeam wood specimens (%)

  13. Results - kinetics of facial swellingFig. 3 Kinetic plots and relative rate constants of facial swelling of hornbeam woodpre-treated by white-rot fungi; 0 - sound wood,1 – T. versicolor, 2 – P. chrysosporium, 3 – C.subvermispora

  14. Results - kinetics of facial swellingFig. 4 Kinetic plots and rate constants of facial swelling of hornbeam woodpre-treated with white-rot fungi; 0 –sound wood, 4 - NaOH/H2O2, 5– NaOH/H2O2 + activator, 6 –NaOH/8 % per-acetic acid, 7- NaOH/4 % per-acetic acid, 8– bio-mimetic system

  15. Results - kinetics of facial swelling • As it follows from Fig. 3, fungal pre-treatments increasedextremely the rate of hornbeam wood facial swelling in its first-fast phase (more than for two orders). • The effect of chemical pre-treatments (Fig. 4) was much weaker, and caused only 1.5 to 2 multiple increase in the relative rate constant of facial swelling, in comparison with sound wood. • The difference in the rate of swelling of bio –, and chemically pre-treated wood is possibly in higher porosity of the bio-degraded material, and in extreme shrinkage (for 30 and 20 %, respectively) of chemically degraded wood.

  16. Results - kinetics of facial swelling • Extreme shrinkage of chemically pre-treated wood in the drying hints at formation of high number of hydrogen bonds among the wood components in its former - deeply relaxedultrastructure. • Numerous cohesive bonds in the structure of dry chemically pre-treated wood possibly slow down the rate of wood/polar liquid interactions, reflected outward in the facial swelling.

  17. Results - axial permeabilityFig.5 Drop in the coefficient of axial permeability of pre-treated hornbeam wood at moisture content above FSP (%)

  18. Results - axial permeability • As it follows from Fig. 5, all pre-treatments significantly reduced the axial permeability of wood. The most „effective” in this respect was the lignin- selective fungus C. subv. and bio-mimetic system. • Explanation of this phenomenon follows from differentswelling mode of the vessels in sound and by white-rot fungi pre-treated hornbeam wood (Fig. 6).

  19. Results - cross-sections of thelumina Fig. 6 Confidence intervals for means of changes in the vessels lumina cross-sections ( A) in wetting; 1-ethanol/water mixture, 2-sulphate liquor, 3-NSSC liquor (hornbeam wood, 30-day degr. by P. chrysosporium,weight loss - 16.2 %, (MANOVA, Duncan test)

  20. Results - swelling mode • Comparison of mean areas of cross-sections of the lumina • in the vessels showed, that the swelling oftheir cell walls in • sound wood enlarged the lumina cross-sections,thus increasing • its permeability. • Swelling of the cell walls inthe vessels of bio-degraded wood proceeds in both directions „inside and outside” the lumina, • and reduces its axial permeability.

  21. Results - chemical alterations Tab. 1 Amounts of lignin and cellulose removedfrom hornbeam wood in the course of pre-treatments (%)

  22. Results - chemical alterations • All biotic pre-treatments resulted in deep delignification of a substrate. Most effective in this respect was the lignin-selective fungus C. subvermispora, that removed approximately 50 % of lignin at the cost of only 2.7 % of cellulose. • From abiotic agents the most effective was the sequence comprising 2.5 % NaOH/8 % per-acetic acid with 35 % of lignin removed from wood. • All alkaline/oxidation sequences of pre-treatments were accompanied by an increase in the content of cellulose - possibly due to sorption of xylane in alkaline environment.

  23. Results - kraft and organosolv pulpFig. 7 Yield of kraft and organosolv pulps based on the weight of pre-treated wood (%)

  24. Results - pulps, residual lignin and DPTab. 2 Content of residual lignin in the unbleached pulps and their DP after hydrogen peroxide bleaching

  25. Results - selectivity of delignificationFig. 8 Effect of pre-treatments on the selctivity of kraft pulping of hornbeam wood, given as residual lignin to pulp yield ratio

  26. Results - selectivity of delignification • Negligible content of residual lignin in the kraft pulps from chemically pre-treated hornbeam wood (Tab. 2), and the corresponding low lignin to pulp ratios ( Fig. 8) point out at the extremely increased selectivity of kraft delignification in this case. • Pre-treatments of hornbeam wood by white-rot fungi influenced the contents of residual lignin in the kraft pulps negatively, and reduced the selectivity of kraft process for 30 %. • On the other hand, the fungal pre-treatments and those based on the application of NaOH/per-acetic acid improved the selectivity of acid catalysed organosolv pulping.

  27. Conclussions • From the obtained experimental data the following conclusions may be derived: • All pre-treatments resulted in the wood weight loss almost equal to • 11 %, exception were those with the use of P. chrysosporium and • NaOH/8 % per-acetic acid, causing approx. 16 % weight loss of the • tested specimens. • Extreme values of facial swelling of woodpre-treated by a-biotic agents hint at deeply relaxed ultra-structure of wood - resulting from cleavage of physical and chemical bondsin the lignin-carbo- hydrate matrix.

  28. Conclussions • Both biotic and a-biotic pre-treatments increased the rate of facial swelling of hornbeam wood- expressing outward the rate of wood/water surface interactions. • All pre-treatments resulted in marked drop in axial permeability of hornbeam wood, especially deep reduction caused fungus C. subvermispora and bio-mimetic system. • White-rot fungi efficiently delignified the pre-treated material, and the amount of ligninremoved varied within 21 – 50 %, however at the cost of deep loss of cellulose.

  29. Conclussions • Chemical agents were less effective in delignification with only 7 to 35 % of removed lignin from wood, but did not cause any loss of cellulose. • Activated hydrogen peroxide markedly increased the hornbeam wood delignification, however as compared to pure hydrogen peroxide pre- treatment, it had no influence on the residual lignin in the pulp. • Comparison of residual lignin in the pulps confirmed highly positive influenceof a-biotic pre-treatments on the selectivity of kraft and organosolv pulping.

  30. Conclussions • Deep biotic or a-biotic delignification of wood prior to pulping does not inevitably guaranteea deep reduction in the content of residual lignin in the unbleached pulp!

  31. Conclussions - illustr. of the last aitem Fig. 9 Lignin contents in the compared wood samples and corresponding unbleached kraft pulps (%)

  32. End Thank you for patience and attention! :-)