Rheologisches Werkstoffverhalten

Mögliche Arten rheologischen Verhaltens (Fließkurve). Rheologisches Werkstoffverhalten. 4. 1a. 3. 1. 1 : newton ´ sch (Luft) 1a: newton ´ sch (hochviskos H 2 O) 2 : strukturviskos (Kunststoff schmelzen) 3 : dilatant (Dispersionen) 4 : Bingham ( Ketch-up ). 2.

bette
Download Presentation

Rheologisches Werkstoffverhalten

An Image/Link below is provided (as is) to download presentation Download Policy: Content on the Website is provided to you AS IS for your information and personal use and may not be sold / licensed / shared on other websites without getting consent from its author. Content is provided to you AS IS for your information and personal use only. Download presentation by click this link. While downloading, if for some reason you are not able to download a presentation, the publisher may have deleted the file from their server. During download, if you can't get a presentation, the file might be deleted by the publisher.

E N D

Presentation Transcript

  1. Mögliche Arten rheologischen Verhaltens (Fließkurve) Rheologisches Werkstoffverhalten 4 1a 3 1 1 : newton´sch (Luft) 1a: newton´sch (hochviskos H2O) 2 : strukturviskos (Kunststoff schmelzen) 3 : dilatant (Dispersionen) 4 : Bingham (Ketch-up) 2 log Schubspannungτ log Schergeschwindigkeit 1

  2. Mögliche Arten rheologischen Verhaltens (Viskositätskurve) Rheologisches Werkstoffverhalten Bingham dilatant log Viskosität η newton´sch strukturviskos log Schergeschwindigkeit 2

  3. Einfluss des Molekulargewichts (Mw) auf die Viskosität a) Mw sehr hoch b) Mw mittel c) Mw niedrig

  4. 10000 log Viskosität [Pa s] 1000 100 10 Blasformtyp Extrusionstyp Folientyp 1 log Scherge- schwindigkeit [1/s] Spritzgießtyp 1 10 100 1000 10000 100000 Kalandrieren Extrudieren Spritzgießen

  5. Einfluss der Temperatur auf die Viskosität 300 °C 320 °C 340 °C 360 °C 101 10² 10³